To eliminate thermal stress and cracks in the process of laser cladding, a kind of bioceramic coating with gradient compositional design was prepared on the surface of Ti alloy by using wide-band laser cladding. And e...To eliminate thermal stress and cracks in the process of laser cladding, a kind of bioceramic coating with gradient compositional design was prepared on the surface of Ti alloy by using wide-band laser cladding. And effect of Y2O3 content on gradient bioceramic composite coating was studied. The experimental results indicate that adding rare earth can refine grain. Different rare earth contents affect formation of HA and β-TCP in bioceramic coating. When the content of rare earth ranges from 0.4% to 0.6%, the active extent of rare earth in synthesizing HA and β-TCP is the best, which indicates that “monosodium glutamate” effect of rare earth plays a dominant role. However, when rare earth content is up to 0.8%, the amount of synthesizing HA and β-TCP in coating conversely goes down, which demonstrates that rare earth gradually losts its catalysis in manufacturing HA and β-TCP.展开更多
Cored wires for electric arc spraying of Al/Al 2 O 3 MMC coatings were developed, with Al 2 O 3 powder as the core material and commercial aluminium strip as the retaining sheath. The bond strength, ...Cored wires for electric arc spraying of Al/Al 2 O 3 MMC coatings were developed, with Al 2 O 3 powder as the core material and commercial aluminium strip as the retaining sheath. The bond strength, Al 2 O 3 content, microstructure, micro-hardness and wear resistance of coatings produced by arc spraying of the cored wires were experimentally investigated and were compared with those of pure aluminum coating.展开更多
Cobalt-based alloys with different Y2O3 contents were deposited on Q235A-carbon steel using plasma transferred arc （PTA） welding machine. The effect of Y2O3 on the microstructure and wear resistance properties of th...Cobalt-based alloys with different Y2O3 contents were deposited on Q235A-carbon steel using plasma transferred arc （PTA） welding machine. The effect of Y2O3 on the microstructure and wear resistance properties of the cobait-based alloys were investigated using an optical microscope, a scanning electron microscope （SEM）, X-ray diffraction （XRD）, and transmission electron microscopy （TEM）. It was found that a cobalt-based solid solution with a face-centered cubic crystal structure was presented accompanied by the secondary phase M7C3 with a hexagonal crystal structure in the Y2O3-free cobalt-based alloy coating. Several stacking faults exist in the cobalt-based solid solution. The addition of Y2O3 leads to the existence of the Y2O3 phase in the Y2O3-modified coatings. Though stacking fault exists in the Y2O3-modified coatings, its density increases. The addition of Y2O3 can refine the microstructure and can increase the wear resistance properties when its contents are less than or equal to 0.8 wt.%. However, further increase of its contents will lead to the agglomeration of undissolved Y2O3 particles at the γ-Co grain boundary, and will lead to a coarse microstructure and lower wear resistance properties.展开更多
TiB2 and Dy2O3 were used as codeposited particles in the preparation of Ni-TiB2-Dy2O3 composite coatings to improve its performance. Ni-TiB2-Dy2O3 composite coatings were prepared by electrodeposition method with a ni...TiB2 and Dy2O3 were used as codeposited particles in the preparation of Ni-TiB2-Dy2O3 composite coatings to improve its performance. Ni-TiB2-Dy2O3 composite coatings were prepared by electrodeposition method with a nickel cetyltrimethylammonium bromide and hexadecylpyridinium bromide solution containing TiB2 and Dy2O3 particles. The content of codeposited TiB2 and Dy2O3 in the composite coatings was controlled by adding TiB2 and Dy2O3 particles of different concentrations into the solution, respectively. The effects of TiB2 and Dy2O3 content on microhardness, wear mass loss and friction coefficients of composite coatings were investigated. The composite coatings were characterized by X-ray diffraction （XRD）, inductively coupled plasma-atomic emission spectrometer （ICP-AES） and scanning electron microscopy （SEM） techniques. Ni-TiBE-Dy2O3 composite coatings showed higher microhardness, lower wear mass loss and friction coefficient compared with those of the pure Ni coating and Ni-TiB2 composite coatings. The wear mass loss of Ni-TiB2-Dy2O3 composite coatings was 9 and 1.57 times lower than that of the pure Ni coating and Ni-TiB2 composite coatings, respectively. The friction coefficient of pure Ni coating, Ni-TiB2 and Ni-TiB2-Dy2O3 composite coatings were 0.723, 0.815 and 0.619, respectively. Ni-TiBE-Dy2O3 composite coatings displayed the least friction coefficient among the three coatings. Dy2O3 particles in composite coatings might serve as a solid lubricant between contact surfaces to decrease the friction coefficient and abate the wear of the composite coatings. The loading-bearing capacity and the wear-reducing effect of the Dy2O3 particles were closely related to the content of Dy2O3 particles in the composite coatings.展开更多
