A unidirectional reaction for synthesis of the high T_c superconductor YBa_2Cu_3O_x has been proposed, Its T_c is 90-94.5 K and △T is 1 K. The phase relationships in the system Y_2BaCuO_5-Y_2Cu_2O_5-CuO-YBa_2Cu_3O_x ...A unidirectional reaction for synthesis of the high T_c superconductor YBa_2Cu_3O_x has been proposed, Its T_c is 90-94.5 K and △T is 1 K. The phase relationships in the system Y_2BaCuO_5-Y_2Cu_2O_5-CuO-YBa_2Cu_3O_x were studied and discussed.展开更多
It is significant for low-cost preparation of YBa2Cu3O7-δ（YBCO） coated conductors to make clear the mechanism of orientation, copper segregation, and nucleation density in BaF2-derived YBCO crystallization. In the ...It is significant for low-cost preparation of YBa2Cu3O7-δ（YBCO） coated conductors to make clear the mechanism of orientation, copper segregation, and nucleation density in BaF2-derived YBCO crystallization. In the present work,a distinct nucleation mechanism was proposed based on a transient liquid phase induced by the size effect as well as near-equilibrium assumption. With this scheme the nucleation of YBCO prepared by metal–organic deposition（MOD） or the physical vapor deposition BaF2 process was semi-quantitatively analyzed, revealing that the direct driving force for nucleation is YBCO supersaturation in the liquid phase. The theoretical analysis on the nucleation orientation portion is evidenced by the experimental result.展开更多
Interfaces and surfaces of YBa_2Cu_3O_(7-x)(YBCO)-Ag have been studied by SEM-EDX and AES.No effect of Ag on 123 structure in X-ray diffraction pattern was observed for 0.4 mol Ag doped YBCO.AES analysis indicated tha...Interfaces and surfaces of YBa_2Cu_3O_(7-x)(YBCO)-Ag have been studied by SEM-EDX and AES.No effect of Ag on 123 structure in X-ray diffraction pattern was observed for 0.4 mol Ag doped YBCO.AES analysis indicated that Ag segregated on surface of YBCO and resulted in decrease of YBCO-metal lead resistance.In addition,solution and segregation of Ag as elemental state were often appeared on interfaces and surfaces of high temperature annealed YBCO,whether elemental Ag or compound Ag_2O and AgNO_3 adopted as doping material.展开更多
Large area YBCO superconducting thin films were grown on the Zr(Y)O2 substrate at 750 and 800℃ respectively by magnetron sputtering, and the surface morphology was studied with AEM. STM and SEM with an EDS and ECP at...Large area YBCO superconducting thin films were grown on the Zr(Y)O2 substrate at 750 and 800℃ respectively by magnetron sputtering, and the surface morphology was studied with AEM. STM and SEM with an EDS and ECP attachments. The YBCO thin film was found to be a caxis orientated single crystal. At 800℃, the surface out-growths of the thin film Were mainly CuO particles and many small holes were found on the surface. which resulted in rougher surface; whereas, at 750℃, the out-growths were mainly the 123 structure in the form of rod-like and polygon and the surface was much smoother because of less small holes on the surface. The mechanism of the thin film growth and the formation of the small holes on the surface grown at the two temperature were discussed.展开更多
YBa2Cu3O7-x(YBCO) thin film has been epitaxially deposited on (1120) sapphire with Y2O3-stabilized ZrO2 (YSZ) buffer layer and shown a high critical current density Jc of 1. 6×106A/cm2 at 77 K in zero magnetic fi...YBa2Cu3O7-x(YBCO) thin film has been epitaxially deposited on (1120) sapphire with Y2O3-stabilized ZrO2 (YSZ) buffer layer and shown a high critical current density Jc of 1. 6×106A/cm2 at 77 K in zero magnetic field. The orientation relationship of the multilayer film superconductor has been determined. The(001) plane of the YBCO film is parallel to the(100) surface of the YSZ intermediate layer. YSZ buffer layer with(100) preferred orientation is about 20 nm thick and contains element Ba, due to out-diffusion of Ba from YBCO layer. The(100) preferred orientation of YSZ buffer permits the growth of high quality YBCO thin film. Y2BaCuO5 precipitates with small size distribute uniformly in the YBCO thin film and it is favourable to raise critical current density Jc.展开更多
