Al2O3 ceramic powder was applied to modify the large pores defects on the surface of the porous metal Ti support,in situ oxidation method was a convenient method to prepare defect free ceramic/Ti composite membranes o...Al2O3 ceramic powder was applied to modify the large pores defects on the surface of the porous metal Ti support,in situ oxidation method was a convenient method to prepare defect free ceramic/Ti composite membranes on this basis.In situ oxidation conditions experimental results show that the best condition for preparing the TiO2-Al2O3/Ti composite membrane is under 800°C for 2 h,and the microstructure and pore sizes of the TiO2-Al2O3/Ti composite membranes are affected obviously.The thickness and composition of the TiO2/Ti composite membranes are determined by SEM and XRD completely.The pore size distribution of the composite membrane is measured by bubble pressure method,the most probable aperture is about 3.12μm,while the average pore size of defect free TiO2-Al2O3/Ti is about 3.23μm.After ultrasonic treatment,the slight weight change of membranes reveals no observable change,which indicates that TiO2-Al2O3/Ti composite membranes maintain a good stability.展开更多
By means of atomic force microscope, the surface pattern, particle size distribution, and specific surface area of La Ti composite oxide were studied. The compound particle surface appears as a smooth sheet, the even ...By means of atomic force microscope, the surface pattern, particle size distribution, and specific surface area of La Ti composite oxide were studied. The compound particle surface appears as a smooth sheet, the even size of the compound ranges from 19.85 nm to 25.38 nm. The particle seems smooth, which erects at a height from 4.69 nm to 5.88 nm.The surface area ranges from 58.90 nm 2 to 1 238.04 nm 2. The La Ti composite oxide nanocrystallines enjoy a narrow and even particle size distribution and accumulate closely.展开更多
One-dimensional and quasi-one-dimensional nanostructure materials are promising building blocks for electromagnetic devices and nanosystems.In this work,the composite Ni0.5Zn0.5Fe2O4（NZFO）/ Pb（Zr0.52Ti0.48）O3（PZT...One-dimensional and quasi-one-dimensional nanostructure materials are promising building blocks for electromagnetic devices and nanosystems.In this work,the composite Ni0.5Zn0.5Fe2O4（NZFO）/ Pb（Zr0.52Ti0.48）O3（PZT） nanofibers with average diameters about 65 nm are prepared by electrospinning from poly（vinyl pyrrolidone） （PVP） and metal salts.The precursor composite NZFO/PZT/PVP nanofibers and the subsequent calcined NZFO/PZT nanofibers are investigated by Fourier transform infrared spectroscopy （FT- IR） ,X-ray diffraction （XRD）,scanning electron microscopy （SEM）.The magnetic properties for nanofibers are measured by vibrating sample magnetometer（VSM）.The NZFO/PZT nanofibers obtained at calcination temperature of 900 °C for 2 h consist of the ferromagnetic spinel NZFO and ferroelectric perovskite PZT phases,which are constructed from about 37 nm NZFO and 17 nm PZT grains.The saturation magnetization of these NZFO/PZT nanofibers increases with increasing calcination temperature and contents of NZFO in the composite.展开更多
With sol-gel method, nanometer La-Ti composite oxide was successfully prepared at a low temperature (750～800C) using polyethylene glycol as dispersant. By means of atomic force microscope, the surface pattern, partic...With sol-gel method, nanometer La-Ti composite oxide was successfully prepared at a low temperature (750～800C) using polyethylene glycol as dispersant. By means of atomic force microscope, the surface pattern, particle size distribution, and specific surface area were studied. The compound particle surface appears as a smooth sheet, the mean size of the compound is 25.38 nm. On the specific surface, the particle erects at a height of 4.69 nm. The surface area is 58.90 nm2. The La-Ti composite oxide nanocrystal prefers to narrow and even particle size distribution and the homogeneity of surface topography.展开更多
Although there have been many reports of metal doping to ameliorate the drawbacks of hematite as the photoanode for water oxidation, most of them focused on monometallic doping, and only a few of them payed attention ...Although there have been many reports of metal doping to ameliorate the drawbacks of hematite as the photoanode for water oxidation, most of them focused on monometallic doping, and only a few of them payed attention to bimetallic doping. What is worse, the synergetic mechanism between two metal dopants was not sufficiently studied, especially the density functional theory(DFT) calculation. In this work, the n-type hematite was synthesized by introducing Ti dopant into hematite through the hydrothermal method, and dipping-sintering treatment was employed to further introduce homogeneously dispersed Zn dopant into that, forming the Ti, Zn co-doped hematite. Under the optimal condition, Tidoped hematite photoanode reached approximately 2-times enhancement of the photocurrent density compared with the pristine one at 1.23 V vs. RHE, while Ti, Zn co-doped hematite anode obtained another25% elevation. UV–Vis spectroscopy, Mott–Schottky plots, EIS analysis, photo-oxidation of hole scavenger(H2O2), and DFT calculation were employed to understand the role of Ti, Zn dopant. Based on the obtained results, the synergetic mechanism of two dopants was discussed, i.e., the improvement of PEC performance of Ti, Zn co-doped hematite photoanode was possibly attributed to greater carrier density and improved charge separation efficiency at the surface of hematite. This work provides new strategy and understanding of the improvement of PEC performance of hematite by doping engineering.展开更多