Al2O3-metal composite coatings with different reactants and diluents were fabricated on mild steel plate with nonpressure combustion synthesis process. The coat-ings were characterized by means of X-ray diffraction, s...Al2O3-metal composite coatings with different reactants and diluents were fabricated on mild steel plate with nonpressure combustion synthesis process. The coat-ings were characterized by means of X-ray diffraction, scanning electron microscopy, and energy-dispersive spec-trometry, respectively. Thermal shock tests were carried out to determine the bond strength of the coating with the steel substrate. The results indicate that the coating is composed of α-A1203, α-（Fe-Cr） and Al2SiO5 as the main phases. It is found that the coating with the diluents of Al2O3-SiO2 and transition layer of Al2O3-Cr presents the hi.ghest hardness of 2270 HV0.2 and the lowest porosity of 3.93 %. Owing to a metallurgical bond of the coating-to-substrate, the coating exhibits a good thermal shock resistance.展开更多
ZrO2-Y2O3 ceramic coating was produced by plasma electrolytic oxidation （PEO） on ZAlSil2Cu3Ni2 alloy. The microstructure and phase composition of the coating were investigated by SEM and XRD.： The results show that...ZrO2-Y2O3 ceramic coating was produced by plasma electrolytic oxidation （PEO） on ZAlSil2Cu3Ni2 alloy. The microstructure and phase composition of the coating were investigated by SEM and XRD.： The results show that adding an appropriate amount of yttrium ion can improve the growing rate of ceramic coating at different oxidation stages and decrease arc voltage. The thickness of ZrO2-Y2O3 coating is 16 μn thicker than that of ZrO2 coating and the maximum oxidation rate improves by 0.6 μm/min. In addition, the arc voltage decreases from 227 to 172 V. It can be seen that the rate of oxidation firstly increases to some extent and then decreases with the content of yttrium ion increasing. The growth rate reaches the maximum while the content of yttrium ion is 0.05 g-L-1The maximum thickness is 90 μm.Compared to ZrO2 coating, the micropores of ZrO2-Y2O3 coating are less and the ceramic layer is repeatedly deposited by ZrO2 and Y2O3 ceramic particles. Meanwhile, the binding force between coating and substrate is better and the coating is uniform and compact. The ceramic layer is mainly composed of c-Y0.15Zr0.85O1.93□0.07, m-ZrO2, α-Al2O3, ,γ-Al2O3 and Y2O3. It is indicated that ZrO2 has beert fully stabilized by yttrium ion through the formation of solid solution.展开更多
Two types of plasma sprayed coatings (NiCrAlY and NiCrAlY-A12O3) were remelted by a 5 kW cw CO2 laser. With increasing laser power and decreasing traverse speed in the ranges of 200-700 W and 5-30 mm/s respectively, t...Two types of plasma sprayed coatings (NiCrAlY and NiCrAlY-A12O3) were remelted by a 5 kW cw CO2 laser. With increasing laser power and decreasing traverse speed in the ranges of 200-700 W and 5-30 mm/s respectively, the melted track grew in width and depth. In the optimum range of laser parameters, a homogeneous remelted layer without voids, cavities, unmelted particles and microcracks was formed. On the surface of remelted layers, Al203 and YAIO3 were detected. As a result of isothermal oxidation tests, weight gains of laser remelted coatings were obviously lower than that only plasma sprayed, especially laser remelted NiCrAlY-Al2O3 coatings. The effects of laser remelting and incorporation of A12O3 second phase in N1CrAlY matrix on high temperature oxidation resistance were discussed.展开更多
Rules and mechanism of damage in Al2O3 coatings irradiated by CO2 CW laser are studied in order to improve the ability of parts of equipment standing against the high power laser. Al2O3 coatings were sprayed by air pl...Rules and mechanism of damage in Al2O3 coatings irradiated by CO2 CW laser are studied in order to improve the ability of parts of equipment standing against the high power laser. Al2O3 coatings were sprayed by air plasma spray（APS） on the 45^# steel substrate, and then were irradiated by CO2 CW laser from 795 W/cm^2 to 31 830 W/cm^2. As the output power of the laser is increasing, its porosity is increasing and cracks are appearing and spreading quickly, And also the phase will transform from γ-Al2O3 to a-Al2O3 in the damaged areas. When the energy density is 17 507 W/cm^2, the coatings are destroyed completely. The thermal infection field on substrate is rather small. The laser energy is depleted by the phase transformation and cracks in Al2O3 coatings during the laser thermal shock.展开更多
NiCoCrAlY-ZrO2·Y2O3 coatings were deposited on the substrates by using a technology of combining electron,atom and ion beams （three beams）. Isothermal oxidation for these samples was performed at 1100℃ for 100...NiCoCrAlY-ZrO2·Y2O3 coatings were deposited on the substrates by using a technology of combining electron,atom and ion beams （three beams）. Isothermal oxidation for these samples was performed at 1100℃ for 100-300 h. The results show that a thermally grown oxide （TGO） layer was formed between NiCoCrAlY layer and oxidation. The TGO contains α-Al2O3 and Y4Al2O9 etc. oxides. The intensity ratio of α-Al2O3/Y4Al2O9 was monotonously decreased with increasing oxidation time based on XRD （X-ray diffraction） analysis. The Y4Al2O9 phase plays the most important role in high temperature oxidation resistance at 1100℃. The related mechanism was also discussed.展开更多
