A kind of novel experiment was disclosed as it possessed two bands of fluorescence emission at 1.4 and 1.6 μm, which were perfectly complimentary to the current C band of optic communication. The fluorescence was bas...A kind of novel experiment was disclosed as it possessed two bands of fluorescence emission at 1.4 and 1.6 μm, which were perfectly complimentary to the current C band of optic communication. The fluorescence was based on energy transfer and up-conversion processes between Tm^3+ and Yb^3+ under direct pumping of 975 nm LD. The spectra and lifetimes of Tm^3+ fluorescence in the tellurite glass were described. The corresponding fluorescence characteristics and energy migration process were analyzed by the method of lifetime and intensity comparison. The mechanism of the up-conversion based IR fluorescence was presented upon analyzing the multi-photon pumping process. The potential advantages of Tm^3+/Yb^3+ co-doped tellurite glass as amplifier material were concluded.展开更多
yb^3+:Er^3+ co-doped oxy-fluoride ceramics glass has been prepared. The mechanism of up-conversion emissions about Er^3+ was discussed, and the temperature properties of green up-conversion fluorescence between 30...yb^3+:Er^3+ co-doped oxy-fluoride ceramics glass has been prepared. The mechanism of up-conversion emissions about Er^3+ was discussed, and the temperature properties of green up-conversion fluorescence between 303 and 823 K were investigated. The results show that the sensitivity of this sample reaches its maximum value, about 0.0047 K^-1, when the temperature is 383 K, indicating that this kind of sample can be used as high temperature and high sensitivity optical temperature sensor.展开更多
Er^3 +/Yb^3 + phosphate glasses were fabricated. According to McCumber theory, the stimulated emission cross-section of Er^3+ ions at 1533 nm was calculated on the basis of absorption spectrum, and 0.84 × 10^-...Er^3 +/Yb^3 + phosphate glasses were fabricated. According to McCumber theory, the stimulated emission cross-section of Er^3+ ions at 1533 nm was calculated on the basis of absorption spectrum, and 0.84 × 10^-20 cm^2 is derived, the fluorescence lifetime of ^4I13/2 level is 8.5 ms. An Er^3+/Yb^3+ co-doped phosphate glass CW laser pumped by LD was demonstrated at room temperature. The maximum output power is 80 mW and slope efficiency is 16.5%.展开更多
The Er^3+/Yb^3+ co-doped TeO2-Nb2O5-Li2O glass is prepared by conventional melting method, and its upconversion spectra are measured. The intense green upconversion luminescence upon excitation with a 976 nm laser d...The Er^3+/Yb^3+ co-doped TeO2-Nb2O5-Li2O glass is prepared by conventional melting method, and its upconversion spectra are measured. The intense green upconversion luminescence upon excitation with a 976 nm laser diode is observed with the naked eyes. The dependence of luminescence intensity on the ratio of Yb^3+/Er^3+ is discussed in detail, and the relationship between the ratio of green luminescence intensity to red luminescence intensity and the ratio of Yb^3+/Er^3+ is also studied, The luminescence intensity increases with the ratio of Yb^3+/Er^3+ increasing. The ratio of Yb^3+/Er^3+ plays a more important role than the concentration of Er^3+ in determining the upconversion luminescence intensity. The ratio of green luminescence intensity to red luminescence intensity reaches a maximum when ratio of Yb^3+/Er^3+ is 3. Thus the glass could be one of the potential candidates for LD pumping solid-state lasers.展开更多
