YBa2Cu3O7-δ-Agx composite superconductors were prepared by hybrid sintering process using YBa2Cu3O7-δ-Agx ultrafine powder and Ag2O finepower, which were prepared by sol-gel process and precipitation process respect...YBa2Cu3O7-δ-Agx composite superconductors were prepared by hybrid sintering process using YBa2Cu3O7-δ-Agx ultrafine powder and Ag2O finepower, which were prepared by sol-gel process and precipitation process respectively. The effect of the Ag content on superconducting crictical transition temperature of YBa2Cu3O7-δ-Agx was not evident as long as YBa2Cu3O7-δ-Agx can form continuous network. But Ag can increase superconduction crictical current and density of the composite superconductors. The normal state (i.e. non-superconducting state at room temperature) resistivity shows a percolation threshold at 20%-30% Ag, whereas the superconducting net-work shows a percolationthreshold at 70% -80% Ag.展开更多
文摘YBa2Cu3O7-δ-Agx composite superconductors were prepared by hybrid sintering process using YBa2Cu3O7-δ-Agx ultrafine powder and Ag2O finepower, which were prepared by sol-gel process and precipitation process respectively. The effect of the Ag content on superconducting crictical transition temperature of YBa2Cu3O7-δ-Agx was not evident as long as YBa2Cu3O7-δ-Agx can form continuous network. But Ag can increase superconduction crictical current and density of the composite superconductors. The normal state (i.e. non-superconducting state at room temperature) resistivity shows a percolation threshold at 20%-30% Ag, whereas the superconducting net-work shows a percolationthreshold at 70% -80% Ag.