The effect of through-thickness reinforcement by composite pins （Z-pins） on the static tensile strength and failure mechanisms of the joints made from ceramic matrix composite （CMC） is investigated. Overlap length...The effect of through-thickness reinforcement by composite pins （Z-pins） on the static tensile strength and failure mechanisms of the joints made from ceramic matrix composite （CMC） is investigated. Overlap length of the single lap joint is 15 mm, 20 mm, 23 mm, 37 mm, and 60 mm, respectively. The experimental results indicate that the final failure modes of the joints can be divided into two groups, （a） the bond-line stops debonding until crack encounters Z-pins; and then the adherends break at the location of Z-pins, when overlap length is more than 20 mm; （b） the bond-line detaches entirely and Z-pins are drawn from adherends, when overlap length is equal to 15 mm. A simple efficient computational approach is presented for analyzing the benefit of through-thickness pins for restricting failure in the single lap joints. Here, the mechanics problem is simplified by representing the effect of the pins by tractions acting on the fracture surfaces of the cracked bond-line. The tractions are prescribed as functions of the crack displacement, which are available in simple forms that summarize the complex deformations to a reasonable accuracy. The resulting model can be used to track the evolution of complete failure mechanisms, for example, bond-line initial delamination and ultimate failure associated with Z-pin pullout, ultimate failure of the adherends. The paper simulates connecting performance of the single lap joints with different Z-pins＇ diameter, spacing and overlap length; the numerical results agree with the experimental results; the numerical results indicate enlarging diameter and decreasing spacing of Z-pins are in favor of improving the connecting performance of the joints. By numerical analysis method, the critical overlap length that lies between two final failure modes is between 18 mm and 19 mm, when Z-pins＇ diameter and spacing are 0.4 mm, 5 mm, respectively.展开更多
In order to study themechanical properties of Z-pins reinforced laminated composite single-lap adhesively bonded joint under un-directional static tensile load,damage failure analysis of the joint was carried out byme...In order to study themechanical properties of Z-pins reinforced laminated composite single-lap adhesively bonded joint under un-directional static tensile load,damage failure analysis of the joint was carried out bymeans of test and numerical simulation.The failure mode and mechanism of the joint were analyzed by tensile failure experiments.According to the experimental results,the joint exhibits mixed failure,and the ultimate failure is Z-pins pulling out of the adherend.In order to study the failure mechanism of the joint,the finite element method is used to predict the failure strength.The numerical results are in good agreement with the experimental results,and the error is 6.0%,which proves the validity of the numerical model.Through progressive damage failure analysis,it is found that matrix tensile failure of laminate at the edge of Z-pins occurs first,then adhesive layer failure-proceeds at the edge of Z-pins,and finally matrix-fiber shear failure of the laminate takes place.With the increase of load,the matrix-fiber shear failure expands gradually in the X direction,and at the same time,the matrix tensile failure at the hole edge gradually extends in different directions,which is consistent with the experimental results.展开更多
The mechanical properties of Z-pins reinforced composites adhesively bonded single-lap joints(SLJs)under un-directional tension loading are investigated by experimental and numerical methods.Three kinds of joint confi...The mechanical properties of Z-pins reinforced composites adhesively bonded single-lap joints(SLJs)under un-directional tension loading are investigated by experimental and numerical methods.Three kinds of joint configurations,including SLJs with three/two rows of Z-pins and“I”array of Z-pins,are investigated by tension test.The failure modes and mechanism of reinforced joints with different Z-pins numbers and alignment are analyzed,and the comparison is performed for the failure strengths of no Z-pins and Z-pins reinforced joints.According to experimental results,failure modes of three kinds of joints are all mixed failure.It turns out that the Z-pins are pulled out ultimately.The strength of joints of more Z-pins at the end of the overlap area is relatively bigger for the joint of the same Z-pins numbers.The strength of joints with Z-pins compared with non Z-pins joints is growing at 16%.Finally,the three-dimensional distribution of interfacial stress in the lap zone of three kinds of Z-pins reinforced joints is simulated,and the numerical results are in good agreement with the experimental results.It is effective that the numerical calculation of stress analysis is verified.展开更多
This paper presents an experimental study of a novel K-Cor sandwich structure rein- forced with partially-cured Z-pins. The influence of pultrusion processing parameters on Z-pins characteristics was studied and the e...This paper presents an experimental study of a novel K-Cor sandwich structure rein- forced with partially-cured Z-pins. The influence of pultrusion processing parameters on Z-pins characteristics was studied and the effect of Z-pins on mechanical properties was disclosed. Differential scanning calorimetry （DSC） and optical microscopy （OM） methods were employed to determine the curing degree of as-prepared Z-pins and observe the implanted Z-pins in the K-Cor structure. These partially-cured Z-pins were treated with a stronger bonding link between face sheets and the foam core by means of a hot-press process, thereby decreasing burrs and cracking defects when the Z-pins were implanted into the Rohacell foam core. The results of the out-of-plane tensile tests and the climbing drum peel （CDP） tests showed that K-Cor structures exhibited superior mechanical performance as compared to X-Cor and blank foam core. The observed results of failure modes revealed that an effective bonding link between the foam core and face sheets that was provided from partially-cured Z-pins contributed to the enhanced mechan- ical performances of K-Cor sandwich structures.展开更多
基金supported by the National Natural Science Foundation of China (No. 90405015)the Research Fund forthe Doctoral Program of Higher Education (No. 20030699040).