The patterning technologies and process order of high Tc(86K) super-conducting film bolometers have been studied. After the deposition, a conventional lithographic process was used to pattern the films with aqueous so...The patterning technologies and process order of high Tc(86K) super-conducting film bolometers have been studied. After the deposition, a conventional lithographic process was used to pattern the films with aqueous solution of HCl, and then the films were transferred into a tube furnace for annealing to form superconducting film. It eliminates the degradation of patterning process. The bolometric responsivity of approximately 34. 32 V/W is measured, and the detectivity is greater than 1. 62× 108cm · Hz1/2 · W-1, the noise equivalent powers NEP is 2. 1×10-9W.展开更多
It is well known that for technological application,a great effort has been done to enchance Jvalue ofsuperconducting YBaCuO sintered bulk.Except oxygen content,the main problem for increasing critical cur-rent densit...It is well known that for technological application,a great effort has been done to enchance Jvalue ofsuperconducting YBaCuO sintered bulk.Except oxygen content,the main problem for increasing critical cur-rent density Jis to eliminate the weak link and to control crystallographic anisotropy.It is necessary tomake YBaCuO superconducting bulk have a strong texture with C-axis orientation.Since Jin et al.has suc-展开更多
By means of X-ray diffraction investigations and electric resistivity measurements the tempera- ture dependence of phase structure and supercon- ductivity in YBa_2Cu_3O_(7_x) over the temperature range of 20℃-950℃ h...By means of X-ray diffraction investigations and electric resistivity measurements the tempera- ture dependence of phase structure and supercon- ductivity in YBa_2Cu_3O_(7_x) over the temperature range of 20℃-950℃ have been studied.The lattice parameters a,b and c as well as conductivity as a function of annealing temperatures can be roughly divided into three zones which are superconductive orthorhombic structure 1(a<b(?)c/3) at 20℃-500℃,normal conductive orthorhombic structure 2(a<b<c/3)from 550℃ to about 750℃ and semiconductive-like tetragonal structure (a=b<c/3)from about 800℃ to 950℃.However, the boundaries of the three zones is not much distinctive because there is a continuous transi- tion from the orthorhombic to tetragonal struc- ture.Furthermore,the processes of orthorhom- bic-tetragonal transition in the range of 350℃-950℃ are not only continuous but also reversible.The isothermal transition of orthorhombic 2 to orthorhombic 1 occurs at 350℃-500℃,while the maximum rate of transition and high T_c superconductivity can be obtained at about 460℃.This process of isothermal transition depends on the ordering of oxygen atoms or vacancies and the thermodynamic equilibrium to allow the oxygen diffusion.展开更多
The structural characteristics of different alkoxides of Y. Ba and Cu are studied with quantum chemi-cal CNDO /2 calculations. The relative hydrolysis rate coefficients k_M of them are obtained according tothe relati...The structural characteristics of different alkoxides of Y. Ba and Cu are studied with quantum chemi-cal CNDO /2 calculations. The relative hydrolysis rate coefficients k_M of them are obtained according tothe relationship between frontier orbitals and organic chemical reactions. Based on the above results. properexperimental conditions for the preparation of homogeneous ultra-purity. submicro high-T_cYBa_2Cu_3O_(7-δ) superconducting powders are proposed.展开更多
As a newly developed method for fabricating Josephson junctions,a focused helium ion beam has the advantage of producing reliable and reproducible junctions.We fabricated Josephson junctions with a focused helium ion ...As a newly developed method for fabricating Josephson junctions,a focused helium ion beam has the advantage of producing reliable and reproducible junctions.We fabricated Josephson junctions with a focused helium ion beam on our 50 nm YBa_(2)Cu_(3)O_(7-δ)(YBCO)thin films.We focused on the junction with irradiation doses ranging from 100 to 300 ions/nm and demonstrated that the junction barrier can be modulated by the ion dose and that within this dose range,the junctions behave like superconductor–normal conductor–superconductor junctions.The measurements of the I–V characteristics,Fraunhofer diffraction pattern,and Shapiro steps of the junctions clearly show AC and DC Josephson effects.Our findings demonstrate high reproducibility of junction fabrication using a focused helium ion beam and suggest that commercial devices based on this nanotechnology could operate at liquid nitrogen temperatures.展开更多
SHI irradiation method may be another method except in-situ growth techniques to generate one-dimensional defects in YBCO(YBa_(2)Cu_(3)O_(7)-x)films and has already been studied since 1990[1].
