The Er^3+/Yb^3+ co-doped TeO2-Nb2O5-Li2O glass is prepared by conventional melting method, and its upconversion spectra are measured. The intense green upconversion luminescence upon excitation with a 976 nm laser d...The Er^3+/Yb^3+ co-doped TeO2-Nb2O5-Li2O glass is prepared by conventional melting method, and its upconversion spectra are measured. The intense green upconversion luminescence upon excitation with a 976 nm laser diode is observed with the naked eyes. The dependence of luminescence intensity on the ratio of Yb^3+/Er^3+ is discussed in detail, and the relationship between the ratio of green luminescence intensity to red luminescence intensity and the ratio of Yb^3+/Er^3+ is also studied, The luminescence intensity increases with the ratio of Yb^3+/Er^3+ increasing. The ratio of Yb^3+/Er^3+ plays a more important role than the concentration of Er^3+ in determining the upconversion luminescence intensity. The ratio of green luminescence intensity to red luminescence intensity reaches a maximum when ratio of Yb^3+/Er^3+ is 3. Thus the glass could be one of the potential candidates for LD pumping solid-state lasers.展开更多
Spectral terms and J-spectral multiplet of low-spin 4f105d configuration of Er3+ were obtained with the method of ligand field theory. According to the selection rules for dipole transitions, the excitation spectr...Spectral terms and J-spectral multiplet of low-spin 4f105d configuration of Er3+ were obtained with the method of ligand field theory. According to the selection rules for dipole transitions, the excitation spectra of Er3+ doped in LiYF4 in vacuum ultraviolet region (120~160 nm) of the spectrum were theoretically interpreted by applying the crystal field model, and the six bands were assigned to the spin-allowed transitions from the ground state (4I15/2) to J-spectral multiplet of low-spin 4f105d configuration of Er3+ion.展开更多
This paper reports that the ultraviolet and visible upconversion luminescence from the ^4S3/2, ^2G9/2 and ^2P3/2 levels have been observed in Er^3+:YAG following 647.2 nm excitation of the ^4F9/2 multiple. Upconvers...This paper reports that the ultraviolet and visible upconversion luminescence from the ^4S3/2, ^2G9/2 and ^2P3/2 levels have been observed in Er^3+:YAG following 647.2 nm excitation of the ^4F9/2 multiple. Upconversion luminescence intensity dependence on pump power was recorded. The measured decay profiles were theoretically fitted by kinetics theory and the basically good agreements were achieved. The results indicate that some energy transfer processes proposed to explain the observed upconversion phenomena are reasonable.展开更多
We have investigated infrared-to-visible upconversion luminescence of Er^3+ in bismuth-lead-germanate glasses. The UV cutoff wavelength is shortened while its lifetime is increased almost linearly, with PbF2 substitu...We have investigated infrared-to-visible upconversion luminescence of Er^3+ in bismuth-lead-germanate glasses. The UV cutoff wavelength is shortened while its lifetime is increased almost linearly, with PbF2 substituting for PbO in the bismuth-lead germanate glasses. Three emissions centred at around 529, 545 and 657 nm are clearly observed, which are identified as originating from the ^2H11/2→^4 I15/2,^4S3/2→^4 I15/2 and ^4 F9/2 →^4 I15/2 transitions, respectively. It is noted that all the upconversion emission intensities increase with PbF2 concentration increasing. The ratio between the intensities of red and green emissions increases with the increasing of PbF2 content. Energy transfer processes and nonradiative phonon-assisted decays account for the populations of the ^2 H11/2,^4 S3/2 and ^4F 9/2 levels. The quadratic dependence of fluorescence on excitation laser power confirms a two-photon process to contribute to the upconversion emissions.展开更多
The luminescence of Er^3+:YAlO3 in ultraviolet visible and infrared ranges under the 518 nm excitation of the multiples ^2H11/2 have been investigated. Ultraviolet (275 nm and 318 nm), violet (405 nm and 413 nm)...The luminescence of Er^3+:YAlO3 in ultraviolet visible and infrared ranges under the 518 nm excitation of the multiples ^2H11/2 have been investigated. Ultraviolet (275 nm and 318 nm), violet (405 nm and 413 nm) and blue (474 nm) upconversion and infrared downconversion luminescence has been observed. By means of measuring the fluorescence decay curves and using the theory of rate equations, the luminescence kinetics was studied in detail and the processes of energy transfer upconversion (ETU) and excitation state absorption (ESA) were proposed to explain the upconversion phenomena.展开更多
A simple three-level system is proposed to produce high index of refraction with zero absorption in an Er^3+-doped yttrium aluminium garnet (YAG) crystal, which is achieved for a probe field between the excited sta...A simple three-level system is proposed to produce high index of refraction with zero absorption in an Er^3+-doped yttrium aluminium garnet (YAG) crystal, which is achieved for a probe field between the excited state 4I13/2 and ground state 4I15/2 by adjusting a strong coherent driving field between the upper excited state 4I11/2 and 4I15/2. It is found that the changes of the frequency of the coherent driving field and the concentration of Er^3+ ions in the YAG crystal can maximize the index of refraction accompanied by vanishing absorption. This result could be useful for the dispersion compensation in fibre communication, laser particle acceleration, high precision magnetometry and so on.展开更多
基金Project supported by the National Natural Science Foundation of China (Grant No 60307004) and the Science and Technology Program of Guangzhou, Guangdong province, China (Grant No 2004Z2-D0131).