The composite coating was prepared by thermal spray welding after making composite powder,which is composed of Ni-based self-melted alloy and AlOceramic powder including nano,sub-micron and micron powders.The influenc...The composite coating was prepared by thermal spray welding after making composite powder,which is composed of Ni-based self-melted alloy and AlOceramic powder including nano,sub-micron and micron powders.The influences of contents and sizes of AlOon the structure and wearability were investigated.The results show that the wear resistance of the coating would be increased greatly by adding AlO,but the spray weldability decreases with increasing AlOcontent.So there is an optimal content of AlOpowder.The composite coating with AlOnano or sub-micron powder of 0.5% has the best abrasive resistance,while the optimal content of AlOmicron powder is 1 %.展开更多
Metal and nano-ceramic nanocomposite coatings were prepared on the gray cast iron surface by the electrodeposition method. The Ni-Co was used as the metal matrix,and nano-Al2O3 was chosen as the second-phase particula...Metal and nano-ceramic nanocomposite coatings were prepared on the gray cast iron surface by the electrodeposition method. The Ni-Co was used as the metal matrix,and nano-Al2O3 was chosen as the second-phase particulates. To avoid poor inter-face bonding and stress distribution,the gradient structure of biology materials was found as the model and therefore the gradient composite coating was prepared. The morphology of the composite coatings was flatter and the microstructure was denser than that of pure Ni-Co coatings. The composite coatings were prepared by different current densities,and the 2-D and 3-D morphologies of the surface coatings were observed. The result indicated that the 2-D structure became rougher and the 3-D surface density of apices became less when the current density was increased. The content of nanoparticulates reached a maximum value at the current density of 40mA·cm^-2,at the same time the properties including microhardness and wear-resistance were analyzed. The microhardness reached a maximum value and the wear volume was also less at the current density of 40mA·cm^-2. The reason was that nano-Al2O3 particles caused dispersive strengthening and grain refining.展开更多
A new technique-series electro-pulse discharge (SEPD)-was developed as a sur-face coating process. In this technique, both positive and negative poles of a pulse power were used as the depositing electrodes with the s...A new technique-series electro-pulse discharge (SEPD)-was developed as a sur-face coating process. In this technique, both positive and negative poles of a pulse power were used as the depositing electrodes with the substrate alloy as an induction electrode. Fe-Cr and Fe-Cr-Y2O3 micro-crystalline coatings were deposited on stain-less steel (Fe-18Cr-8Ni) surfaces. Oxidation at 950℃ in ambient air showed that the coatings greatly improved the oxidation resistance of the steel. The addition of dis-persed Y2O3 nano-particles into the alloy coatings was found to further reduce the scaling rate and enhance the adhesion of oxide scales.展开更多
To improve the wear resistance and corrosion resistance of magnesium alloys, a 5 kW continuous wave CO2 laser was used to investigate the laser surface cladding on AZ31 B magnesium alloys with Al-Si/Al2O3-TiO2 composi...To improve the wear resistance and corrosion resistance of magnesium alloys, a 5 kW continuous wave CO2 laser was used to investigate the laser surface cladding on AZ31 B magnesium alloys with Al-Si/Al2O3-TiO2 composite powders. A detailed microstructure, chemical composition, and phase analysis of the composite coatings were studied by scanning electron microscopy （SEM）, energy dispersive spectroscopy （EDS）, and X-ray diffraction （XRD）. The laser cladding shows good metallurgical bonding with the substrate. The composite coatings are composed of Mgl7Al12, Al3Mg2, Mg2Si, Al2O3, and TiO2 phases. Compared to the average microhardness （50HV0.05） of the AZ3 1 B substrate, that of the composite coatings （230HV0.05） is improved significantly. The wear resistances of the surface layers were evaluated in detail. The results demonstrate that the wear resistances of the laser surface-modified samples are considerably improved compared to the substrate. It also show that the composite coatings exhibit better corrosion resistance than that of the substrate in 3.5wt% NaCI solution.展开更多
Al2O3p/Al composite coatings were prepared on the surface of AZ31 magnesium alloy by plasma spraying technology with mixed powders of Al and Al2O3. An orthogonal test containing six factors and five levels was carried...Al2O3p/Al composite coatings were prepared on the surface of AZ31 magnesium alloy by plasma spraying technology with mixed powders of Al and Al2O3. An orthogonal test containing six factors and five levels was carried out to acquire the optimum technical parameters. Mierostruetures and properties of the composite coatings were studied. The results show that the coatings consist of Al2O3 particulates distributed uniformly and Al matrix, and the interface between the particulate and matrix is continuous, compact and clean. With increasing the mass fraction of Al2O3 in the mixed powders, the volume fraction of Al2O3 in the coatings iacreases. The Al2O3p/Al composite coating with 14% Al2O3 volume fraction has more compact microstrueture and more satisfactory properties.展开更多
