The microstructures and corrosion behaviors of as-cast,T4-treated,and T6-treated Mg-6Gd-3Y-0.5Zr alloys were systematically investigated by SEM,TEM,immersion test,and electrochemical corrosion test.The results show th...The microstructures and corrosion behaviors of as-cast,T4-treated,and T6-treated Mg-6Gd-3Y-0.5Zr alloys were systematically investigated by SEM,TEM,immersion test,and electrochemical corrosion test.The results show that the microstructure of the as-cast alloy is composed ofα-Mg and Mg_(24)(Gd,Y)_(5) eutectic phase,and in T4-treated alloy,Mg_(24)(Gd,Y)_(5) phase dissolves into theα-Mg matrix,leading to an increase in the(Y,Gd)H_(2) phase.After T6 treatment,nanoscale Mg_(24)(Gd,Y)_(5) phase dispersedly precipitates from theα-Mg matrix,and exhibits a specific orientation relationship with the α-Mg:(332)Mg_((24)(Gd,Y)_(5))//(1011)_(α-Mg),[136]Mg_((24)(Gd,Y)_(5))//[1210]_(α-Mg).The corrosion resistance of the Mg-6Gd-3Y-0.5Zr alloys can be ranked in the following order:T6-treated alloy exhibits the highest corrosion resistance,followed by the T4-treated alloy,and finally,the as-cast alloy.The corrosion products of the alloys are all composed of MgO,Mg(OH)_(2),Gd_(2)O_(3),Y_(2)O_(3),and MgCl_(2).The corrosion behavior of Mg-6Gd-3Y-0.5Zr alloy is closely related to the precipitated phase.By establishing the relationship between corrosion rate,hydrogen evolution rate,and corrosion potential,it is further demonstrated that during the micro galvanic corrosion process,the coarse Mg_(24)(Gd,Y)_(5)phase in the as-cast alloy undergoes extensive dissolution,and(Y,Gd)H_(2) phase promotes the dissolution of theα-Mg matrix in the T4-treated alloy,intensifying the hydrogen evolution reaction.The T6-treated alloy,with dispersive precipitation of nanoscale Mg_(24)(Gd,Y)_(5) phase,exhibits better corrosion resistance performance.展开更多
The effects of the ultrasonic treatment on the microstructure and mechanical properties of Mg-6Zn-0.5Y-2Sn alloy were investigated. The results show that the ultrasonic treatment has significant effect on the microstr...The effects of the ultrasonic treatment on the microstructure and mechanical properties of Mg-6Zn-0.5Y-2Sn alloy were investigated. The results show that the ultrasonic treatment has significant effect on the microstructure and mechanical properties of Mg-6Zn-0.5Y-2Sn alloy. The phases in Mg-6Zn-0.5Y-2Sn alloy are α-Mg, MgZn2, MgSnY, Mg2Sn, and a small amount of I-phase. With the application of ultrasonic treatment, I-phase nearly disappears, and with increasing the ultrasonic treatment power, the coarse dendrites gradually change into roundish equiaxed grains. The second phases at the α-Mg boundaries transform from coarse, semicontinuous and non-uniform to fine, discontinuous, uniform and dispersive. When the ultrasonic treatment power is 700 W, the best comprehensive mechanical properties of Mg-6Zn-0.5Y-2Sn alloy are obtained. Compared with the untreated alloy, the 0.2%tensile yield strength, ultimate tensile strength and elongation are improved by 28%, 30%and 67%, respectively.展开更多
Rapidly solidified（RS） Mg-6Zn-1Y-1Ce ribbons were prepared by single roller melt-spinning technique.Transmission electron microscopy and energy dispersive X-ray spectroscopy were employed to characterize the microst...Rapidly solidified（RS） Mg-6Zn-1Y-1Ce ribbons were prepared by single roller melt-spinning technique.Transmission electron microscopy and energy dispersive X-ray spectroscopy were employed to characterize the microstructure of RS ribbons.The results show that there is high density of particles distributed within grains and at grain boundaries in the region near wheel side.The particle density is decreased in the middle region and free surface region.The alloy is predominantly composed of supersaturated--Mg solid solution,T phase and W phase;meanwhile,a few icosahedral quasicrystalline and Mg4Zn7 particles are also observed.The T phase is confirmed having a body-centered orthorhombic structure that is transformed from the body-centered tetragonal structure Mg12Ce phase due to the partial substitution of Mg atoms by Zn.展开更多
