Microstructures and mechanical properties of as-extruded and heat treated Mg-6Zn-1Mn-4Sn-1.5Nd alloy

The microstructures and mechanical properties of Mg-6Zn-1Mn-4Sn-1.5Nd alloy subjected to extrusion and T5 treatment were investigated using optical microscopy（OM）, X-ray diffractometer（XRD）, scanning electron microscopy（SEM）, electron back scattered diffraction（EBSD）, transmission electron microscopy（TEM）, hardness tests and uniaxial tensile tests. The results showed that the as-cast alloy consisted of α（Mg）, Mn, Mg7Zn3, Mg2 Sn and Mg Sn Nd phases. Dynamic recrystallization has completed during the extrusion process and the average grain size was 7.2 μm. After T5 treatment, the strength increased obviously, the yield strength and ultimate tensile strength of as-extruded alloy were increased by 94 and 34 MPa, respectively. Microstructure characterization revealed that the improvement of strength was determined by the high number density of β′1 rods.

Effects of calcium addition on as-cast microstructure and mechanical properties of Mg-5Zn-5Sn alloy

The effects of Ca addition on the as-cast microstructure and mechanical properties of the Mg-5Zn-5Sn (mass fraction,%) alloy were investigated.The results indicate that an addition of 0.5%-1.5% (mass fraction) Ca to the Mg-5Zn-5Sn alloy not only refines the as-cast microstructure of the alloy but also causes the formation of the primary and/or eutectic CaMgSn phases with high thermal stability;an increase in Ca amount from 0.5% to 1.5% (mass fraction) increases the amount and size of the CaMgSn phase.In addition,Ca addition to the Mg-5Zn-5Sn alloy improves not only the tensile properties at room temperature and 150 ℃ but also the creep properties.Among the Ca-containing Mg-5Zn-5Sn alloys,the one added 0.5% (mass fraction) Ca obtains the optimum ultimate tensile strength and elongation at room temperature and 150 ℃,however,the alloy added 1.5% (mass fraction) Ca exhibits the optimum yield strength and creep properties.

Residual stress and precipitation of Mg-5Zn-3.5Sn-1Mn-0.5Ca-0.5Cu alloy with different quenching rates

The effect of the quenching rate after solution treatment on the residual stress and precipitation behavior of a high strength Mg-5 Zn-3.5 Sn-1 Mn-0.5 Ca-0.5 Cu plate is studied.The simulation results show decreasing temperature gradient in the plate with decreasing quenching rate,which leads to weakened inhomogeneous plastic deformation and decreased residual stress.No dynamic precipitation on the grain boundary happens after either cold water cooling or air cooling,however,air cooling leads to dynamic precipitation of Mg-Zn phase on Mn particles around which a low-density precipitate zone develops after aging treatment.Moreover,the fine and densely distributed Mg-Zn precipitates observed after aging treatment of the cold water cooled alloy are replaced by coarse precipitates with low density for the air cooled alloy.Both the low-density precipitate zone near Mn particles and the coarsening of precipitates are the source of the decrease in hardness and tensile properties of the air cooled alloy.The residual stress drops faster than the hardness with decreasing quenching rate,which makes it possible to lower the residual stress without sacrificing too much age-hardening ability of the alloy.

Microstructure evolution and mechanical properties of ultrasonic-assisted soldering joints of 2024 aluminum alloys

Ultrasonic-assisted soldering of 2024 aluminum alloys using a filler metal of Zn-5Al alloy was investigated at the temperature of 400 ℃,which is lower than the solution strengthening temperature of Al-Cu alloys.The ultrasonic vibration with power of 200 W and vibration amplitude of 15 μm at the frequency of 21 kHz was applied on the top samples.The ultrasonic vibration promoted the dissolution of Al elements in the base metal.The reduction of volume fraction of the eutectic phases in the bonds was investigated by increasing ultrasonic vibration time.As the ultrasonic vibration time increased from 3 s to 30 s,the volume fraction of the eutectic phase in the bonds decreased from 12.9% to 0.9%,and the shear strength of the joints was up to 149-153 MPa,increased by 20%.The improvement of the mechanical properties of joints was discussed based on the modulus and hardness of the phases in the bonds and the fracture of the joints.

Friction and wear behavior of Mg–11Y–5Gd–2Zn–0.5Zr(wt%)alloy with oil lubricant

The sliding friction and wear behaviors of Mg-11Y-5Gd-2Zn-0.5Zr （wt%） alloy were investigated under oil lubricant condition by pin-on-disk configuration with a constant sliding distance of 1,000 m in the temperature range of 25-200℃. Results indicate that the volumetric wear rates and average friction coefficients decrease with the increase of sliding speeds, and increase with the increase of test temperature below 150℃. The hard and thermally stable Mg12（Y,Gd）Zn phase with long-period stacking order structure in the alloy presents significant wear resistance, The wear mechanism below 100℃ is abrasive wear as a result of plastic extrusion deformation. The corporate effects of severe abrasive, oxidative, and delaminating wear result in the tribological mechanism above 100℃.

Formation mechanism of the Zn-5%Al hot-dip coating amorphous alloys(Ⅰ)--The analysis of differential scanning calorimetry

HOT-DIPPING Zn+5% Al + (0.01%-0.2%) RE alloy on steel surface by the gas reductionmethod is a new technology. Owing to its good anti-corrosive and forming properties as wellas good technical periormances, the coating attracts wide interest and has been put into indus-trial production rapidly. The authors successfully produced the coating by the electrolytic ac-tivity aid agent method and put it into industrial production. The products have been used inthe electric power and railway engineerings. Results show that the anti-corrosive

Fe和Ce含量对Galfan合金力学性能及耐蚀性的影响

将真空熔炼的Zn-Fe-Ce中间合金加入到Zn-Al熔池中,制备Zn-5Al-0.1Ce-xFe和Zn-5Al-yCe-0.1Fe合金,分析了Fe和Ce含量对合金显微组织及力学性能的影响,并使用电化学工作站测试了合金的电化学性能。结果表明,在Zn-5Al-0.1Ce合金中Fe含量大于0.02%后会形成颗粒状的FeAl3Znx相。随着Fe含量的增加,FeAl3Znx相和先共晶的η-Zn相增加,Zn-Al共晶组织由层片状向点状转变。添加0.1%以下的Fe可提高Galfan合金的抗拉强度。但随着Fe含量的增加,合金的抗拉强度略有降低,Zn-5Al-0.1Ce-0.02Fe合金的综合力学性能最好。添加0.04%以下的Fe会提升合金耐蚀性。此外,随着Ce含量的增加,Zn-5Al-yCe-0.1Fe合金的抗拉强度有所降低,耐蚀性变化不明显。因此,在生产中需要根据镀层性能要求,严格控制合金液中的Fe和Ce含量。