The Er^3+/yb^3+ co-doped transparent oxyfluoride glass-ceramics containing CaF2 nano-crystals were successfully prepared. After heat treatments, transmission electron microscopy (TEM) images showed that CaF2 nano-...The Er^3+/yb^3+ co-doped transparent oxyfluoride glass-ceramics containing CaF2 nano-crystals were successfully prepared. After heat treatments, transmission electron microscopy (TEM) images showed that CaF2 nano-crystals of 20-30 nm in diameter precipitated uniformly in the glass matrix. luminescence of Er^3+ at 540 nm and 658 nm was observed in Comparing with the host glass, high efficiency upconversion the glass ceramics under the excitation of 980 nm. Moreover, the size of the precipitated nano-crystals can be controlled by heat-treatment temperature and time. With the increase of the nano-crystal size, the intensity of the red emission increased more rapidly than that of the green emission. The energy transfer process of Er^3+ and Yb^3+ was convinced and the possible mechanism of Er^3+ up-conversion was discussed.展开更多
The fluorozirconate glasses ZBLANP( ZrF\-4-BaF\-2-LaF\-3-AlF\-3-NaF-PbF\-2) doped with different Yb\+ 3+ concentration were prepared. The Raman spectra and absorption spectra are measured to substantiate the existenc...The fluorozirconate glasses ZBLANP( ZrF\-4-BaF\-2-LaF\-3-AlF\-3-NaF-PbF\-2) doped with different Yb\+ 3+ concentration were prepared. The Raman spectra and absorption spectra are measured to substantiate the existence of phonon-assisted emission. After analyzing the normalized absorption spectra of samples with different Yb\+ 3+-doped concentration, we calculated the maximum cooling effect in the 3 wt% Yb\+ 3+-doped sample pumped at 1 012.5 nm. The corresponding cooling capability is about -4.09 ℃/W and the cooling efficiency reaches 1.76%.展开更多
Oxyfluoride glasses were developed with composition 60GeO 2 ·10AlF 3 ·25BaF 2 ·(1.95-x)GdF 3 · 3YbF 3 ·0.05TmF 3 ·xErF 3 (x=0.02,0.05,0.08,0.11,0.14,0.17)in mole percent.Intense blue...Oxyfluoride glasses were developed with composition 60GeO 2 ·10AlF 3 ·25BaF 2 ·(1.95-x)GdF 3 · 3YbF 3 ·0.05TmF 3 ·xErF 3 (x=0.02,0.05,0.08,0.11,0.14,0.17)in mole percent.Intense blue(476 nm),green(524 and 546 nm)and red(658 nm)emissions which identified from the 1G 4 →3H 6 transition of Tm3+and the(2H 11/2 ,4S 3/2 )→4I 15/2 ,4F 9/2 →4I 15/2 transitions of Er3+,respectively,were simultaneously observed under 980 nm excitation at room temperature.The results show that multicolor luminescence including white light can be adjustably tuned by changing doping concentrations of Er3+ion or the excitation power.In addition,the energy transfer processes among Tm3+,Er3+and Yb3+ions,and up-conversion mechanisms are discussed.展开更多
The Yb3+/Er3+ doped TeO2-WO3-ZnO glasses were prepared. The absorption spectra, emission spectra and fluorescence lifetime of Er3+ at 1.5 um, excited by 970 nm were measured. The influence of Er2O3, Yb2O3 and OH-conte...The Yb3+/Er3+ doped TeO2-WO3-ZnO glasses were prepared. The absorption spectra, emission spectra and fluorescence lifetime of Er3+ at 1.5 um, excited by 970 nm were measured. The influence of Er2O3, Yb2O3 and OH-contents on emission properties of Er3+ at 1.5μm was investigated. The optimum doping concentrations for Er3+ and Yb3+ is around 3.34×1020 ions/cm3 and 6.63×1020 ions/cm3, respectively. The peak emission cross section is 0.83~0.87 pm2. With the increasing concentration of Yb3+, the FWHM of Er3+ emission at 1.5μm in the glass increases from 77 nm to 83 nm. The results show that Yb3+/Er3+ doped TeO2-WO3-ZnO glasses are promising candidate for Er3+-doped broadband optical amplifier.展开更多
