The development of blue semiconductor light-emitting diodes(LEDs)has produced potential applications for Prdoped materials that can absorb blue light,especially crystals,and we now report structure and optical propert...The development of blue semiconductor light-emitting diodes(LEDs)has produced potential applications for Prdoped materials that can absorb blue light,especially crystals,and we now report structure and optical properties for high-quality Pr-doped single crystals of yttria-stabilized zirconia(YSZ)grown by the optical floating zone(FZ)method.X-ray diffraction(XRD)and Raman spectroscopy showed that all of the single crystal samples were in the cubic phase,whereas the corresponding ceramic samples contained a mixture of monoclinic and cubic phases.X-ray photoelectron spectroscopy(XPS)and electron paramagnetic resonance(EPR)spectroscopy showed that Pr was present as the Pr^(3+)ion in ceramic rods and single crystals after heating to high temperatures.The absorption and photoluminescence excitation(PLE)spectra of the Pr-doped YSZ crystals measured at room temperature showed strong absorption of blue light,while their photoluminescence(PL)spectra showed five emission peaks at 565 nm,588 nm,614 nm,638 nm,and 716 nm under450 nm excitation.The optimum luminescence properties were obtained with the crystal prepared using 0.15 mol%Pr_(6)O_(11),and those with higher concentrations showed evidence of quenching of the luminescence properties.In addition,the color purity of Pr-doped YSZ single crystal reached 98.9%in the orange–red region.展开更多
We reported the development of a Ф100 cm growth apparatus for skull melting growth of yttria-stabilized cubic zirconia(YSZ) crystals and more than 1000 kg crystals have been grown in the furnace each time.The growth ...We reported the development of a Ф100 cm growth apparatus for skull melting growth of yttria-stabilized cubic zirconia(YSZ) crystals and more than 1000 kg crystals have been grown in the furnace each time.The growth conditions were optimized and the structure of the as-grown crystals was characterized by X-ray diffraction.The transmittance of 15 mol.% yttria-stabilized cubic zirconia crystal was nearly 80% in the range of 400–1600 nm.The refractive indices were measured and fitted the Sellmeier equation whi...展开更多
The sintering behavior and mechanical properties of zirconia doped with 2.0mol%-3.0mol%Y_(2)O_(3)were studied by pressure-less sintering.The experimental results show that the densification temperature of zirconia cer...The sintering behavior and mechanical properties of zirconia doped with 2.0mol%-3.0mol%Y_(2)O_(3)were studied by pressure-less sintering.The experimental results show that the densification temperature of zirconia ceramics increases gradually with the decrease of Y_(2)O_(3)doping content by which decreases the sintering driving force due to the lower oxygen vacancy concentration of the systems.Furthermore,the bending strength and fracture toughness of the prepared zirconia ceramics increase with the decrease of Y_(2)O_(3)doping content.It can be attributed to the fact that the phase stability of tetragonal zirconia decreases with the decrease of Y_(2)O_(3)doping content,which is easier to induce"phase transformation toughening"and dissipate impact energy.The relative density,bending strength and fracture toughness of 2.0 mol%Y_(2)O_(3)doped zirconia ceramics(2.0Y-ZrO_(2))sintered at 1525℃are 99.00%,1256.65±20.82 MPa and 9.85±0.13 MPa·m^(1/2),respectively.展开更多
The yttria-stabilized zirconia(YSZ)film was fabricated on the La 0.8 Sr 0.2 MnO 3(LSM)substrate by electrochemical deposition.The effects of electrochemical deposition conditions on morphological structure of Y(OH) 3 ...The yttria-stabilized zirconia(YSZ)film was fabricated on the La 0.8 Sr 0.2 MnO 3(LSM)substrate by electrochemical deposition.The effects of electrochemical deposition conditions on morphological structure of Y(OH) 3 -Zr(OH) 4 film were studied.The optimal conditions for depositing homogeneous and compact hydroxide film were obtained.The experimental results show that the density of the electrophoretic deposition film is increased remarkably if electrochemical deposition is applied to fill in the pores.展开更多
基金the National Natural Science Foundation of China(Grant No.11975004)the Key Research and Development Plan Project of Guangxi,China(Grant No.Guike AB18281007)。
文摘The development of blue semiconductor light-emitting diodes(LEDs)has produced potential applications for Prdoped materials that can absorb blue light,especially crystals,and we now report structure and optical properties for high-quality Pr-doped single crystals of yttria-stabilized zirconia(YSZ)grown by the optical floating zone(FZ)method.X-ray diffraction(XRD)and Raman spectroscopy showed that all of the single crystal samples were in the cubic phase,whereas the corresponding ceramic samples contained a mixture of monoclinic and cubic phases.X-ray photoelectron spectroscopy(XPS)and electron paramagnetic resonance(EPR)spectroscopy showed that Pr was present as the Pr^(3+)ion in ceramic rods and single crystals after heating to high temperatures.The absorption and photoluminescence excitation(PLE)spectra of the Pr-doped YSZ crystals measured at room temperature showed strong absorption of blue light,while their photoluminescence(PL)spectra showed five emission peaks at 565 nm,588 nm,614 nm,638 nm,and 716 nm under450 nm excitation.The optimum luminescence properties were obtained with the crystal prepared using 0.15 mol%Pr_(6)O_(11),and those with higher concentrations showed evidence of quenching of the luminescence properties.In addition,the color purity of Pr-doped YSZ single crystal reached 98.9%in the orange–red region.
基金supported by the National Natural Science Foundation of China (50672111)Shanghai Science and Technology Committee (08520513100)
文摘We reported the development of a Ф100 cm growth apparatus for skull melting growth of yttria-stabilized cubic zirconia(YSZ) crystals and more than 1000 kg crystals have been grown in the furnace each time.The growth conditions were optimized and the structure of the as-grown crystals was characterized by X-ray diffraction.The transmittance of 15 mol.% yttria-stabilized cubic zirconia crystal was nearly 80% in the range of 400–1600 nm.The refractive indices were measured and fitted the Sellmeier equation whi...
基金Funded by the National Key Research and Development Plan of China(No.2021YFB3701401)the National Natural Science Foundation of China(Nos.92163208,51902233,51972243,51521001,and 51832003)。
文摘The sintering behavior and mechanical properties of zirconia doped with 2.0mol%-3.0mol%Y_(2)O_(3)were studied by pressure-less sintering.The experimental results show that the densification temperature of zirconia ceramics increases gradually with the decrease of Y_(2)O_(3)doping content by which decreases the sintering driving force due to the lower oxygen vacancy concentration of the systems.Furthermore,the bending strength and fracture toughness of the prepared zirconia ceramics increase with the decrease of Y_(2)O_(3)doping content.It can be attributed to the fact that the phase stability of tetragonal zirconia decreases with the decrease of Y_(2)O_(3)doping content,which is easier to induce"phase transformation toughening"and dissipate impact energy.The relative density,bending strength and fracture toughness of 2.0 mol%Y_(2)O_(3)doped zirconia ceramics(2.0Y-ZrO_(2))sintered at 1525℃are 99.00%,1256.65±20.82 MPa and 9.85±0.13 MPa·m^(1/2),respectively.
文摘The yttria-stabilized zirconia(YSZ)film was fabricated on the La 0.8 Sr 0.2 MnO 3(LSM)substrate by electrochemical deposition.The effects of electrochemical deposition conditions on morphological structure of Y(OH) 3 -Zr(OH) 4 film were studied.The optimal conditions for depositing homogeneous and compact hydroxide film were obtained.The experimental results show that the density of the electrophoretic deposition film is increased remarkably if electrochemical deposition is applied to fill in the pores.