YBa2Cu3O7-x （YBCO） superconducting film was fabricated on {001} LaAlO3 （LAO） substrate by pulse laser deposition （PLD）, and its microstructure was examined by high resolution X-ray diffraction technology （HRXRD...YBa2Cu3O7-x （YBCO） superconducting film was fabricated on {001} LaAlO3 （LAO） substrate by pulse laser deposition （PLD）, and its microstructure was examined by high resolution X-ray diffraction technology （HRXRD）, such as pole figure, rocking curve, reciprocal space mapping. The results show that the YBCO crystalline alignment is almost {001}YBCO//{001}LAO, 100YBCO//100LAO besides 2% {001}YBCO//{001}LAO, 110YBCO//100LAO. The out-plane alignment of YBCO is some spreading （the breadth is 0.75°）. There are 90°±0.65°110 twin domains in the film, which is caused by the high local stress and stress difference between 100 and 010 during the tetragonal to orthorhombic phase transition.展开更多
基金Project (50972019) supported by the National Natural Science Foundation of ChinaProject (2011CBA00105) supported by the National Basic Research Program of China
文摘YBa2Cu3O7-x （YBCO） superconducting film was fabricated on {001} LaAlO3 （LAO） substrate by pulse laser deposition （PLD）, and its microstructure was examined by high resolution X-ray diffraction technology （HRXRD）, such as pole figure, rocking curve, reciprocal space mapping. The results show that the YBCO crystalline alignment is almost {001}YBCO//{001}LAO, 100YBCO//100LAO besides 2% {001}YBCO//{001}LAO, 110YBCO//100LAO. The out-plane alignment of YBCO is some spreading （the breadth is 0.75°）. There are 90°±0.65°110 twin domains in the film, which is caused by the high local stress and stress difference between 100 and 010 during the tetragonal to orthorhombic phase transition.