To improve the durability of underwater rotating products,the corrosion characteristics in harsh marine environment were evaluated through various electrochemical experiments on the Al2O3-3TiO2 and CoNiCrAlY coating l...To improve the durability of underwater rotating products,the corrosion characteristics in harsh marine environment were evaluated through various electrochemical experiments on the Al2O3-3TiO2 and CoNiCrAlY coating layers by atmospheric pressure plasma spray coating process.By evaluating the corrosion resistance of these materials,their applicability to environmentally friendly power generation equipment such as blades of tidal current turbines was examined.According to the Tafel analysis for micro-areas including the coating layer,the coating/metal interlayer and the base metal,the Al2O3-3TiO2 coating layer and the CoNiCrAlY coating layer show markedly lower corrosion current density than the base metal.The corrosion current density of the CoNiCrAlY coating layer (9.75316×10-8A/cm2) is about 1.6 times more than that of the Al2O3-3TiO2 coating layer (6.13139×10-8A/cm2).展开更多
A newly developed method is introduced for producing Cr 2O 3 base ceramic coating on aluminum alloys. On the basis of properly selecting base reactions, slurry is prepared and then applied onto the substrate surface...A newly developed method is introduced for producing Cr 2O 3 base ceramic coating on aluminum alloys. On the basis of properly selecting base reactions, slurry is prepared and then applied onto the substrate surface. By chemical reactions taken place in situ on the surface of aluminum alloy at relative low temperature, Cr 2O 3 base ceramic coating is formed. By means of scanning electron microscopy, the coating microstructure and the bonding mechanism are studied. X ray diffraction analysis is also used to investigate the chemical composition of the coating. The coating formation mechanism is further discussed. With a pin on disk tester, wear test is made to evaluate the wear performances of the coating. The results show that by applying the coating on aluminum alloy, the wear decreases 5 times in comparation to that without coating.展开更多
The conventional Al2O3-13 wt. % TiO2 composite ceramic coatings are fabricated by plasma spraying on the surface of extrusion wheel. The microstrueture, morphology and phase compositions of the substrate and coat- ing...The conventional Al2O3-13 wt. % TiO2 composite ceramic coatings are fabricated by plasma spraying on the surface of extrusion wheel. The microstrueture, morphology and phase compositions of the substrate and coat- ing are investigated by using X-ray diffractometry （XRD） , scanning electron microsopy （SEM） and energy dis- persive spectroscopy （EDS）. Moreover, the microhardness of the substrate and the coating are investigated using Vickers mierohardness tester, the friction and wear behaviors of the substrate and the coating are investigated by using a block-on-ring tribometer under dry sliding conditions with the load of 245 N. The results show that both γ-Al2O3 and α-Al2O3 phases are observed in the as-sprayed coatings, the mian phase is γ-Al2O3. There are white particulates Al2O3 on its surface. The Al2O3-13 wt. % TiO2 coating possesses higher mierohardness which is about 1018HV and 1.6 times that of the substrate. The wear performance of coating is better than that of the substrate. In a practical application, the life of the extrusion wheel which is plasma sprayed Al2O3-13 wt. % TiO2 coating on the surface is 1.2 times that of the conventional extrusion wheel, and the life is about 330 h.展开更多
SS304 is a commercial grade stainless steel which is used for various engineering applications like shafts, guides, jigs, fixtures, etc. Ceramic coating of the wear areas of such parts is a regular practice which sign...SS304 is a commercial grade stainless steel which is used for various engineering applications like shafts, guides, jigs, fixtures, etc. Ceramic coating of the wear areas of such parts is a regular practice which significantly enhances the Mean Time Between Failure (MTBF). The final coating quality depends mainly on the coating thickness, surface roughness and hardness which ultimately decides the life. This paper presents an experimental study to effectively optimize the Atmospheric Plasma Spray (APS) process input parameters of Al<sub>2</sub>O<sub>3</sub>-40% TiO2 ceramic coatings to get the best quality of coating on commercial SS304 substrate. The experiments are conducted with a three-level L<sub>18</sub> Orthogonal Array (OA) Design of Experiments (DoE). Critical input parameters considered are: spray nozzle distance, substrate rotating speed, current of the arc, carrier gas flow and coating powder flow rate. The surface roughness, coating thickness and hardness are considered as the output parameters. Mathematical models are generated using regression analysis for individual output parameters. The Analytic Hierarchy Process (AHP) method is applied to generate weights for the individual objective functions and a combined objective function is generated. An advanced optimization method, Teaching-Learning-Based Optimization algorithm (TLBO), is applied to the combined objective function to optimize the values of input parameters to get the best output parameters and confirmation tests are conducted based on that. The significant effects of spray parameters on surface roughness, coating thickness and coating hardness are studied in detail.展开更多