In this work,a high-strength Mg–10Gd–6Y–1.5Zn–0.5Zr(wt.%)alloy was fabricated by successive multi-pass equal channel angular pressing(ECAP).The microstructure and mechanical property of as-cast and ECAP alloys wer...In this work,a high-strength Mg–10Gd–6Y–1.5Zn–0.5Zr(wt.%)alloy was fabricated by successive multi-pass equal channel angular pressing(ECAP).The microstructure and mechanical property of as-cast and ECAP alloys were systematically researched by X-ray diffractometer,scanning electron microscopy,transmission electron microscopy and compression test.The results show that the microstructure of as-cast alloy consists ofα-Mg grains,Mg24Y5 networks,18R blocks,fine 14H lamellas,and fewY-rich particles.After 8 passes ECAP,dynamic recrystallization ofα-Mg is developed and their average grain size decreases to about 1μm.The network Mg_(24)Y_(5) phase at grain boundaries is broken into small particles with average diameter lower than 0.5μm.Moreover,18R blocks are kinked and delaminated,or broken into small particles and blended with Mg24Y5 particles.14H lamellas grow gradually or are dynamically precipitated within certainα-Mg grains.Compression tests indicate that 8p ECAP alloy exhibits excellent mechanical property with compressive strength of 537 MPa and fracture strain of 17.0%.The significant improvement for both strength and ductility of deformed alloy could be ascribed to DRX grains,refined Mg24Y5 particles,18R kinking and dynamical precipitation of 14H.展开更多
In this work,a new(Y,Gd)H_(2) precipitate was identified and systematically investigated in the as-cast Mg-6Gd-3Y-0.5Zr alloy by XRD,SEM with EDS,TEM with EDS techniques and thermodynamics analysis.Results show that t...In this work,a new(Y,Gd)H_(2) precipitate was identified and systematically investigated in the as-cast Mg-6Gd-3Y-0.5Zr alloy by XRD,SEM with EDS,TEM with EDS techniques and thermodynamics analysis.Results show that the as-cast alloy contains α-Mg,Mg_(24)(Gd,Y)_(5),and(Y,Gd)H_(2) phase.The(Y,Gd)H_(2) phase usually forms near the eutectic phase Mg_(24)(Gd,Y)_(5) or in the α-Mg grains,displaying a rectangle-shape.The Mg_(24)(Gd,Y)_(5) and(Y,Gd)H_(2) phases crystalize in bcc and fcc structure,respectively,and the(Y,Gd)H_(2) phase has a semi-coherent relationship with α-Mg matrix.The thermodynamics calculation results reveal that the hydrogen dissolved in the melt leads to the formation of hydrides.It is also found that the(Y,Gd)H_(2) hydride can form directly from the liquid phase during solidification.Additionally,it can precipitate by the decomposition of Mg_(24)(Gd,Y)_(5) phase due to absorbing hydrogen from the remaining melt.展开更多
基金supported by the Key Project of Equipment Pre-research Field Fund under Grant No.61409230407.
文摘The microstructures and corrosion behaviors of as-cast,T4-treated,and T6-treated Mg-6Gd-3Y-0.5Zr alloys were systematically investigated by SEM,TEM,immersion test,and electrochemical corrosion test.The results show that the microstructure of the as-cast alloy is composed ofα-Mg and Mg_(24)(Gd,Y)_(5) eutectic phase,and in T4-treated alloy,Mg_(24)(Gd,Y)_(5) phase dissolves into theα-Mg matrix,leading to an increase in the(Y,Gd)H_(2) phase.After T6 treatment,nanoscale Mg_(24)(Gd,Y)_(5) phase dispersedly precipitates from theα-Mg matrix,and exhibits a specific orientation relationship with the α-Mg:(332)Mg_((24)(Gd,Y)_(5))//(1011)_(α-Mg),[136]Mg_((24)(Gd,Y)_(5))//[1210]_(α-Mg).The corrosion resistance of the Mg-6Gd-3Y-0.5Zr alloys can be ranked in the following order:T6-treated alloy exhibits the highest corrosion resistance,followed by the T4-treated alloy,and finally,the as-cast alloy.The corrosion products of the alloys are all composed of MgO,Mg(OH)_(2),Gd_(2)O_(3),Y_(2)O_(3),and MgCl_(2).The corrosion behavior of Mg-6Gd-3Y-0.5Zr alloy is closely related to the precipitated phase.By establishing the relationship between corrosion rate,hydrogen evolution rate,and corrosion potential,it is further demonstrated that during the micro galvanic corrosion process,the coarse Mg_(24)(Gd,Y)_(5)phase in the as-cast alloy undergoes extensive dissolution,and(Y,Gd)H_(2) phase promotes the dissolution of theα-Mg matrix in the T4-treated alloy,intensifying the hydrogen evolution reaction.The T6-treated alloy,with dispersive precipitation of nanoscale Mg_(24)(Gd,Y)_(5) phase,exhibits better corrosion resistance performance.
