We report the thickness dependence of critical current density （Jc） in YBa2Cu3O7-x （YBCO） films with BaZrO3 （BZO） and Y2O3 additions grown on single crystal LaAlO3 substrates by metalorganic deposition using tri...We report the thickness dependence of critical current density （Jc） in YBa2Cu3O7-x （YBCO） films with BaZrO3 （BZO） and Y2O3 additions grown on single crystal LaAlO3 substrates by metalorganic deposition using trifluoroacetates （TFA-MOD）. Comparing with pttre YBCO films, the Jc of BZO/Y2O3-doped YBCO films was significantly enhanced. It was also found that with the increase of the thickness of YBCO film from 0.25 μm to 1.5 μm, the Ic of BZO/Y2O3-doped YBCO film increased from 130 A/cm to 250 A/cm and yet Jc of YBCO film decreased from 6.5 MA/cm2 to 2.5 M A/cm2. The thick BZO/Y2O3-doped MOD-YBCO film showed lower Jc, which is mainly attributed to the formation of a-axis grains and pores.展开更多
To upgrade the electric properties of lead-free piezoceramics,(1-x)(Ba_(0.98)Ca_(0.02)Ti_(0.94)Sn_(0.04)Zr_(0.02))O_(3)-xY_(2)O_(3)(abbreviated as(1-x)BCTSZ-xY,x=0 mol%,0.02 mol%,0.04 mol%,0.06 mol%,0.08 mol%and 0.1 m...To upgrade the electric properties of lead-free piezoceramics,(1-x)(Ba_(0.98)Ca_(0.02)Ti_(0.94)Sn_(0.04)Zr_(0.02))O_(3)-xY_(2)O_(3)(abbreviated as(1-x)BCTSZ-xY,x=0 mol%,0.02 mol%,0.04 mol%,0.06 mol%,0.08 mol%and 0.1 mol%)ceramics were successfully synthesized by traditional solid-state sintering method.The phase structure and microstructure of ceramics were investigated by X-ray diffraction(XRD),scanning electron microscopy(SEM)and piezoresponse force microscopyeramics(PFM).The electric properties of ceramics were researched through piezoelectric,dielectric and ferroelectric test instruments.The results show that all samples have pure perovskite structure and favorable electric properties.The optimal electric properties which especially include superior ferroelectric properties are gained when Y_(2)O_(3)content is 0.06 mol%(d_(33)=419 pC/N,k_(p)=52%,T_(c)=89.5℃,ε_(r)=26900,tanδ=2.86%,P_(r)=14.41μC/cm^(2),Ec=1.8 kV/cm).Moreover,the temperature-dependent dielectricity of samples shows apparent relaxor behavior under different frequencies.The Curie-Weiss law further proves that all samples are typical relaxor ferroelectrics,and the relaxor degree of samples decreases with increase of Y_(2)O_(3)content.In conclusion,Y_(2)O_(3)plays a significant role in enhancing electric properties of BCTSZ ceramics.展开更多
基金supported by the National Natural Science Foundation of China(Grant No.51272250)the National Basic Research Program of China(Grant No.2011CBA00105)+1 种基金the National High Technology Research and Development Program of China(Grant No.2014AA032702)the Beijing Natural Science Foundation,China(Grant No.2152035)
文摘We report the thickness dependence of critical current density （Jc） in YBa2Cu3O7-x （YBCO） films with BaZrO3 （BZO） and Y2O3 additions grown on single crystal LaAlO3 substrates by metalorganic deposition using trifluoroacetates （TFA-MOD）. Comparing with pttre YBCO films, the Jc of BZO/Y2O3-doped YBCO films was significantly enhanced. It was also found that with the increase of the thickness of YBCO film from 0.25 μm to 1.5 μm, the Ic of BZO/Y2O3-doped YBCO film increased from 130 A/cm to 250 A/cm and yet Jc of YBCO film decreased from 6.5 MA/cm2 to 2.5 M A/cm2. The thick BZO/Y2O3-doped MOD-YBCO film showed lower Jc, which is mainly attributed to the formation of a-axis grains and pores.
基金Project supported by the Guizhou Province Graduate Research Fund(YJSCXJH2020029)Specialized Funds from Industry and Information Technology Department of Guizhou Province(2016056)+1 种基金the National Natural Science Foundation of China(51602066)High-level Innovative Talents Plan of Guizhou Province((2015)4009)。
文摘To upgrade the electric properties of lead-free piezoceramics,(1-x)(Ba_(0.98)Ca_(0.02)Ti_(0.94)Sn_(0.04)Zr_(0.02))O_(3)-xY_(2)O_(3)(abbreviated as(1-x)BCTSZ-xY,x=0 mol%,0.02 mol%,0.04 mol%,0.06 mol%,0.08 mol%and 0.1 mol%)ceramics were successfully synthesized by traditional solid-state sintering method.The phase structure and microstructure of ceramics were investigated by X-ray diffraction(XRD),scanning electron microscopy(SEM)and piezoresponse force microscopyeramics(PFM).The electric properties of ceramics were researched through piezoelectric,dielectric and ferroelectric test instruments.The results show that all samples have pure perovskite structure and favorable electric properties.The optimal electric properties which especially include superior ferroelectric properties are gained when Y_(2)O_(3)content is 0.06 mol%(d_(33)=419 pC/N,k_(p)=52%,T_(c)=89.5℃,ε_(r)=26900,tanδ=2.86%,P_(r)=14.41μC/cm^(2),Ec=1.8 kV/cm).Moreover,the temperature-dependent dielectricity of samples shows apparent relaxor behavior under different frequencies.The Curie-Weiss law further proves that all samples are typical relaxor ferroelectrics,and the relaxor degree of samples decreases with increase of Y_(2)O_(3)content.In conclusion,Y_(2)O_(3)plays a significant role in enhancing electric properties of BCTSZ ceramics.