基金Project supported by Governor's Foundation of Guizhou Province (2004-07)
文摘To eliminate thermal stress and cracks in the process of laser cladding, a kind of bioceramic coating with gradient compositional design was prepared on the surface of Ti alloy by using wide-band laser cladding. And effect of Y2O3 content on gradient bioceramic composite coating was studied. The experimental results indicate that adding rare earth can refine grain. Different rare earth contents affect formation of HA and β-TCP in bioceramic coating. When the content of rare earth ranges from 0.4% to 0.6%, the active extent of rare earth in synthesizing HA and β-TCP is the best, which indicates that “monosodium glutamate” effect of rare earth plays a dominant role. However, when rare earth content is up to 0.8%, the amount of synthesizing HA and β-TCP in coating conversely goes down, which demonstrates that rare earth gradually losts its catalysis in manufacturing HA and β-TCP.
文摘Cored wires for electric arc spraying of Al/Al 2 O 3 MMC coatings were developed, with Al 2 O 3 powder as the core material and commercial aluminium strip as the retaining sheath. The bond strength, Al 2 O 3 content, microstructure, micro-hardness and wear resistance of coatings produced by arc spraying of the cored wires were experimentally investigated and were compared with those of pure aluminum coating.
基金This work is financially supported by the Scientific Research Foundation for Young Teachers of Anhui Province, China (No. 2006jql082).
文摘Cobalt-based alloys with different Y2O3 contents were deposited on Q235A-carbon steel using plasma transferred arc （PTA） welding machine. The effect of Y2O3 on the microstructure and wear resistance properties of the cobait-based alloys were investigated using an optical microscope, a scanning electron microscope （SEM）, X-ray diffraction （XRD）, and transmission electron microscopy （TEM）. It was found that a cobalt-based solid solution with a face-centered cubic crystal structure was presented accompanied by the secondary phase M7C3 with a hexagonal crystal structure in the Y2O3-free cobalt-based alloy coating. Several stacking faults exist in the cobalt-based solid solution. The addition of Y2O3 leads to the existence of the Y2O3 phase in the Y2O3-modified coatings. Though stacking fault exists in the Y2O3-modified coatings, its density increases. The addition of Y2O3 can refine the microstructure and can increase the wear resistance properties when its contents are less than or equal to 0.8 wt.%. However, further increase of its contents will lead to the agglomeration of undissolved Y2O3 particles at the γ-Co grain boundary, and will lead to a coarse microstructure and lower wear resistance properties.
基金supported by the Science Technology Foundation of Shanghai (072305113)the Program for Professor of Special Appointment (Eastern Scholar) at Shanghai Institutions of Higher Learning and Science Technology Foundation of Shanghai Institute of Technology (KJ2008-07)
文摘TiB2 and Dy2O3 were used as codeposited particles in the preparation of Ni-TiB2-Dy2O3 composite coatings to improve its performance. Ni-TiB2-Dy2O3 composite coatings were prepared by electrodeposition method with a nickel cetyltrimethylammonium bromide and hexadecylpyridinium bromide solution containing TiB2 and Dy2O3 particles. The content of codeposited TiB2 and Dy2O3 in the composite coatings was controlled by adding TiB2 and Dy2O3 particles of different concentrations into the solution, respectively. The effects of TiB2 and Dy2O3 content on microhardness, wear mass loss and friction coefficients of composite coatings were investigated. The composite coatings were characterized by X-ray diffraction （XRD）, inductively coupled plasma-atomic emission spectrometer （ICP-AES） and scanning electron microscopy （SEM） techniques. Ni-TiBE-Dy2O3 composite coatings showed higher microhardness, lower wear mass loss and friction coefficient compared with those of the pure Ni coating and Ni-TiB2 composite coatings. The wear mass loss of Ni-TiB2-Dy2O3 composite coatings was 9 and 1.57 times lower than that of the pure Ni coating and Ni-TiB2 composite coatings, respectively. The friction coefficient of pure Ni coating, Ni-TiB2 and Ni-TiB2-Dy2O3 composite coatings were 0.723, 0.815 and 0.619, respectively. Ni-TiBE-Dy2O3 composite coatings displayed the least friction coefficient among the three coatings. Dy2O3 particles in composite coatings might serve as a solid lubricant between contact surfaces to decrease the friction coefficient and abate the wear of the composite coatings. The loading-bearing capacity and the wear-reducing effect of the Dy2O3 particles were closely related to the content of Dy2O3 particles in the composite coatings.
