Hot deformation behavior of the annealed ZK61 M magnesium alloy sheet was explored using tensile tests with strain rates varying from 0.001 to 0.030 s^(-1) in temperatures range of 423-513 K.The obtained results indic...Hot deformation behavior of the annealed ZK61 M magnesium alloy sheet was explored using tensile tests with strain rates varying from 0.001 to 0.030 s^(-1) in temperatures range of 423-513 K.The obtained results indicate that the flow stress increased with deformation temperature decreasing and strain rate increasing.Dynamic recrystallization(DRX)occurs when the temperature is higher than 423 K,and the recrystallization volume fraction increases with temperature rising.At a given temperature,the measured DRX volume fraction at a higher strain rate is smaller than that at a lower strain rate.Dimples are observed throughout the tested temperature range.Moreover,they grow larger as temperature increases.An average absolute relative error(AARE)of 2.65%proves that the peak stress predicted by the constitutive model is in good agreement with the experimental results.The correlation coefficient(R’)obtained for the predicted stress and the experimental value considering the strain on the material constant are between 0.9831 and 0.9977.In addition,AARE and root mean square error(RMSE)are less than 6.5%and 8.5 MPa,respectively.This indicates that the deviation of the predicted value from the experimental value is small and the predictions of the proposed model are reliable.展开更多
基金financially supported by the National Natural Science Foundation of China(No.51275444)the Natural Science Foundation of Hebei Province(No.E2018203254)the Innovative Research Assistant Project for Graduate Students of Yanshan University(No.CXZS202001)。
文摘Hot deformation behavior of the annealed ZK61 M magnesium alloy sheet was explored using tensile tests with strain rates varying from 0.001 to 0.030 s^(-1) in temperatures range of 423-513 K.The obtained results indicate that the flow stress increased with deformation temperature decreasing and strain rate increasing.Dynamic recrystallization(DRX)occurs when the temperature is higher than 423 K,and the recrystallization volume fraction increases with temperature rising.At a given temperature,the measured DRX volume fraction at a higher strain rate is smaller than that at a lower strain rate.Dimples are observed throughout the tested temperature range.Moreover,they grow larger as temperature increases.An average absolute relative error(AARE)of 2.65%proves that the peak stress predicted by the constitutive model is in good agreement with the experimental results.The correlation coefficient(R’)obtained for the predicted stress and the experimental value considering the strain on the material constant are between 0.9831 and 0.9977.In addition,AARE and root mean square error(RMSE)are less than 6.5%and 8.5 MPa,respectively.This indicates that the deviation of the predicted value from the experimental value is small and the predictions of the proposed model are reliable.