Tungsten coating is considered as a promising alternative material for plasma facing materials(PFC) in future fusion devices.The electro-deposition of tungsten in Na_2WO_4-ZnO-WO_3 melt at 1173 K on low activation ste...Tungsten coating is considered as a promising alternative material for plasma facing materials(PFC) in future fusion devices.The electro-deposition of tungsten in Na_2WO_4-ZnO-WO_3 melt at 1173 K on low activation steel substrates was studied in this work.Adherent and smooth tungsten films were deposited under various pulsed current conditions.The crystal structure and microstructure of tungsten deposits were characterized by XRD,SEM and EDX techniques.The results show that pulsed current density and duty cycle have a significant influence on tungsten nucleation and electro-crystallization phenomena.Uniform and smooth tungsten coating with high purity and high adherence is obtained on low active steel substrates as cathodic current density ranges from 35 to 25 mA·cm_(-2).展开更多
锂硫电池由于其高能量密度、低成本效益被认为是最有前途的下一代电池体系之一.然而多硫化物的穿梭效应大幅降低了锂硫电池的循环稳定性和寿命,严重阻碍其实际应用.无机金属化合物材料改性的隔膜不仅能抑制多硫化锂(LiPS)的穿梭效应,其...锂硫电池由于其高能量密度、低成本效益被认为是最有前途的下一代电池体系之一.然而多硫化物的穿梭效应大幅降低了锂硫电池的循环稳定性和寿命,严重阻碍其实际应用.无机金属化合物材料改性的隔膜不仅能抑制多硫化锂(LiPS)的穿梭效应,其部分特殊的晶面还能加速多硫化物的氧化还原反应动力学.本文在罗盘状ZnS表面原位生长球状的MoO_(2),制备MoO_(2)/ZnS复合材料.MoO_(2)对多硫化物有着较强的吸附作用,ZnS有着良好的电导率,两者的复合可加速电子传导效率和氧化还原速率.以所制备的MoO_(2)/ZnS作为隔膜改性材料,锂硫电池在5 C的大电流密度下,经过1000次循环后仍可以保持690 mAh g^(-1)的放电比容量,平均每圈的容量衰减率仅为0.014%,表现出优异的循环性能和倍率性能.展开更多
In this paper, diamond-like carbon (DLC) films were deposited on Ti alloy by electro-deposition. DLC films were brown andcomposed of the compact grains whose diameter was about 400 nm. Examined by XPS, the main compos...In this paper, diamond-like carbon (DLC) films were deposited on Ti alloy by electro-deposition. DLC films were brown andcomposed of the compact grains whose diameter was about 400 nm. Examined by XPS, the main composition of the filmswas carbon. In the Raman spectrum, there were a broad peak at 1350 cm^(-1) and a broad peak at 1600 cm^(-1), which indicatedthat the films were DLC films.展开更多
基金supported by the International Thermonuclear Experimental Reactor (ITER) Project of China (No. 2010GB109000)the National Natural Science Foundation of China (No. 50972008)
文摘Tungsten coating is considered as a promising alternative material for plasma facing materials(PFC) in future fusion devices.The electro-deposition of tungsten in Na_2WO_4-ZnO-WO_3 melt at 1173 K on low activation steel substrates was studied in this work.Adherent and smooth tungsten films were deposited under various pulsed current conditions.The crystal structure and microstructure of tungsten deposits were characterized by XRD,SEM and EDX techniques.The results show that pulsed current density and duty cycle have a significant influence on tungsten nucleation and electro-crystallization phenomena.Uniform and smooth tungsten coating with high purity and high adherence is obtained on low active steel substrates as cathodic current density ranges from 35 to 25 mA·cm_(-2).
文摘锂硫电池由于其高能量密度、低成本效益被认为是最有前途的下一代电池体系之一.然而多硫化物的穿梭效应大幅降低了锂硫电池的循环稳定性和寿命,严重阻碍其实际应用.无机金属化合物材料改性的隔膜不仅能抑制多硫化锂(LiPS)的穿梭效应,其部分特殊的晶面还能加速多硫化物的氧化还原反应动力学.本文在罗盘状ZnS表面原位生长球状的MoO_(2),制备MoO_(2)/ZnS复合材料.MoO_(2)对多硫化物有着较强的吸附作用,ZnS有着良好的电导率,两者的复合可加速电子传导效率和氧化还原速率.以所制备的MoO_(2)/ZnS作为隔膜改性材料,锂硫电池在5 C的大电流密度下,经过1000次循环后仍可以保持690 mAh g^(-1)的放电比容量,平均每圈的容量衰减率仅为0.014%,表现出优异的循环性能和倍率性能.
基金supported by the Jiangsu Province Industry–University–Research Project,China(No.BY20221160)the Postgraduate Research and Practice Innovation Program of Jiangsu Province,China(No.KYCX22_3798)+2 种基金the National Natural Science Foundation of China(No.52275339)the Key Research and Development Plan of the Ministry of Science and Technology,China(No.2023YFE0200400)the Science and Technology Project of Jiangsu Province,China(No.BZ2021053)。
基金Our work is supported by the Natural Science Fund of Jiangsu Province(BK20001414).
文摘In this paper, diamond-like carbon (DLC) films were deposited on Ti alloy by electro-deposition. DLC films were brown andcomposed of the compact grains whose diameter was about 400 nm. Examined by XPS, the main composition of the filmswas carbon. In the Raman spectrum, there were a broad peak at 1350 cm^(-1) and a broad peak at 1600 cm^(-1), which indicatedthat the films were DLC films.