The energy transfer and upconversion of Er 3+ /Yb 3+ co-doped TeO2-TiO2-K2O glasses upon excitation with 976nm lasers diode were studied. The tellurite glasses were prepared by conventional melting methods. Their op...The energy transfer and upconversion of Er 3+ /Yb 3+ co-doped TeO2-TiO2-K2O glasses upon excitation with 976nm lasers diode were studied. The tellurite glasses were prepared by conventional melting methods. Their optical properties and sensitization upconversion spectra were performed. The dependence of green upconversion luminescence intensity on the mole ratio of Yb 3+ to Er 3+ and Er 3+ concentration were discussed in detail. When the mole ratio of Yb 3+ to Er 3+ is 25/1 and Er 3+ concentration is 0.1% (mole fraction), or when the mole ratio of Yb 3+ to Er 3+ is 10/1 and Er 3+ concentration is 0.15%, the optimal upconversion luminescence intensity is obtained. The obtained glasses can be one of the potential candidates for lasers-diode pumping microchip solid-state lasers.展开更多
The Nd^3+-doped pared. The absorption and tellurite glasses were preemission spectra of Nd^3 +- doped tellurite glasses at room temperature were measured. The Judd-Ofelt parameters (Ω2, Ω4, Ω6) of the glasses w...The Nd^3+-doped pared. The absorption and tellurite glasses were preemission spectra of Nd^3 +- doped tellurite glasses at room temperature were measured. The Judd-Ofelt parameters (Ω2, Ω4, Ω6) of the glasses were calculated from measured absorption spectra. The calculation results of luminescence properties (A, β, τrad, σ) of Nd^3+ ions in the tellurite were glasses were given. Spectroscopic properties, concentration quenching in these kinds of the glasses were investigated. The results indicate that the tellurite glasses with composition of 70% TeO2, 20% ZnO, ( 10 - x ) % La2O3, x % Nd2O3 ( mol% ) show high emission cross section and low phonon energy. The fluorescent intensity and the emission cross section have a maxi- mum value at x = 0.5, namely, the optimum Nd^3 + ion concentration in the tellurite glass is 0.5% (1.93 × 10^20 ions·cm^-3). The fluorescence properties of Nd^3+ measured are basically in accord with the calculated results.展开更多
Yb^3+:Er^3+:Tm^3+co-doped borosilicate glasses are prepared. Their strong up-conversion photoluminescence spectra in a range from ultra-violet to near-infrared, which are excited by a 978-nm laser diode, are meas...Yb^3+:Er^3+:Tm^3+co-doped borosilicate glasses are prepared. Their strong up-conversion photoluminescence spectra in a range from ultra-violet to near-infrared, which are excited by a 978-nm laser diode, are measured, and the mechanisms of energy transfer among Yb^3+ Er^3+ and Tm^3+ ions are discussed. The results show that there is an unexpected wavelength at 900-nm emission from Yb^3+ Stark splitting levels to pump Tm^3+ ions and there exists an optimum pump power. The concentration of the Tm^3+ dopant gives rise to a prominent effect on the intensity of visible and near-infrared emissions for the yb^3+:Er^3+:Tm^3+ co-doped borosilicate glasses.展开更多
The Er^(3+)-doped TeO_2-WO_3-ZnO-ZnF_2(TWZOF) glasses were prepared. The absorption spectra, 1.5 μm emission spectra and fluorescence lifetimes of Er^(3+), excited at 970 nm, were measured. The J-O parameters Ω_ t (...The Er^(3+)-doped TeO_2-WO_3-ZnO-ZnF_2(TWZOF) glasses were prepared. The absorption spectra, 1.5 μm emission spectra and fluorescence lifetimes of Er^(3+), excited at 970 nm, were measured. The J-O parameters Ω_ t (t =2, 4, 6), absorption and emission cross-sections were calculated. The dependence of the 1.5 μm emission intensity, fluorescence lifetime and bandwidth of the Er^(3+) emission upon the contents of ZnF_2 in glass were investigated. In TWZOF glass, Er^(3+) ions had a broad emission profile around 1.5 μm with the maximum FWHM of 83 nm. With the increasing of the content of ZnF_2, the emission intensity at peak wavelength and the fluorescence lifetime of Er^(3+) at 1.5 μm increase.展开更多