文摘A unidirectional reaction for synthesis of the high T_c superconductor YBa_2Cu_3O_x has been proposed, Its T_c is 90-94.5 K and △T is 1 K. The phase relationships in the system Y_2BaCuO_5-Y_2Cu_2O_5-CuO-YBa_2Cu_3O_x were studied and discussed.
基金Project supported by the Science and Technology Commission of Shanghai Municipality,China(Grant Nos.13111102300 and 11dz1100302)the National Natural Science Foundation of China(Grant Nos.11174193 and 51202141)+1 种基金the National Basic Research Program of China(Grant Nos.2011CBA00105)the Science and Technology Commission of Shanghai Municipality,China(Grant No.14DZ2260700)
文摘It is significant for low-cost preparation of YBa2Cu3O7-δ（YBCO） coated conductors to make clear the mechanism of orientation, copper segregation, and nucleation density in BaF2-derived YBCO crystallization. In the present work,a distinct nucleation mechanism was proposed based on a transient liquid phase induced by the size effect as well as near-equilibrium assumption. With this scheme the nucleation of YBCO prepared by metal–organic deposition（MOD） or the physical vapor deposition BaF2 process was semi-quantitatively analyzed, revealing that the direct driving force for nucleation is YBCO supersaturation in the liquid phase. The theoretical analysis on the nucleation orientation portion is evidenced by the experimental result.
文摘Interfaces and surfaces of YBa_2Cu_3O_(7-x)(YBCO)-Ag have been studied by SEM-EDX and AES.No effect of Ag on 123 structure in X-ray diffraction pattern was observed for 0.4 mol Ag doped YBCO.AES analysis indicated that Ag segregated on surface of YBCO and resulted in decrease of YBCO-metal lead resistance.In addition,solution and segregation of Ag as elemental state were often appeared on interfaces and surfaces of high temperature annealed YBCO,whether elemental Ag or compound Ag_2O and AgNO_3 adopted as doping material.
文摘Large area YBCO superconducting thin films were grown on the Zr(Y)O2 substrate at 750 and 800℃ respectively by magnetron sputtering, and the surface morphology was studied with AEM. STM and SEM with an EDS and ECP attachments. The YBCO thin film was found to be a caxis orientated single crystal. At 800℃, the surface out-growths of the thin film Were mainly CuO particles and many small holes were found on the surface. which resulted in rougher surface; whereas, at 750℃, the out-growths were mainly the 123 structure in the form of rod-like and polygon and the surface was much smoother because of less small holes on the surface. The mechanism of the thin film growth and the formation of the small holes on the surface grown at the two temperature were discussed.
文摘YBa2Cu3O7-x(YBCO) thin film has been epitaxially deposited on (1120) sapphire with Y2O3-stabilized ZrO2 (YSZ) buffer layer and shown a high critical current density Jc of 1. 6×106A/cm2 at 77 K in zero magnetic field. The orientation relationship of the multilayer film superconductor has been determined. The(001) plane of the YBCO film is parallel to the(100) surface of the YSZ intermediate layer. YSZ buffer layer with(100) preferred orientation is about 20 nm thick and contains element Ba, due to out-diffusion of Ba from YBCO layer. The(100) preferred orientation of YSZ buffer permits the growth of high quality YBCO thin film. Y2BaCuO5 precipitates with small size distribute uniformly in the YBCO thin film and it is favourable to raise critical current density Jc.