基金Project(cstc2015jcyj BX0036)supported by Chongqing Research Program of Basic Research and Frontier Technology,ChinaProject(51571040)supported by the National Natural Science Foundation of ChinaProject supported by the Sharing Fund of Chongqing University’s Large-scale Equipment,China
文摘The effects of the ultrasonic treatment on the microstructure and mechanical properties of Mg-6Zn-0.5Y-2Sn alloy were investigated. The results show that the ultrasonic treatment has significant effect on the microstructure and mechanical properties of Mg-6Zn-0.5Y-2Sn alloy. The phases in Mg-6Zn-0.5Y-2Sn alloy are α-Mg, MgZn2, MgSnY, Mg2Sn, and a small amount of I-phase. With the application of ultrasonic treatment, I-phase nearly disappears, and with increasing the ultrasonic treatment power, the coarse dendrites gradually change into roundish equiaxed grains. The second phases at the α-Mg boundaries transform from coarse, semicontinuous and non-uniform to fine, discontinuous, uniform and dispersive. When the ultrasonic treatment power is 700 W, the best comprehensive mechanical properties of Mg-6Zn-0.5Y-2Sn alloy are obtained. Compared with the untreated alloy, the 0.2%tensile yield strength, ultimate tensile strength and elongation are improved by 28%, 30%and 67%, respectively.
基金Project (50271054) supported by the National Natural Science Foundation of ChinaProject (20070700003) supported by the Doctorate Programs Foundation of Ministry of Education of China+1 种基金Project (102102210031) supported by the Science and Technologies Foundation of Henan Province,ChinaProject (2010A430008) supported by the Natural Science Foundation of Henan Educational Committee of China
文摘Rapidly solidified（RS） Mg-6Zn-1Y-1Ce ribbons were prepared by single roller melt-spinning technique.Transmission electron microscopy and energy dispersive X-ray spectroscopy were employed to characterize the microstructure of RS ribbons.The results show that there is high density of particles distributed within grains and at grain boundaries in the region near wheel side.The particle density is decreased in the middle region and free surface region.The alloy is predominantly composed of supersaturated--Mg solid solution,T phase and W phase;meanwhile,a few icosahedral quasicrystalline and Mg4Zn7 particles are also observed.The T phase is confirmed having a body-centered orthorhombic structure that is transformed from the body-centered tetragonal structure Mg12Ce phase due to the partial substitution of Mg atoms by Zn.
基金the Natural Science Foundation of Jiangsu Province of China(No.BK20160869)the financial support from the Nantong Science and Technology Project(No.GY12015009)+1 种基金the Fundamental Research Funds for the Central Universities(No.2015B01314)the National Natural Science Foundation of China(No.51501039).
文摘In this work,a high-strength Mg–10Gd–6Y–1.5Zn–0.5Zr(wt.%)alloy was fabricated by successive multi-pass equal channel angular pressing(ECAP).The microstructure and mechanical property of as-cast and ECAP alloys were systematically researched by X-ray diffractometer,scanning electron microscopy,transmission electron microscopy and compression test.The results show that the microstructure of as-cast alloy consists ofα-Mg grains,Mg24Y5 networks,18R blocks,fine 14H lamellas,and fewY-rich particles.After 8 passes ECAP,dynamic recrystallization ofα-Mg is developed and their average grain size decreases to about 1μm.The network Mg_(24)Y_(5) phase at grain boundaries is broken into small particles with average diameter lower than 0.5μm.Moreover,18R blocks are kinked and delaminated,or broken into small particles and blended with Mg24Y5 particles.14H lamellas grow gradually or are dynamically precipitated within certainα-Mg grains.Compression tests indicate that 8p ECAP alloy exhibits excellent mechanical property with compressive strength of 537 MPa and fracture strain of 17.0%.The significant improvement for both strength and ductility of deformed alloy could be ascribed to DRX grains,refined Mg24Y5 particles,18R kinking and dynamical precipitation of 14H.
基金financially supported by the Key Project of Equipment Pre-research Field Fund under Grant No.61409230407the National Natural Science Foundation of China(NSFC)under Grant No.51601054the Central Government Guides Local Science and Technology Development Fund Projects under Grant No.206Z1005G。
文摘In this work,a new(Y,Gd)H_(2) precipitate was identified and systematically investigated in the as-cast Mg-6Gd-3Y-0.5Zr alloy by XRD,SEM with EDS,TEM with EDS techniques and thermodynamics analysis.Results show that the as-cast alloy contains α-Mg,Mg_(24)(Gd,Y)_(5),and(Y,Gd)H_(2) phase.The(Y,Gd)H_(2) phase usually forms near the eutectic phase Mg_(24)(Gd,Y)_(5) or in the α-Mg grains,displaying a rectangle-shape.The Mg_(24)(Gd,Y)_(5) and(Y,Gd)H_(2) phases crystalize in bcc and fcc structure,respectively,and the(Y,Gd)H_(2) phase has a semi-coherent relationship with α-Mg matrix.The thermodynamics calculation results reveal that the hydrogen dissolved in the melt leads to the formation of hydrides.It is also found that the(Y,Gd)H_(2) hydride can form directly from the liquid phase during solidification.Additionally,it can precipitate by the decomposition of Mg_(24)(Gd,Y)_(5) phase due to absorbing hydrogen from the remaining melt.