Nanocrystalline zinc-nickel alloy coatings were deposited from an alkaline zincate bath contained an organic additive that can reduce polarization and a complexing agent. SEM and TEM observations and XRD analysis were...Nanocrystalline zinc-nickel alloy coatings were deposited from an alkaline zincate bath contained an organic additive that can reduce polarization and a complexing agent. SEM and TEM observations and XRD analysis were performed to examine the microstructure and phase composition of the coatings. The nickel content in deposits is 12.0-14.7% and the coating is consisted of single nanocrystalline y-phase structure (Ni5Zn2i), with grain average grain size about 15nm. The nanocrystalline zinc-nickel alloy coatings have better corrosion resistance, less bnttleness and higher microhardness than the conventional zinc coatings.展开更多
Despite the promising potential of transition metal oxides(TMOs)as capacitive deionization(CDI)electrodes,the actual capacity of TMOs electrodes for sodium storage is significantly lower than the theoretical capacity,...Despite the promising potential of transition metal oxides(TMOs)as capacitive deionization(CDI)electrodes,the actual capacity of TMOs electrodes for sodium storage is significantly lower than the theoretical capacity,posing a major obstacle.Herein,we prepared the kinetically favorable Zn_(x)Ni_(1−x)O electrode in situ growth on carbon felt(Zn_(x)Ni_(1−x)O@CF)through constraining the rate of OH^(−)generation in the hydrothermal method.Zn_(x)Ni_(1−x)O@CF exhibited a high-density hierarchical nanosheet structure with three-dimensional open pores,benefitting the ion transport/electron transfer.And tuning the moderate amount of redox-inert Zn-doping can enhance surface electroactive sites,actual activity of redox-active Ni species,and lower adsorption energy,promoting the adsorption kinetic and thermodynamic of the Zn_(0.2)Ni_(0.8)O@CF.Benefitting from the kinetic-thermodynamic facilitation mechanism,Zn_(0.2)Ni_(0.8)O@CF achieved ultrahigh desalination capacity(128.9 mgNaCl g^(-1)),ultra-low energy consumption(0.164 kW h kgNaCl^(-1)),high salt removal rate(1.21 mgNaCl g^(-1) min^(-1)),and good cyclability.The thermodynamic facilitation and Na^(+)intercalation mechanism of Zn_(0.2)Ni_(0.8)O@CF are identified by the density functional theory calculations and electrochemical quartz crystal microbalance with dissipation monitoring,respectively.This research provides new insights into controlling electrochemically favorable morphology and demonstrates that Zn-doping,which is redox-inert,is essential for enhancing the electrochemical performance of CDI electrodes.展开更多
Novel zinc-nickel-cobalt ternary oxide nanosheets were successfully synthesized via an easy solvothermal method followed by calcination and were tailored to have different numbers of wrinkles by controlling the vohtrn...Novel zinc-nickel-cobalt ternary oxide nanosheets were successfully synthesized via an easy solvothermal method followed by calcination and were tailored to have different numbers of wrinkles by controlling the vohtrne ratio of the components in the mixed solvent. Nanosheets with more wrinkles yielded a large specific surface area（111.61 m2/g）, which improved their electrochemical properties. The resulting products were characterized using a three-electrode system in 6 mol/L KOH electrolyte solution. With unique structures, the nanosheets with more wrinkles displayed a good capacitive behavior and an excellent specific capacitance retention of 97.18% after 2000 continuous charge-discharge cycles. Considering their high electrochemical performance and simple fabrication, we proposed that these unique zinc-nickel-cobalt oxide nanosheets are promising supercapacitor electrodes for energy storage applications.展开更多
文摘Nanocrystalline zinc-nickel alloy coatings were deposited from an alkaline zincate bath contained an organic additive that can reduce polarization and a complexing agent. SEM and TEM observations and XRD analysis were performed to examine the microstructure and phase composition of the coatings. The nickel content in deposits is 12.0-14.7% and the coating is consisted of single nanocrystalline y-phase structure (Ni5Zn2i), with grain average grain size about 15nm. The nanocrystalline zinc-nickel alloy coatings have better corrosion resistance, less bnttleness and higher microhardness than the conventional zinc coatings.
基金supported by The National Natural Science Foundation of China(22276137,52170087)the Fundamental Research Funds for the Central Universities(XJEDU2023Z009).
文摘Despite the promising potential of transition metal oxides(TMOs)as capacitive deionization(CDI)electrodes,the actual capacity of TMOs electrodes for sodium storage is significantly lower than the theoretical capacity,posing a major obstacle.Herein,we prepared the kinetically favorable Zn_(x)Ni_(1−x)O electrode in situ growth on carbon felt(Zn_(x)Ni_(1−x)O@CF)through constraining the rate of OH^(−)generation in the hydrothermal method.Zn_(x)Ni_(1−x)O@CF exhibited a high-density hierarchical nanosheet structure with three-dimensional open pores,benefitting the ion transport/electron transfer.And tuning the moderate amount of redox-inert Zn-doping can enhance surface electroactive sites,actual activity of redox-active Ni species,and lower adsorption energy,promoting the adsorption kinetic and thermodynamic of the Zn_(0.2)Ni_(0.8)O@CF.Benefitting from the kinetic-thermodynamic facilitation mechanism,Zn_(0.2)Ni_(0.8)O@CF achieved ultrahigh desalination capacity(128.9 mgNaCl g^(-1)),ultra-low energy consumption(0.164 kW h kgNaCl^(-1)),high salt removal rate(1.21 mgNaCl g^(-1) min^(-1)),and good cyclability.The thermodynamic facilitation and Na^(+)intercalation mechanism of Zn_(0.2)Ni_(0.8)O@CF are identified by the density functional theory calculations and electrochemical quartz crystal microbalance with dissipation monitoring,respectively.This research provides new insights into controlling electrochemically favorable morphology and demonstrates that Zn-doping,which is redox-inert,is essential for enhancing the electrochemical performance of CDI electrodes.
基金Supported by the National Natural Science Foundation of China（Nos.51372124, 51572134）.
文摘Novel zinc-nickel-cobalt ternary oxide nanosheets were successfully synthesized via an easy solvothermal method followed by calcination and were tailored to have different numbers of wrinkles by controlling the vohtrne ratio of the components in the mixed solvent. Nanosheets with more wrinkles yielded a large specific surface area（111.61 m2/g）, which improved their electrochemical properties. The resulting products were characterized using a three-electrode system in 6 mol/L KOH electrolyte solution. With unique structures, the nanosheets with more wrinkles displayed a good capacitive behavior and an excellent specific capacitance retention of 97.18% after 2000 continuous charge-discharge cycles. Considering their high electrochemical performance and simple fabrication, we proposed that these unique zinc-nickel-cobalt oxide nanosheets are promising supercapacitor electrodes for energy storage applications.