基金financially supported by the Ministry of Education of China(No.625010312)
文摘Al2O3-metal composite coatings with different reactants and diluents were fabricated on mild steel plate with nonpressure combustion synthesis process. The coat-ings were characterized by means of X-ray diffraction, scanning electron microscopy, and energy-dispersive spec-trometry, respectively. Thermal shock tests were carried out to determine the bond strength of the coating with the steel substrate. The results indicate that the coating is composed of α-A1203, α-（Fe-Cr） and Al2SiO5 as the main phases. It is found that the coating with the diluents of Al2O3-SiO2 and transition layer of Al2O3-Cr presents the hi.ghest hardness of 2270 HV0.2 and the lowest porosity of 3.93 %. Owing to a metallurgical bond of the coating-to-substrate, the coating exhibits a good thermal shock resistance.
基金Funded by the National Natural Science Foundation of China(No.51401155)the School Foundation(No.XAGDXJJ1012)The Open Fund of Shaanxi Key Laboratory of Photoelectric Functional Materials and Devices(No.ZSKJ201416)
文摘ZrO2-Y2O3 ceramic coating was produced by plasma electrolytic oxidation （PEO） on ZAlSil2Cu3Ni2 alloy. The microstructure and phase composition of the coating were investigated by SEM and XRD.： The results show that adding an appropriate amount of yttrium ion can improve the growing rate of ceramic coating at different oxidation stages and decrease arc voltage. The thickness of ZrO2-Y2O3 coating is 16 μn thicker than that of ZrO2 coating and the maximum oxidation rate improves by 0.6 μm/min. In addition, the arc voltage decreases from 227 to 172 V. It can be seen that the rate of oxidation firstly increases to some extent and then decreases with the content of yttrium ion increasing. The growth rate reaches the maximum while the content of yttrium ion is 0.05 g-L-1The maximum thickness is 90 μm.Compared to ZrO2 coating, the micropores of ZrO2-Y2O3 coating are less and the ceramic layer is repeatedly deposited by ZrO2 and Y2O3 ceramic particles. Meanwhile, the binding force between coating and substrate is better and the coating is uniform and compact. The ceramic layer is mainly composed of c-Y0.15Zr0.85O1.93□0.07, m-ZrO2, α-Al2O3, ,γ-Al2O3 and Y2O3. It is indicated that ZrO2 has beert fully stabilized by yttrium ion through the formation of solid solution.
文摘Two types of plasma sprayed coatings (NiCrAlY and NiCrAlY-A12O3) were remelted by a 5 kW cw CO2 laser. With increasing laser power and decreasing traverse speed in the ranges of 200-700 W and 5-30 mm/s respectively, the melted track grew in width and depth. In the optimum range of laser parameters, a homogeneous remelted layer without voids, cavities, unmelted particles and microcracks was formed. On the surface of remelted layers, Al203 and YAIO3 were detected. As a result of isothermal oxidation tests, weight gains of laser remelted coatings were obviously lower than that only plasma sprayed, especially laser remelted NiCrAlY-Al2O3 coatings. The effects of laser remelting and incorporation of A12O3 second phase in N1CrAlY matrix on high temperature oxidation resistance were discussed.
基金the Ministerial Level Advanced Research Foundation (1040020440703)
文摘Rules and mechanism of damage in Al2O3 coatings irradiated by CO2 CW laser are studied in order to improve the ability of parts of equipment standing against the high power laser. Al2O3 coatings were sprayed by air plasma spray（APS） on the 45^# steel substrate, and then were irradiated by CO2 CW laser from 795 W/cm^2 to 31 830 W/cm^2. As the output power of the laser is increasing, its porosity is increasing and cracks are appearing and spreading quickly, And also the phase will transform from γ-Al2O3 to a-Al2O3 in the damaged areas. When the energy density is 17 507 W/cm^2, the coatings are destroyed completely. The thermal infection field on substrate is rather small. The laser energy is depleted by the phase transformation and cracks in Al2O3 coatings during the laser thermal shock.
