In this study, we have explored the ways to fabricate and optimize high-quality ultrathin YBa2 Cu3 O7-δ(YBCO) films grown on single-crystal(001) SrTiO3 substrates. Nearly atomic-flat YBCO films are obtained by pulsed...In this study, we have explored the ways to fabricate and optimize high-quality ultrathin YBa2 Cu3 O7-δ(YBCO) films grown on single-crystal(001) SrTiO3 substrates. Nearly atomic-flat YBCO films are obtained by pulsed laser deposition.Our result shows that the termination of SrTiO3 has only a negligible effect on the properties of YBCO. In contrast, we found that capping a non-superconducting oxide layer can generally enhance the superconductivity of YBCO. PrBa2 Cu3 O7,La2 CuO4, LaMnO3, SrTiO3, and LaAlO3 have been examined as capping layers, and the minimum thickness of superconducting YBCO with capping is ~ 2 unit cells–3 unit cells. This result might be useful in constructing good-performance YBCO-based field effect devices.展开更多
YBa2Cu3O7-x（YBCO） films with co-doping BaTiO3（BTO） and Y2O3 nanostructures were prepared by metal organic deposition using trifluoroacetates（TFA-MOD）. The properties of the BTO/Y2O3co-doped YBCO films with diffe...YBa2Cu3O7-x（YBCO） films with co-doping BaTiO3（BTO） and Y2O3 nanostructures were prepared by metal organic deposition using trifluoroacetates（TFA-MOD）. The properties of the BTO/Y2O3co-doped YBCO films with different excess yttrium have been systematically studied by x-ray diffraction（XRD）, Raman spectra, and scanning electron microscope（SEM）. The optimized content of yttrium excess in the BTO/Y2O3co-doped YBCO films is 10 mol.%, and the critical current density is as high as - 17 mA/cm^2（self-field, 65 K） by the magnetic signal. In addition, the Y2Cu2O5 was formed when the content of yttrium excess increases to 24 mol.%, which may result in the deterioration of the superconducting properties and the microstructure. The unique combination of the different types of nanostructures of BTO and Y2O3 in the doped YBCO films, compared with the pure YBCO films and BTO doped YBCO films, enhances the critical current density（JC） not only at the self-magnetic field, but also in the applied magnetic field.展开更多
We report the thickness dependence of critical current density （Jc） in YBa2Cu3O7-x （YBCO） films with BaZrO3 （BZO） and Y2O3 additions grown on single crystal LaAlO3 substrates by metalorganic deposition using tri...We report the thickness dependence of critical current density （Jc） in YBa2Cu3O7-x （YBCO） films with BaZrO3 （BZO） and Y2O3 additions grown on single crystal LaAlO3 substrates by metalorganic deposition using trifluoroacetates （TFA-MOD）. Comparing with pttre YBCO films, the Jc of BZO/Y2O3-doped YBCO films was significantly enhanced. It was also found that with the increase of the thickness of YBCO film from 0.25 μm to 1.5 μm, the Ic of BZO/Y2O3-doped YBCO film increased from 130 A/cm to 250 A/cm and yet Jc of YBCO film decreased from 6.5 MA/cm2 to 2.5 M A/cm2. The thick BZO/Y2O3-doped MOD-YBCO film showed lower Jc, which is mainly attributed to the formation of a-axis grains and pores.展开更多
Superconducting thin films are widely used in superconducting quantum interferometers,microwave devices,etc.The electrical performance of a superconducting thin film is often affected by structural deformation or stre...Superconducting thin films are widely used in superconducting quantum interferometers,microwave devices,etc.The electrical performance of a superconducting thin film is often affected by structural deformation or stress.Based on four-point bending of a Cu-Be beam,we constructed a device that could apply uniaxial,uniform.compressive strain to a superconducting thin film at both room temperature and the temperature of liquid nitrogen.The thin film was placed into a slot carved in the Cu-Be beam.We optimized the size of this slot via numerical simulation.Our results indicated that the slot width was optimal when it was same as the width of the Cu-Be beam.Notably,the sample bended hardly after machining two slits along width direction on both sides of the slot.A YBa2Cu3O7-δSrTiO3(YBCO-STO)film was used as an example.It was loadedby the aforementioned device to determine its electrical characteristics as functions of the uniaxial-uniform-compressive strain.The optimized design allowed the sample to be compressed to a larger strain without breaking it.展开更多
基金Project supported by the National Key Research and Development Program of the Ministry of Science and Technology of China(Grants Nos.2017YFA0303002and 2016YFA0300204)the Fundamental Research Funds for the Central Universities,China
文摘In this study, we have explored the ways to fabricate and optimize high-quality ultrathin YBa2 Cu3 O7-δ(YBCO) films grown on single-crystal(001) SrTiO3 substrates. Nearly atomic-flat YBCO films are obtained by pulsed laser deposition.Our result shows that the termination of SrTiO3 has only a negligible effect on the properties of YBCO. In contrast, we found that capping a non-superconducting oxide layer can generally enhance the superconductivity of YBCO. PrBa2 Cu3 O7,La2 CuO4, LaMnO3, SrTiO3, and LaAlO3 have been examined as capping layers, and the minimum thickness of superconducting YBCO with capping is ~ 2 unit cells–3 unit cells. This result might be useful in constructing good-performance YBCO-based field effect devices.