yb^3+-Er^3+ co-doped Na20-Al2O3-SiO2-P2O5 glasses with different SiO2 content have been fabricated and characterized. Absorption and emission spectra were measured. Judd-Ofelt theory and McCumber theory are performe...yb^3+-Er^3+ co-doped Na20-Al2O3-SiO2-P2O5 glasses with different SiO2 content have been fabricated and characterized. Absorption and emission spectra were measured. Judd-Ofelt theory and McCumber theory are performed to analyze the measured absorption spectra. The Judd-Ofelt intensity parameters Ω4 and Ω6 decrease with increasing SiO2 content. The emission cross-section of Er^3+ decreases from 0.82×10^-20cm^2 to 0.76 × 10^-20cm^2 as the SiO2 content varies from 0 to 20 mol%.展开更多
基金supported by the Natural Science Foundation of Zhejiang Provience, China (2006C21082)National Natural Science Foundation of China (60677015)+1 种基金Foundation of Ningbo University (XR0710018)sponsored by KC Wong Magna Fund in NingBo University
文摘A kind of novel experiment was disclosed as it possessed two bands of fluorescence emission at 1.4 and 1.6 μm, which were perfectly complimentary to the current C band of optic communication. The fluorescence was based on energy transfer and up-conversion processes between Tm^3+ and Yb^3+ under direct pumping of 975 nm LD. The spectra and lifetimes of Tm^3+ fluorescence in the tellurite glass were described. The corresponding fluorescence characteristics and energy migration process were analyzed by the method of lifetime and intensity comparison. The mechanism of the up-conversion based IR fluorescence was presented upon analyzing the multi-photon pumping process. The potential advantages of Tm^3+/Yb^3+ co-doped tellurite glass as amplifier material were concluded.
基金Project supported by the National Natural Science Foundation of China (Grant No. 10804015 )the Science Foundation of the Education Department of Liaoning Province of China (Grant No. 2009A417)
文摘yb^3+:Er^3+ co-doped oxy-fluoride ceramics glass has been prepared. The mechanism of up-conversion emissions about Er^3+ was discussed, and the temperature properties of green up-conversion fluorescence between 303 and 823 K were investigated. The results show that the sensitivity of this sample reaches its maximum value, about 0.0047 K^-1, when the temperature is 383 K, indicating that this kind of sample can be used as high temperature and high sensitivity optical temperature sensor.
文摘Er^3 +/Yb^3 + phosphate glasses were fabricated. According to McCumber theory, the stimulated emission cross-section of Er^3+ ions at 1533 nm was calculated on the basis of absorption spectrum, and 0.84 × 10^-20 cm^2 is derived, the fluorescence lifetime of ^4I13/2 level is 8.5 ms. An Er^3+/Yb^3+ co-doped phosphate glass CW laser pumped by LD was demonstrated at room temperature. The maximum output power is 80 mW and slope efficiency is 16.5%.
基金Project supported by the National Natural Science Foundation of China (Grant No 60307004) and the Science and Technology Program of Guangzhou, Guangdong province, China (Grant No 2004Z2-D0131).
文摘The Er^3+/Yb^3+ co-doped TeO2-Nb2O5-Li2O glass is prepared by conventional melting method, and its upconversion spectra are measured. The intense green upconversion luminescence upon excitation with a 976 nm laser diode is observed with the naked eyes. The dependence of luminescence intensity on the ratio of Yb^3+/Er^3+ is discussed in detail, and the relationship between the ratio of green luminescence intensity to red luminescence intensity and the ratio of Yb^3+/Er^3+ is also studied, The luminescence intensity increases with the ratio of Yb^3+/Er^3+ increasing. The ratio of Yb^3+/Er^3+ plays a more important role than the concentration of Er^3+ in determining the upconversion luminescence intensity. The ratio of green luminescence intensity to red luminescence intensity reaches a maximum when ratio of Yb^3+/Er^3+ is 3. Thus the glass could be one of the potential candidates for LD pumping solid-state lasers.