基金financial supports from the National High-Tech Research and Development Program of China("863"Program,863-715-23-01-02)the National Natural Science Foundation of China(No.59441009).
文摘NiCoCrAlY-ZrO2·Y2O3 coatings were deposited on the substrates by using a technology of combining electron,atom and ion beams （three beams）. Isothermal oxidation for these samples was performed at 1100℃ for 100-300 h. The results show that a thermally grown oxide （TGO） layer was formed between NiCoCrAlY layer and oxidation. The TGO contains α-Al2O3 and Y4Al2O9 etc. oxides. The intensity ratio of α-Al2O3/Y4Al2O9 was monotonously decreased with increasing oxidation time based on XRD （X-ray diffraction） analysis. The Y4Al2O9 phase plays the most important role in high temperature oxidation resistance at 1100℃. The related mechanism was also discussed.
基金Item Sponsored by Provincial Natural Science Foundation of Jiangsu of China(BK2000012)
文摘The composite coating was prepared by thermal spray welding after making composite powder,which is composed of Ni-based self-melted alloy and AlOceramic powder including nano,sub-micron and micron powders.The influences of contents and sizes of AlOon the structure and wearability were investigated.The results show that the wear resistance of the coating would be increased greatly by adding AlO,but the spray weldability decreases with increasing AlOcontent.So there is an optimal content of AlOpowder.The composite coating with AlOnano or sub-micron powder of 0.5% has the best abrasive resistance,while the optimal content of AlOmicron powder is 1 %.
基金the National Natural Science Foundation of China (No50635030)the National Basic Research of China (No2007CB616913)the Program for New Century Excellent Talents in University (2005)
文摘Metal and nano-ceramic nanocomposite coatings were prepared on the gray cast iron surface by the electrodeposition method. The Ni-Co was used as the metal matrix,and nano-Al2O3 was chosen as the second-phase particulates. To avoid poor inter-face bonding and stress distribution,the gradient structure of biology materials was found as the model and therefore the gradient composite coating was prepared. The morphology of the composite coatings was flatter and the microstructure was denser than that of pure Ni-Co coatings. The composite coatings were prepared by different current densities,and the 2-D and 3-D morphologies of the surface coatings were observed. The result indicated that the 2-D structure became rougher and the 3-D surface density of apices became less when the current density was increased. The content of nanoparticulates reached a maximum value at the current density of 40mA·cm^-2,at the same time the properties including microhardness and wear-resistance were analyzed. The microhardness reached a maximum value and the wear volume was also less at the current density of 40mA·cm^-2. The reason was that nano-Al2O3 particles caused dispersive strengthening and grain refining.
基金This project was supported by The National Natural Science Foundation of China (Grant No. 59801002).
文摘A new technique-series electro-pulse discharge (SEPD)-was developed as a sur-face coating process. In this technique, both positive and negative poles of a pulse power were used as the depositing electrodes with the substrate alloy as an induction electrode. Fe-Cr and Fe-Cr-Y2O3 micro-crystalline coatings were deposited on stain-less steel (Fe-18Cr-8Ni) surfaces. Oxidation at 950℃ in ambient air showed that the coatings greatly improved the oxidation resistance of the steel. The addition of dis-persed Y2O3 nano-particles into the alloy coatings was found to further reduce the scaling rate and enhance the adhesion of oxide scales.
基金Funded by the national Natural Science Foundation of China (No. 51075293)the Foundation for Development of Science and Technology of Taiyuan University of Technology,China(No.K201014)
文摘To improve the wear resistance and corrosion resistance of magnesium alloys, a 5 kW continuous wave CO2 laser was used to investigate the laser surface cladding on AZ31 B magnesium alloys with Al-Si/Al2O3-TiO2 composite powders. A detailed microstructure, chemical composition, and phase analysis of the composite coatings were studied by scanning electron microscopy （SEM）, energy dispersive spectroscopy （EDS）, and X-ray diffraction （XRD）. The laser cladding shows good metallurgical bonding with the substrate. The composite coatings are composed of Mgl7Al12, Al3Mg2, Mg2Si, Al2O3, and TiO2 phases. Compared to the average microhardness （50HV0.05） of the AZ3 1 B substrate, that of the composite coatings （230HV0.05） is improved significantly. The wear resistances of the surface layers were evaluated in detail. The results demonstrate that the wear resistances of the laser surface-modified samples are considerably improved compared to the substrate. It also show that the composite coatings exhibit better corrosion resistance than that of the substrate in 3.5wt% NaCI solution.
基金This research was supported by Jilin Province Science Foundation （No. 20090552）.