Anodized composite films containing Si C nanoparticles were synthesized on Ti6Al4 V alloy by anodic oxidation procedure in C4O6H4Na2 electrolyte. Scanning electron microscopy(SEM), energy dispersive spectroscopy(EDS) ...Anodized composite films containing Si C nanoparticles were synthesized on Ti6Al4 V alloy by anodic oxidation procedure in C4O6H4Na2 electrolyte. Scanning electron microscopy(SEM), energy dispersive spectroscopy(EDS) and X-ray photoelectron spectroscopy(XPS) were employed to characterize the morphology and composition of the films fabricated in the electrolytes with and without addition of Si C nanoparticles. Results show that Si C particles can be successfully incorporated into the oxide film during the anodizing process and preferentially concentrate within internal cavities and micro-cracks. The ball-on-disk sliding tests indicate that Si C-containing oxide films register much lower wear rate than the oxide films without Si C under dry sliding condition. Si C particles are likely to melt and then are oxidized by frictional heat during sliding tests. Potentiodynamic polarization behavior reveals that the anodized alloy with Si C nanoparticles results in a reduction in passive current density to about 1.54×10-8 A/cm2, which is more than two times lower than that of the Ti O2 film(3.73×10-8 A/cm2). The synthesized composite film has good anti-wear and anti-corrosion properties and the growth mechanism of nanocomposite film is also discussed.展开更多
The Xinjie layered intrusion in the Panxi region,SW China,hosts both Fe-Ti oxide and platinum-group element（PGE） sulfide mineralization.The intrusion can be divided,from the base upward,into UnitsⅠ,ⅡandⅢ,in terms...The Xinjie layered intrusion in the Panxi region,SW China,hosts both Fe-Ti oxide and platinum-group element（PGE） sulfide mineralization.The intrusion can be divided,from the base upward,into UnitsⅠ,ⅡandⅢ,in terms of mineral assemblages.UnitsⅠandⅡare mainly composed of wehrlite and clino-pyroxenite, whereas UnitⅢis mainly composed of gabbro.PGE sulfide-rich layers mainly occur in Unit I, whereas thick Fe-Ti oxide-rich layers mainly occur in UnitⅢ.An ilmenite-rich layer occurs at the top of UnitⅠ.Fe-Ti oxides include magnetite and ilmenite.Small amounts of cumulus and intercumulus magnetite occur in UnitsⅠandⅡ.Cumulus magnetite grains are commonly euhedral and enclosed within olivine and clinopyroxene.They have high Cr2O3 contents ranging from 6.02 to 22.5 wt.%,indicating that they are likely an early crystallized phase from magmas.Intercumulus magnetite that usually displays ilmenite exsolution occupies the interstices between cumulus olivine crystals and coexists with interstitial clinopyroxene and plagioclase.Intercumulus magnetite has Cr2O3 ranging from 1.65 to 6.18 wt.%, lower than cumulus magnetite.The intercumulus magnetite may have crystallized from the trapped liquid.Large amounts of magnetite in UnitⅢcontains Cr2O3（＆lt;0.28 wt.%） much lower than magnetite in UnitsⅠandⅡ.The magnetite in UnitⅢis proposed to be accumulated from a Fe-Ti-rich melt.The Fe-Ti-rich melt is estimated to contain 35.9 wt.%of SiO2,26.9 wt.%of FeOt,8.2 wt.%of TiO2,13.2 wt.%of CaO, 8.3 wt.%of MgO,5.5 wt.%of Al2O3 and 1.0 wt.%of P2O5.The composition is comparable with the Fe-rich melts in the Skaergaard and Sept Iles intrusions.Paired non-reactive microstructures,granophyre pockets and ilmenite-rich intergrowths,are representative of Si-rich melt and Fe-Ti-rich melt,and are the direct evidence for the existence of an immiscible Fe-Ti-rich melt that formed from an evolved ferro-basaltic magma.展开更多
基金Projects(212006065,21666018)supported by the National Natural Science Foundation of China
文摘Al2O3 ceramic powder was applied to modify the large pores defects on the surface of the porous metal Ti support,in situ oxidation method was a convenient method to prepare defect free ceramic/Ti composite membranes on this basis.In situ oxidation conditions experimental results show that the best condition for preparing the TiO2-Al2O3/Ti composite membrane is under 800°C for 2 h,and the microstructure and pore sizes of the TiO2-Al2O3/Ti composite membranes are affected obviously.The thickness and composition of the TiO2/Ti composite membranes are determined by SEM and XRD completely.The pore size distribution of the composite membrane is measured by bubble pressure method,the most probable aperture is about 3.12μm,while the average pore size of defect free TiO2-Al2O3/Ti is about 3.23μm.After ultrasonic treatment,the slight weight change of membranes reveals no observable change,which indicates that TiO2-Al2O3/Ti composite membranes maintain a good stability.