文摘The effect of through-thickness reinforcement by composite pins （Z-pins） on the static tensile strength and failure mechanisms of the joints made from ceramic matrix composite （CMC） is investigated. Overlap length of the single lap joint is 15 mm, 20 mm, 23 mm, 37 mm, and 60 mm, respectively. The experimental results indicate that the final failure modes of the joints can be divided into two groups, （a） the bond-line stops debonding until crack encounters Z-pins; and then the adherends break at the location of Z-pins, when overlap length is more than 20 mm; （b） the bond-line detaches entirely and Z-pins are drawn from adherends, when overlap length is equal to 15 mm. A simple efficient computational approach is presented for analyzing the benefit of through-thickness pins for restricting failure in the single lap joints. Here, the mechanics problem is simplified by representing the effect of the pins by tractions acting on the fracture surfaces of the cracked bond-line. The tractions are prescribed as functions of the crack displacement, which are available in simple forms that summarize the complex deformations to a reasonable accuracy. The resulting model can be used to track the evolution of complete failure mechanisms, for example, bond-line initial delamination and ultimate failure associated with Z-pin pullout, ultimate failure of the adherends. The paper simulates connecting performance of the single lap joints with different Z-pins＇ diameter, spacing and overlap length; the numerical results agree with the experimental results; the numerical results indicate enlarging diameter and decreasing spacing of Z-pins are in favor of improving the connecting performance of the joints. By numerical analysis method, the critical overlap length that lies between two final failure modes is between 18 mm and 19 mm, when Z-pins＇ diameter and spacing are 0.4 mm, 5 mm, respectively.
基金supported by Natural Science Talents Program of Lingnan Normal University(No.ZL2021011).
文摘In order to study themechanical properties of Z-pins reinforced laminated composite single-lap adhesively bonded joint under un-directional static tensile load,damage failure analysis of the joint was carried out bymeans of test and numerical simulation.The failure mode and mechanism of the joint were analyzed by tensile failure experiments.According to the experimental results,the joint exhibits mixed failure,and the ultimate failure is Z-pins pulling out of the adherend.In order to study the failure mechanism of the joint,the finite element method is used to predict the failure strength.The numerical results are in good agreement with the experimental results,and the error is 6.0%,which proves the validity of the numerical model.Through progressive damage failure analysis,it is found that matrix tensile failure of laminate at the edge of Z-pins occurs first,then adhesive layer failure-proceeds at the edge of Z-pins,and finally matrix-fiber shear failure of the laminate takes place.With the increase of load,the matrix-fiber shear failure expands gradually in the X direction,and at the same time,the matrix tensile failure at the hole edge gradually extends in different directions,which is consistent with the experimental results.
基金This work was supported by Natural Science Talents Program of Lingnan Normal University(No.ZL2021011).
文摘The mechanical properties of Z-pins reinforced composites adhesively bonded single-lap joints(SLJs)under un-directional tension loading are investigated by experimental and numerical methods.Three kinds of joint configurations,including SLJs with three/two rows of Z-pins and“I”array of Z-pins,are investigated by tension test.The failure modes and mechanism of reinforced joints with different Z-pins numbers and alignment are analyzed,and the comparison is performed for the failure strengths of no Z-pins and Z-pins reinforced joints.According to experimental results,failure modes of three kinds of joints are all mixed failure.It turns out that the Z-pins are pulled out ultimately.The strength of joints of more Z-pins at the end of the overlap area is relatively bigger for the joint of the same Z-pins numbers.The strength of joints with Z-pins compared with non Z-pins joints is growing at 16%.Finally,the three-dimensional distribution of interfacial stress in the lap zone of three kinds of Z-pins reinforced joints is simulated,and the numerical results are in good agreement with the experimental results.It is effective that the numerical calculation of stress analysis is verified.
基金the financial support from JPTT project (No.JPTT-1146)
文摘This paper presents an experimental study of a novel K-Cor sandwich structure rein- forced with partially-cured Z-pins. The influence of pultrusion processing parameters on Z-pins characteristics was studied and the effect of Z-pins on mechanical properties was disclosed. Differential scanning calorimetry （DSC） and optical microscopy （OM） methods were employed to determine the curing degree of as-prepared Z-pins and observe the implanted Z-pins in the K-Cor structure. These partially-cured Z-pins were treated with a stronger bonding link between face sheets and the foam core by means of a hot-press process, thereby decreasing burrs and cracking defects when the Z-pins were implanted into the Rohacell foam core. The results of the out-of-plane tensile tests and the climbing drum peel （CDP） tests showed that K-Cor structures exhibited superior mechanical performance as compared to X-Cor and blank foam core. The observed results of failure modes revealed that an effective bonding link between the foam core and face sheets that was provided from partially-cured Z-pins contributed to the enhanced mechan- ical performances of K-Cor sandwich structures.