基金Project supported by the National Natural Science Foundation of China(Grant No.51272250)the National Basic Research Program of China(Grant No.2011CBA00105)+1 种基金the National High Technology Research and Development Program of China(Grant No.2014AA032702)the Natural Science Foundation of Beijing,China(Grant No.2152035)
文摘YBa2Cu3O7-x（YBCO） films with co-doping BaTiO3（BTO） and Y2O3 nanostructures were prepared by metal organic deposition using trifluoroacetates（TFA-MOD）. The properties of the BTO/Y2O3co-doped YBCO films with different excess yttrium have been systematically studied by x-ray diffraction（XRD）, Raman spectra, and scanning electron microscope（SEM）. The optimized content of yttrium excess in the BTO/Y2O3co-doped YBCO films is 10 mol.%, and the critical current density is as high as - 17 mA/cm^2（self-field, 65 K） by the magnetic signal. In addition, the Y2Cu2O5 was formed when the content of yttrium excess increases to 24 mol.%, which may result in the deterioration of the superconducting properties and the microstructure. The unique combination of the different types of nanostructures of BTO and Y2O3 in the doped YBCO films, compared with the pure YBCO films and BTO doped YBCO films, enhances the critical current density（JC） not only at the self-magnetic field, but also in the applied magnetic field.
基金supported by the National Natural Science Foundation of China(Grant No.51272250)the National Basic Research Program of China(Grant No.2011CBA00105)+1 种基金the National High Technology Research and Development Program of China(Grant No.2014AA032702)the Beijing Natural Science Foundation,China(Grant No.2152035)
文摘We report the thickness dependence of critical current density （Jc） in YBa2Cu3O7-x （YBCO） films with BaZrO3 （BZO） and Y2O3 additions grown on single crystal LaAlO3 substrates by metalorganic deposition using trifluoroacetates （TFA-MOD）. Comparing with pttre YBCO films, the Jc of BZO/Y2O3-doped YBCO films was significantly enhanced. It was also found that with the increase of the thickness of YBCO film from 0.25 μm to 1.5 μm, the Ic of BZO/Y2O3-doped YBCO film increased from 130 A/cm to 250 A/cm and yet Jc of YBCO film decreased from 6.5 MA/cm2 to 2.5 M A/cm2. The thick BZO/Y2O3-doped MOD-YBCO film showed lower Jc, which is mainly attributed to the formation of a-axis grains and pores.
基金Project (50972019) supported by the National Natural Science Foundation of ChinaProject (2011CBA00105) supported by the National Basic Research Program of China
基金the National Natural Science Foundation of China(Grants 11622217,11872196,and11902130)the Fundamental ResearchFunds for the Central Universities(Grant lzujbky-2018-9).
文摘Superconducting thin films are widely used in superconducting quantum interferometers,microwave devices,etc.The electrical performance of a superconducting thin film is often affected by structural deformation or stress.Based on four-point bending of a Cu-Be beam,we constructed a device that could apply uniaxial,uniform.compressive strain to a superconducting thin film at both room temperature and the temperature of liquid nitrogen.The thin film was placed into a slot carved in the Cu-Be beam.We optimized the size of this slot via numerical simulation.Our results indicated that the slot width was optimal when it was same as the width of the Cu-Be beam.Notably,the sample bended hardly after machining two slits along width direction on both sides of the slot.A YBa2Cu3O7-δSrTiO3(YBCO-STO)film was used as an example.It was loadedby the aforementioned device to determine its electrical characteristics as functions of the uniaxial-uniform-compressive strain.The optimized design allowed the sample to be compressed to a larger strain without breaking it.