文摘By means of atomic force microscope, the surface pattern, particle size distribution, and specific surface area of La Ti composite oxide were studied. The compound particle surface appears as a smooth sheet, the even size of the compound ranges from 19.85 nm to 25.38 nm. The particle seems smooth, which erects at a height from 4.69 nm to 5.88 nm.The surface area ranges from 58.90 nm 2 to 1 238.04 nm 2. The La Ti composite oxide nanocrystallines enjoy a narrow and even particle size distribution and accumulate closely.
基金Funded by the National Natural Science Foundation of China (No. 50674048)Research Fund for the Doctoral Program of Higher Education of China(No.20103227110006)
文摘One-dimensional and quasi-one-dimensional nanostructure materials are promising building blocks for electromagnetic devices and nanosystems.In this work,the composite Ni0.5Zn0.5Fe2O4（NZFO）/ Pb（Zr0.52Ti0.48）O3（PZT） nanofibers with average diameters about 65 nm are prepared by electrospinning from poly（vinyl pyrrolidone） （PVP） and metal salts.The precursor composite NZFO/PZT/PVP nanofibers and the subsequent calcined NZFO/PZT nanofibers are investigated by Fourier transform infrared spectroscopy （FT- IR） ,X-ray diffraction （XRD）,scanning electron microscopy （SEM）.The magnetic properties for nanofibers are measured by vibrating sample magnetometer（VSM）.The NZFO/PZT nanofibers obtained at calcination temperature of 900 °C for 2 h consist of the ferromagnetic spinel NZFO and ferroelectric perovskite PZT phases,which are constructed from about 37 nm NZFO and 17 nm PZT grains.The saturation magnetization of these NZFO/PZT nanofibers increases with increasing calcination temperature and contents of NZFO in the composite.
基金This project was supported by the National Natural Science Foundation of China (1972003).
文摘With sol-gel method, nanometer La-Ti composite oxide was successfully prepared at a low temperature (750～800C) using polyethylene glycol as dispersant. By means of atomic force microscope, the surface pattern, particle size distribution, and specific surface area were studied. The compound particle surface appears as a smooth sheet, the mean size of the compound is 25.38 nm. On the specific surface, the particle erects at a height of 4.69 nm. The surface area is 58.90 nm2. The La-Ti composite oxide nanocrystal prefers to narrow and even particle size distribution and the homogeneity of surface topography.
基金supported by Major Science and Technology Project of Water Pollution Control and Management(No.2017ZX07101003)Zhejiang Provincial Natural Science Foundation of China under Grant no.LR17B060003financially supported by the Natural Science Foundation of China(Project Nos.21436007,21522606,21476201,21676246,U1462201,and 21776248)
文摘Although there have been many reports of metal doping to ameliorate the drawbacks of hematite as the photoanode for water oxidation, most of them focused on monometallic doping, and only a few of them payed attention to bimetallic doping. What is worse, the synergetic mechanism between two metal dopants was not sufficiently studied, especially the density functional theory(DFT) calculation. In this work, the n-type hematite was synthesized by introducing Ti dopant into hematite through the hydrothermal method, and dipping-sintering treatment was employed to further introduce homogeneously dispersed Zn dopant into that, forming the Ti, Zn co-doped hematite. Under the optimal condition, Tidoped hematite photoanode reached approximately 2-times enhancement of the photocurrent density compared with the pristine one at 1.23 V vs. RHE, while Ti, Zn co-doped hematite anode obtained another25% elevation. UV–Vis spectroscopy, Mott–Schottky plots, EIS analysis, photo-oxidation of hole scavenger(H2O2), and DFT calculation were employed to understand the role of Ti, Zn dopant. Based on the obtained results, the synergetic mechanism of two dopants was discussed, i.e., the improvement of PEC performance of Ti, Zn co-doped hematite photoanode was possibly attributed to greater carrier density and improved charge separation efficiency at the surface of hematite. This work provides new strategy and understanding of the improvement of PEC performance of hematite by doping engineering.
