A chemical composite plating of Ni-B_(4)C was used to prepare the surface-modified zirconia toughened alumina(ZTA)ceramic particles.The ceramic preforms were prepared by the plated ZTA and sodium silicate solution bin...A chemical composite plating of Ni-B_(4)C was used to prepare the surface-modified zirconia toughened alumina(ZTA)ceramic particles.The ceramic preforms were prepared by the plated ZTA and sodium silicate solution binder,followed by casting infiltration to prepare the ZTA particles reinforced high chromium cast iron(HCCI)composites.The result reveals that a distinct interface layer forms at the ZTA/HCCI interface,which consists of phases of ZrB_(2),FeB,Fe_(2)B,and NaSiO_(4).The interfacial wettability between ZTA and HCCI is improved by the diffusion and reaction of Ni and B_(4)C.The wear test reveals that the Ni-B_(4)C plated ZTA particles can effectively improve the wear resistance of the ZTA/HCCI composite,and the wear rate of the composite is decreased to 11.6%of HCCI.展开更多
The impact-abrasive wear behavior of ZTA(zirconia toughened alumina)particle(ZTAp)and NbC particle(NbCp)reinforced Fe60 matrix composites(ZTAp-NbCp/Fe60)were investigated.Specimens of pure Fe60 matrix material,NbCp re...The impact-abrasive wear behavior of ZTA(zirconia toughened alumina)particle(ZTAp)and NbC particle(NbCp)reinforced Fe60 matrix composites(ZTAp-NbCp/Fe60)were investigated.Specimens of pure Fe60 matrix material,NbCp reinforced Fe60 composite(NbCp/Fe60)and ZTAp-NbCp/Fe60 with different contents of ZTAp were prepared through vacuum sintering and tested on an MLD-10B Impact Wear Rig.As revealed by the results,NbCp could strengthen Fe60 matrix,and had fine grain strengthening effect on Fe60matrix.When the mass fraction of ZTAp was 5%-15%,the impact-abrasive wear performance of ZTAp-NbCp/Fe60 composites was better than that of Fe60 and NbCp/Fe60.When the mass fraction was 15%,the ZTApNbCp/Fe60 had the best performance.ZTAp could weaken the impact and wear effect of abrasive particles on the composite and protect the matrix.Cracks occured at the interface and at defects in the ZTAp.The former leaded to ZTAp shedding,while the latter leaded to ZTAp fracturing.In both cases,the performance of the composite material would decrease.展开更多
基金financially supported by the National Natural Science Foundation of China(52005217)the University Research Platform and Research Projects of Guangdong Education Department(2022ZDZX3003)+2 种基金Basic and Applied Basic Research Fund Project of Guangdong Province in China(2022A1515010091,2021A1515010523,and 2020A1515110020)Basic Scientific Research Projects of Central Universities(No.21620344)Jinan University Open Fund for Advanced Materials(JNIWRM2021004)。
文摘A chemical composite plating of Ni-B_(4)C was used to prepare the surface-modified zirconia toughened alumina(ZTA)ceramic particles.The ceramic preforms were prepared by the plated ZTA and sodium silicate solution binder,followed by casting infiltration to prepare the ZTA particles reinforced high chromium cast iron(HCCI)composites.The result reveals that a distinct interface layer forms at the ZTA/HCCI interface,which consists of phases of ZrB_(2),FeB,Fe_(2)B,and NaSiO_(4).The interfacial wettability between ZTA and HCCI is improved by the diffusion and reaction of Ni and B_(4)C.The wear test reveals that the Ni-B_(4)C plated ZTA particles can effectively improve the wear resistance of the ZTA/HCCI composite,and the wear rate of the composite is decreased to 11.6%of HCCI.
基金Funded by the National Key Research and Development Program(No.2017YFB0305105)the National Natural Science Foundation of China(No.51571210)。
文摘The impact-abrasive wear behavior of ZTA(zirconia toughened alumina)particle(ZTAp)and NbC particle(NbCp)reinforced Fe60 matrix composites(ZTAp-NbCp/Fe60)were investigated.Specimens of pure Fe60 matrix material,NbCp reinforced Fe60 composite(NbCp/Fe60)and ZTAp-NbCp/Fe60 with different contents of ZTAp were prepared through vacuum sintering and tested on an MLD-10B Impact Wear Rig.As revealed by the results,NbCp could strengthen Fe60 matrix,and had fine grain strengthening effect on Fe60matrix.When the mass fraction of ZTAp was 5%-15%,the impact-abrasive wear performance of ZTAp-NbCp/Fe60 composites was better than that of Fe60 and NbCp/Fe60.When the mass fraction was 15%,the ZTApNbCp/Fe60 had the best performance.ZTAp could weaken the impact and wear effect of abrasive particles on the composite and protect the matrix.Cracks occured at the interface and at defects in the ZTAp.The former leaded to ZTAp shedding,while the latter leaded to ZTAp fracturing.In both cases,the performance of the composite material would decrease.