基金Project supported by the National Natural Science Foundation of China(Grant Nos.61265004,51272097,and 11204113)the Nature and Science Fund from Yunnan Province Ministry of Education,China(Grant No.2011C13211708)
文摘The Er^3+/yb^3+ co-doped transparent oxyfluoride glass-ceramics containing CaF2 nano-crystals were successfully prepared. After heat treatments, transmission electron microscopy (TEM) images showed that CaF2 nano-crystals of 20-30 nm in diameter precipitated uniformly in the glass matrix. luminescence of Er^3+ at 540 nm and 658 nm was observed in Comparing with the host glass, high efficiency upconversion the glass ceramics under the excitation of 980 nm. Moreover, the size of the precipitated nano-crystals can be controlled by heat-treatment temperature and time. With the increase of the nano-crystal size, the intensity of the red emission increased more rapidly than that of the green emission. The energy transfer process of Er^3+ and Yb^3+ was convinced and the possible mechanism of Er^3+ up-conversion was discussed.
文摘The fluorozirconate glasses ZBLANP( ZrF\-4-BaF\-2-LaF\-3-AlF\-3-NaF-PbF\-2) doped with different Yb\+ 3+ concentration were prepared. The Raman spectra and absorption spectra are measured to substantiate the existence of phonon-assisted emission. After analyzing the normalized absorption spectra of samples with different Yb\+ 3+-doped concentration, we calculated the maximum cooling effect in the 3 wt% Yb\+ 3+-doped sample pumped at 1 012.5 nm. The corresponding cooling capability is about -4.09 ℃/W and the cooling efficiency reaches 1.76%.
基金Funded by the National Natural Science Foundation of China (No. 50772045)the Society Development Foundation of Yunnan Province (No. 2007E036M)
文摘Oxyfluoride glasses were developed with composition 60GeO 2 ·10AlF 3 ·25BaF 2 ·(1.95-x)GdF 3 · 3YbF 3 ·0.05TmF 3 ·xErF 3 (x=0.02,0.05,0.08,0.11,0.14,0.17)in mole percent.Intense blue(476 nm),green(524 and 546 nm)and red(658 nm)emissions which identified from the 1G 4 →3H 6 transition of Tm3+and the(2H 11/2 ,4S 3/2 )→4I 15/2 ,4F 9/2 →4I 15/2 transitions of Er3+,respectively,were simultaneously observed under 980 nm excitation at room temperature.The results show that multicolor luminescence including white light can be adjustably tuned by changing doping concentrations of Er3+ion or the excitation power.In addition,the energy transfer processes among Tm3+,Er3+and Yb3+ions,and up-conversion mechanisms are discussed.
文摘The Yb3+/Er3+ doped TeO2-WO3-ZnO glasses were prepared. The absorption spectra, emission spectra and fluorescence lifetime of Er3+ at 1.5 um, excited by 970 nm were measured. The influence of Er2O3, Yb2O3 and OH-contents on emission properties of Er3+ at 1.5μm was investigated. The optimum doping concentrations for Er3+ and Yb3+ is around 3.34×1020 ions/cm3 and 6.63×1020 ions/cm3, respectively. The peak emission cross section is 0.83~0.87 pm2. With the increasing concentration of Yb3+, the FWHM of Er3+ emission at 1.5μm in the glass increases from 77 nm to 83 nm. The results show that Yb3+/Er3+ doped TeO2-WO3-ZnO glasses are promising candidate for Er3+-doped broadband optical amplifier.