文摘The Er^3+/Yb^3+ co-doped TeO2-Nb2O5-Li2O glass is prepared by conventional melting method, and its upconversion spectra are measured. The intense green upconversion luminescence upon excitation with a 976 nm laser diode is observed with the naked eyes. The dependence of luminescence intensity on the ratio of Yb^3+/Er^3+ is discussed in detail, and the relationship between the ratio of green luminescence intensity to red luminescence intensity and the ratio of Yb^3+/Er^3+ is also studied, The luminescence intensity increases with the ratio of Yb^3+/Er^3+ increasing. The ratio of Yb^3+/Er^3+ plays a more important role than the concentration of Er^3+ in determining the upconversion luminescence intensity. The ratio of green luminescence intensity to red luminescence intensity reaches a maximum when ratio of Yb^3+/Er^3+ is 3. Thus the glass could be one of the potential candidates for LD pumping solid-state lasers.
文摘Spectral terms and J-spectral multiplet of low-spin 4f105d configuration of Er3+ were obtained with the method of ligand field theory. According to the selection rules for dipole transitions, the excitation spectra of Er3+ doped in LiYF4 in vacuum ultraviolet region (120~160 nm) of the spectrum were theoretically interpreted by applying the crystal field model, and the six bands were assigned to the spin-allowed transitions from the ground state (4I15/2) to J-spectral multiplet of low-spin 4f105d configuration of Er3+ion.
基金Project supported by the National Natural Science Foundation of China (Grant No 10074020).Acknowledgement The authors would like to thank Professor Siyuan Zhang for providing Er^3+:YAG crystal.
文摘This paper reports that the ultraviolet and visible upconversion luminescence from the ^4S3/2, ^2G9/2 and ^2P3/2 levels have been observed in Er^3+:YAG following 647.2 nm excitation of the ^4F9/2 multiple. Upconversion luminescence intensity dependence on pump power was recorded. The measured decay profiles were theoretically fitted by kinetics theory and the basically good agreements were achieved. The results indicate that some energy transfer processes proposed to explain the observed upconversion phenomena are reasonable.
基金Project supported by the National Natural Science Foundation of China (Grant No 50472053), the Programme for New-Century Excellent Talents in Universities of Ministry of Education, China (Grant No NCET-04-0823) and the Natural Science Foundation of Guangdong Province, China (Grant No 04020036).
文摘We have investigated infrared-to-visible upconversion luminescence of Er^3+ in bismuth-lead-germanate glasses. The UV cutoff wavelength is shortened while its lifetime is increased almost linearly, with PbF2 substituting for PbO in the bismuth-lead germanate glasses. Three emissions centred at around 529, 545 and 657 nm are clearly observed, which are identified as originating from the ^2H11/2→^4 I15/2,^4S3/2→^4 I15/2 and ^4 F9/2 →^4 I15/2 transitions, respectively. It is noted that all the upconversion emission intensities increase with PbF2 concentration increasing. The ratio between the intensities of red and green emissions increases with the increasing of PbF2 content. Energy transfer processes and nonradiative phonon-assisted decays account for the populations of the ^2 H11/2,^4 S3/2 and ^4F 9/2 levels. The quadratic dependence of fluorescence on excitation laser power confirms a two-photon process to contribute to the upconversion emissions.
基金Project supported by the National Natural Science Foundation of China (Grant No 10074020).
文摘The luminescence of Er^3+:YAlO3 in ultraviolet visible and infrared ranges under the 518 nm excitation of the multiples ^2H11/2 have been investigated. Ultraviolet (275 nm and 318 nm), violet (405 nm and 413 nm) and blue (474 nm) upconversion and infrared downconversion luminescence has been observed. By means of measuring the fluorescence decay curves and using the theory of rate equations, the luminescence kinetics was studied in detail and the processes of energy transfer upconversion (ETU) and excitation state absorption (ESA) were proposed to explain the upconversion phenomena.
基金Project supported by the National Natural Science Foundation of China (Grant No 10334010).
文摘A simple three-level system is proposed to produce high index of refraction with zero absorption in an Er^3+-doped yttrium aluminium garnet (YAG) crystal, which is achieved for a probe field between the excited state 4I13/2 and ground state 4I15/2 by adjusting a strong coherent driving field between the upper excited state 4I11/2 and 4I15/2. It is found that the changes of the frequency of the coherent driving field and the concentration of Er^3+ ions in the YAG crystal can maximize the index of refraction accompanied by vanishing absorption. This result could be useful for the dispersion compensation in fibre communication, laser particle acceleration, high precision magnetometry and so on.