By using an Ar+ ion laser, a tunable Rh 6G dye laser(Linewidth: 0.5 cm -1) and a Coherent 899-21 dye laser as light sources and using a monochromator and a phase-locking amplifier, the optical properties of Eu 3+∶Y_2...By using an Ar+ ion laser, a tunable Rh 6G dye laser(Linewidth: 0.5 cm -1) and a Coherent 899-21 dye laser as light sources and using a monochromator and a phase-locking amplifier, the optical properties of Eu 3+∶Y_2SiO_5 crystal were detected. Persistent spectral hole burning (PSHB) were also observed in 5D_0-7F_0 transition in the crystal at the temperature of 16 K. For 15 mW dye laser (Wavelength: 579.62 nm) burning the crystal for 0.1 s a spectral hole with about 80 MHz hole width were detected and the hole can been keep for longer than 10 h.展开更多
By using a whitelight lamp, an Ar+ ion laser whosewavelength was tuned to 457. 9 nmand a tunable Rh 6G dye laser(linewidth: 0. 5 cm-1) pumped bythe second harmonic of a Nd: YAGlaser as light sources and using amonochr...By using a whitelight lamp, an Ar+ ion laser whosewavelength was tuned to 457. 9 nmand a tunable Rh 6G dye laser(linewidth: 0. 5 cm-1) pumped bythe second harmonic of a Nd: YAGlaser as light sources and using amonochromator, a phase-lockingamplifier and a computer as the data detecting system, the transmission spectrum, fluorescence spectra, excitation spectrum and siteselective fluorescence spectra ofthe Eu3+: Y2SiO5 crystal were observed. More than thirty out of thetotal fifty spectral lines were observed for 5D0→7F0,1,2,3,4 transitions. The Eu3+ ions occupy twokinds of the Y3+ sites with the lowsymmetry in this crystal. The difference of the wavelengths of thetwo Eu3+ sites for 7F0→5D0 transition is about 0. 2 nm. It was foundthat the two sites were nonequivalent optical ones at room temperature. Crystal lattice constants a,b, c, and β of Eu3+: Y2SiO5 werealso measured by the X-ray diffraction method. The results show thatthe lattice constants a, b, and cof the crystal doped Eu3+ ions isvery close to those of the Y2SiO5crystal undoped Eu3+ ions.展开更多
文章主要研究了Y_(2)SiO_(5):Pr^(3+)上转换纳米荧光粉对ZnO:Pr^(3+)的光催化性能的影响,通过XRD、FE-SEM、FL和UV-Vis对样品的物相、形貌、发光性能和光催化行性能进行了分析表征,实验结果表明:随着Y_(2)SiO_(5):Pr^(3+)上转换纳米荧...文章主要研究了Y_(2)SiO_(5):Pr^(3+)上转换纳米荧光粉对ZnO:Pr^(3+)的光催化性能的影响,通过XRD、FE-SEM、FL和UV-Vis对样品的物相、形貌、发光性能和光催化行性能进行了分析表征,实验结果表明:随着Y_(2)SiO_(5):Pr^(3+)上转换纳米荧光粉的加入量增加,ZnO:Pr^(3+)光催化效率逐渐提高,当加入0.2 g Y_(2)SiO_(5):Pr^(3+)时,光催化效率最高,在光照60 min后对亚甲基蓝的降解率达到了98.11%,相比未加入Y_(2)SiO_(5):Pr^(3+)时的光催化效率有显著提升。展开更多
文摘By using an Ar+ ion laser, a tunable Rh 6G dye laser(Linewidth: 0.5 cm -1) and a Coherent 899-21 dye laser as light sources and using a monochromator and a phase-locking amplifier, the optical properties of Eu 3+∶Y_2SiO_5 crystal were detected. Persistent spectral hole burning (PSHB) were also observed in 5D_0-7F_0 transition in the crystal at the temperature of 16 K. For 15 mW dye laser (Wavelength: 579.62 nm) burning the crystal for 0.1 s a spectral hole with about 80 MHz hole width were detected and the hole can been keep for longer than 10 h.
文摘By using a whitelight lamp, an Ar+ ion laser whosewavelength was tuned to 457. 9 nmand a tunable Rh 6G dye laser(linewidth: 0. 5 cm-1) pumped bythe second harmonic of a Nd: YAGlaser as light sources and using amonochromator, a phase-lockingamplifier and a computer as the data detecting system, the transmission spectrum, fluorescence spectra, excitation spectrum and siteselective fluorescence spectra ofthe Eu3+: Y2SiO5 crystal were observed. More than thirty out of thetotal fifty spectral lines were observed for 5D0→7F0,1,2,3,4 transitions. The Eu3+ ions occupy twokinds of the Y3+ sites with the lowsymmetry in this crystal. The difference of the wavelengths of thetwo Eu3+ sites for 7F0→5D0 transition is about 0. 2 nm. It was foundthat the two sites were nonequivalent optical ones at room temperature. Crystal lattice constants a,b, c, and β of Eu3+: Y2SiO5 werealso measured by the X-ray diffraction method. The results show thatthe lattice constants a, b, and cof the crystal doped Eu3+ ions isvery close to those of the Y2SiO5crystal undoped Eu3+ ions.
文摘文章主要研究了Y_(2)SiO_(5):Pr^(3+)上转换纳米荧光粉对ZnO:Pr^(3+)的光催化性能的影响,通过XRD、FE-SEM、FL和UV-Vis对样品的物相、形貌、发光性能和光催化行性能进行了分析表征,实验结果表明:随着Y_(2)SiO_(5):Pr^(3+)上转换纳米荧光粉的加入量增加,ZnO:Pr^(3+)光催化效率逐渐提高,当加入0.2 g Y_(2)SiO_(5):Pr^(3+)时,光催化效率最高,在光照60 min后对亚甲基蓝的降解率达到了98.11%,相比未加入Y_(2)SiO_(5):Pr^(3+)时的光催化效率有显著提升。