基金Project(51271012)supported by the National Natural Science Foundation of China
文摘Anodized composite films containing Si C nanoparticles were synthesized on Ti6Al4 V alloy by anodic oxidation procedure in C4O6H4Na2 electrolyte. Scanning electron microscopy(SEM), energy dispersive spectroscopy(EDS) and X-ray photoelectron spectroscopy(XPS) were employed to characterize the morphology and composition of the films fabricated in the electrolytes with and without addition of Si C nanoparticles. Results show that Si C particles can be successfully incorporated into the oxide film during the anodizing process and preferentially concentrate within internal cavities and micro-cracks. The ball-on-disk sliding tests indicate that Si C-containing oxide films register much lower wear rate than the oxide films without Si C under dry sliding condition. Si C particles are likely to melt and then are oxidized by frictional heat during sliding tests. Potentiodynamic polarization behavior reveals that the anodized alloy with Si C nanoparticles results in a reduction in passive current density to about 1.54×10-8 A/cm2, which is more than two times lower than that of the Ti O2 film(3.73×10-8 A/cm2). The synthesized composite film has good anti-wear and anti-corrosion properties and the growth mechanism of nanocomposite film is also discussed.
基金supported by a National Program on Key Basic Research Project(973 Program,Grant No.2011CB808903)National Natural Science Foundation of China(Grant Nos.41073030 and 41121002)a 'CAS Hundred Talents' project under Chinese Academy of Sciences to CYW and a GIGCAS 135 project Y234041001
文摘The Xinjie layered intrusion in the Panxi region,SW China,hosts both Fe-Ti oxide and platinum-group element（PGE） sulfide mineralization.The intrusion can be divided,from the base upward,into UnitsⅠ,ⅡandⅢ,in terms of mineral assemblages.UnitsⅠandⅡare mainly composed of wehrlite and clino-pyroxenite, whereas UnitⅢis mainly composed of gabbro.PGE sulfide-rich layers mainly occur in Unit I, whereas thick Fe-Ti oxide-rich layers mainly occur in UnitⅢ.An ilmenite-rich layer occurs at the top of UnitⅠ.Fe-Ti oxides include magnetite and ilmenite.Small amounts of cumulus and intercumulus magnetite occur in UnitsⅠandⅡ.Cumulus magnetite grains are commonly euhedral and enclosed within olivine and clinopyroxene.They have high Cr2O3 contents ranging from 6.02 to 22.5 wt.%,indicating that they are likely an early crystallized phase from magmas.Intercumulus magnetite that usually displays ilmenite exsolution occupies the interstices between cumulus olivine crystals and coexists with interstitial clinopyroxene and plagioclase.Intercumulus magnetite has Cr2O3 ranging from 1.65 to 6.18 wt.%, lower than cumulus magnetite.The intercumulus magnetite may have crystallized from the trapped liquid.Large amounts of magnetite in UnitⅢcontains Cr2O3（＆lt;0.28 wt.%） much lower than magnetite in UnitsⅠandⅡ.The magnetite in UnitⅢis proposed to be accumulated from a Fe-Ti-rich melt.The Fe-Ti-rich melt is estimated to contain 35.9 wt.%of SiO2,26.9 wt.%of FeOt,8.2 wt.%of TiO2,13.2 wt.%of CaO, 8.3 wt.%of MgO,5.5 wt.%of Al2O3 and 1.0 wt.%of P2O5.The composition is comparable with the Fe-rich melts in the Skaergaard and Sept Iles intrusions.Paired non-reactive microstructures,granophyre pockets and ilmenite-rich intergrowths,are representative of Si-rich melt and Fe-Ti-rich melt,and are the direct evidence for the existence of an immiscible Fe-Ti-rich melt that formed from an evolved ferro-basaltic magma.