基金Projects(2004Z2-D0131 and 2004A10602002) supported by the Science and Technology Programof Guangzhou , Guang-dong Province project(60307004 and 50472053) supported by the National Natural Science Foundation of China project(04200036) sup-ported by the Natural Foundation of Guangdong Province
文摘The energy transfer and upconversion of Er 3+ /Yb 3+ co-doped TeO2-TiO2-K2O glasses upon excitation with 976nm lasers diode were studied. The tellurite glasses were prepared by conventional melting methods. Their optical properties and sensitization upconversion spectra were performed. The dependence of green upconversion luminescence intensity on the mole ratio of Yb 3+ to Er 3+ and Er 3+ concentration were discussed in detail. When the mole ratio of Yb 3+ to Er 3+ is 25/1 and Er 3+ concentration is 0.1% (mole fraction), or when the mole ratio of Yb 3+ to Er 3+ is 10/1 and Er 3+ concentration is 0.15%, the optimal upconversion luminescence intensity is obtained. The obtained glasses can be one of the potential candidates for lasers-diode pumping microchip solid-state lasers.
文摘The Nd^3+-doped pared. The absorption and tellurite glasses were preemission spectra of Nd^3 +- doped tellurite glasses at room temperature were measured. The Judd-Ofelt parameters (Ω2, Ω4, Ω6) of the glasses were calculated from measured absorption spectra. The calculation results of luminescence properties (A, β, τrad, σ) of Nd^3+ ions in the tellurite were glasses were given. Spectroscopic properties, concentration quenching in these kinds of the glasses were investigated. The results indicate that the tellurite glasses with composition of 70% TeO2, 20% ZnO, ( 10 - x ) % La2O3, x % Nd2O3 ( mol% ) show high emission cross section and low phonon energy. The fluorescent intensity and the emission cross section have a maxi- mum value at x = 0.5, namely, the optimum Nd^3 + ion concentration in the tellurite glass is 0.5% (1.93 × 10^20 ions·cm^-3). The fluorescence properties of Nd^3+ measured are basically in accord with the calculated results.
基金Project supported by the National Natural Science Foundation of China (Grant No. 10804015)the Science Foundation of the Education Department of Liaoning Province of China (Grant No. 2009A417)
文摘Yb^3+:Er^3+:Tm^3+co-doped borosilicate glasses are prepared. Their strong up-conversion photoluminescence spectra in a range from ultra-violet to near-infrared, which are excited by a 978-nm laser diode, are measured, and the mechanisms of energy transfer among Yb^3+ Er^3+ and Tm^3+ ions are discussed. The results show that there is an unexpected wavelength at 900-nm emission from Yb^3+ Stark splitting levels to pump Tm^3+ ions and there exists an optimum pump power. The concentration of the Tm^3+ dopant gives rise to a prominent effect on the intensity of visible and near-infrared emissions for the yb^3+:Er^3+:Tm^3+ co-doped borosilicate glasses.
文摘The Er^(3+)-doped TeO_2-WO_3-ZnO-ZnF_2(TWZOF) glasses were prepared. The absorption spectra, 1.5 μm emission spectra and fluorescence lifetimes of Er^(3+), excited at 970 nm, were measured. The J-O parameters Ω_ t (t =2, 4, 6), absorption and emission cross-sections were calculated. The dependence of the 1.5 μm emission intensity, fluorescence lifetime and bandwidth of the Er^(3+) emission upon the contents of ZnF_2 in glass were investigated. In TWZOF glass, Er^(3+) ions had a broad emission profile around 1.5 μm with the maximum FWHM of 83 nm. With the increasing of the content of ZnF_2, the emission intensity at peak wavelength and the fluorescence lifetime of Er^(3+) at 1.5 μm increase.
基金Funded by the International Cooperation Project of Shanghai Municipal Science and Technology Commission (No.05S207103)
文摘yb^3+-Er^3+ co-doped Na20-Al2O3-SiO2-P2O5 glasses with different SiO2 content have been fabricated and characterized. Absorption and emission spectra were measured. Judd-Ofelt theory and McCumber theory are performed to analyze the measured absorption spectra. The Judd-Ofelt intensity parameters Ω4 and Ω6 decrease with increasing SiO2 content. The emission cross-section of Er^3+ decreases from 0.82×10^-20cm^2 to 0.76 × 10^-20cm^2 as the SiO2 content varies from 0 to 20 mol%.