文摘The patterning technologies and process order of high Tc(86K) super-conducting film bolometers have been studied. After the deposition, a conventional lithographic process was used to pattern the films with aqueous solution of HCl, and then the films were transferred into a tube furnace for annealing to form superconducting film. It eliminates the degradation of patterning process. The bolometric responsivity of approximately 34. 32 V/W is measured, and the detectivity is greater than 1. 62× 108cm · Hz1/2 · W-1, the noise equivalent powers NEP is 2. 1×10-9W.
文摘It is well known that for technological application,a great effort has been done to enchance Jvalue ofsuperconducting YBaCuO sintered bulk.Except oxygen content,the main problem for increasing critical cur-rent density Jis to eliminate the weak link and to control crystallographic anisotropy.It is necessary tomake YBaCuO superconducting bulk have a strong texture with C-axis orientation.Since Jin et al.has suc-
文摘By means of X-ray diffraction investigations and electric resistivity measurements the tempera- ture dependence of phase structure and supercon- ductivity in YBa_2Cu_3O_(7_x) over the temperature range of 20℃-950℃ have been studied.The lattice parameters a,b and c as well as conductivity as a function of annealing temperatures can be roughly divided into three zones which are superconductive orthorhombic structure 1(a<b(?)c/3) at 20℃-500℃,normal conductive orthorhombic structure 2(a<b<c/3)from 550℃ to about 750℃ and semiconductive-like tetragonal structure (a=b<c/3)from about 800℃ to 950℃.However, the boundaries of the three zones is not much distinctive because there is a continuous transi- tion from the orthorhombic to tetragonal struc- ture.Furthermore,the processes of orthorhom- bic-tetragonal transition in the range of 350℃-950℃ are not only continuous but also reversible.The isothermal transition of orthorhombic 2 to orthorhombic 1 occurs at 350℃-500℃,while the maximum rate of transition and high T_c superconductivity can be obtained at about 460℃.This process of isothermal transition depends on the ordering of oxygen atoms or vacancies and the thermodynamic equilibrium to allow the oxygen diffusion.
文摘The structural characteristics of different alkoxides of Y. Ba and Cu are studied with quantum chemi-cal CNDO /2 calculations. The relative hydrolysis rate coefficients k_M of them are obtained according tothe relationship between frontier orbitals and organic chemical reactions. Based on the above results. properexperimental conditions for the preparation of homogeneous ultra-purity. submicro high-T_cYBa_2Cu_3O_(7-δ) superconducting powders are proposed.
基金supported by the National Key Research and Development Program of China(Grant No.2017YFC0601901)the National Natural Science Foundation of China(Grant No.61571019)。
文摘As a newly developed method for fabricating Josephson junctions,a focused helium ion beam has the advantage of producing reliable and reproducible junctions.We fabricated Josephson junctions with a focused helium ion beam on our 50 nm YBa_(2)Cu_(3)O_(7-δ)(YBCO)thin films.We focused on the junction with irradiation doses ranging from 100 to 300 ions/nm and demonstrated that the junction barrier can be modulated by the ion dose and that within this dose range,the junctions behave like superconductor–normal conductor–superconductor junctions.The measurements of the I–V characteristics,Fraunhofer diffraction pattern,and Shapiro steps of the junctions clearly show AC and DC Josephson effects.Our findings demonstrate high reproducibility of junction fabrication using a focused helium ion beam and suggest that commercial devices based on this nanotechnology could operate at liquid nitrogen temperatures.
基金National Natural Science Foundation of China(11675233,11690041,11705246)CAS“Light of West China”Program and Natural Science Foundation of Gansu Province(18JR3RA392)。
文摘SHI irradiation method may be another method except in-situ growth techniques to generate one-dimensional defects in YBCO(YBa_(2)Cu_(3)O_(7)-x)films and has already been studied since 1990[1].