文摘Al2O3p/Al composite coatings were prepared on the surface of AZ31 magnesium alloy by plasma spraying technology with mixed powders of Al and Al2O3. An orthogonal test containing six factors and five levels was carried out to acquire the optimum technical parameters. Mierostruetures and properties of the composite coatings were studied. The results show that the coatings consist of Al2O3 particulates distributed uniformly and Al matrix, and the interface between the particulate and matrix is continuous, compact and clean. With increasing the mass fraction of Al2O3 in the mixed powders, the volume fraction of Al2O3 in the coatings iacreases. The Al2O3p/Al composite coating with 14% Al2O3 volume fraction has more compact microstrueture and more satisfactory properties.
基金Project supported by the Ministry of Education,Science Technology(MEST)Korea Industrial Technology Foundation(KOTEF)through the Human Resource Training Project for Regional Innovation
文摘To improve the durability of underwater rotating products,the corrosion characteristics in harsh marine environment were evaluated through various electrochemical experiments on the Al2O3-3TiO2 and CoNiCrAlY coating layers by atmospheric pressure plasma spray coating process.By evaluating the corrosion resistance of these materials,their applicability to environmentally friendly power generation equipment such as blades of tidal current turbines was examined.According to the Tafel analysis for micro-areas including the coating layer,the coating/metal interlayer and the base metal,the Al2O3-3TiO2 coating layer and the CoNiCrAlY coating layer show markedly lower corrosion current density than the base metal.The corrosion current density of the CoNiCrAlY coating layer (9.75316×10-8A/cm2) is about 1.6 times more than that of the Al2O3-3TiO2 coating layer (6.13139×10-8A/cm2).
文摘A newly developed method is introduced for producing Cr 2O 3 base ceramic coating on aluminum alloys. On the basis of properly selecting base reactions, slurry is prepared and then applied onto the substrate surface. By chemical reactions taken place in situ on the surface of aluminum alloy at relative low temperature, Cr 2O 3 base ceramic coating is formed. By means of scanning electron microscopy, the coating microstructure and the bonding mechanism are studied. X ray diffraction analysis is also used to investigate the chemical composition of the coating. The coating formation mechanism is further discussed. With a pin on disk tester, wear test is made to evaluate the wear performances of the coating. The results show that by applying the coating on aluminum alloy, the wear decreases 5 times in comparation to that without coating.
文摘The conventional Al2O3-13 wt. % TiO2 composite ceramic coatings are fabricated by plasma spraying on the surface of extrusion wheel. The microstrueture, morphology and phase compositions of the substrate and coat- ing are investigated by using X-ray diffractometry （XRD） , scanning electron microsopy （SEM） and energy dis- persive spectroscopy （EDS）. Moreover, the microhardness of the substrate and the coating are investigated using Vickers mierohardness tester, the friction and wear behaviors of the substrate and the coating are investigated by using a block-on-ring tribometer under dry sliding conditions with the load of 245 N. The results show that both γ-Al2O3 and α-Al2O3 phases are observed in the as-sprayed coatings, the mian phase is γ-Al2O3. There are white particulates Al2O3 on its surface. The Al2O3-13 wt. % TiO2 coating possesses higher mierohardness which is about 1018HV and 1.6 times that of the substrate. The wear performance of coating is better than that of the substrate. In a practical application, the life of the extrusion wheel which is plasma sprayed Al2O3-13 wt. % TiO2 coating on the surface is 1.2 times that of the conventional extrusion wheel, and the life is about 330 h.
文摘SS304 is a commercial grade stainless steel which is used for various engineering applications like shafts, guides, jigs, fixtures, etc. Ceramic coating of the wear areas of such parts is a regular practice which significantly enhances the Mean Time Between Failure (MTBF). The final coating quality depends mainly on the coating thickness, surface roughness and hardness which ultimately decides the life. This paper presents an experimental study to effectively optimize the Atmospheric Plasma Spray (APS) process input parameters of Al<sub>2</sub>O<sub>3</sub>-40% TiO2 ceramic coatings to get the best quality of coating on commercial SS304 substrate. The experiments are conducted with a three-level L<sub>18</sub> Orthogonal Array (OA) Design of Experiments (DoE). Critical input parameters considered are: spray nozzle distance, substrate rotating speed, current of the arc, carrier gas flow and coating powder flow rate. The surface roughness, coating thickness and hardness are considered as the output parameters. Mathematical models are generated using regression analysis for individual output parameters. The Analytic Hierarchy Process (AHP) method is applied to generate weights for the individual objective functions and a combined objective function is generated. An advanced optimization method, Teaching-Learning-Based Optimization algorithm (TLBO), is applied to the combined objective function to optimize the values of input parameters to get the best output parameters and confirmation tests are conducted based on that. The significant effects of spray parameters on surface roughness, coating thickness and coating hardness are studied in detail.