A new zinc hydrogen phosphite C4H8N2H4·Zn（HPO3）2 was prepared by hydrothermal method in the presence of piperazine as a structure-directing agent and the crystal structure was determined by single-crystal X-ray...A new zinc hydrogen phosphite C4H8N2H4·Zn（HPO3）2 was prepared by hydrothermal method in the presence of piperazine as a structure-directing agent and the crystal structure was determined by single-crystal X-ray diffraction analysis and further characterized by X-ray powder diffraction, IR, ICP, elemental analysis and TG analysis. This compound has one-dimensional anionic chains containing four-membered rings built from corner-sharing linked alternating ZnO4 tetrahedra and HPO3 pseudo pyramids. The zinc hydrogen phosphite chains are interacted with the templates of diprotonated piperazine by N—H…O hydrogen bond. Crystal data for C4H8N2H4·Zn（HPO3）2∶monoclinic, space group C2/c. a=1.774 8（2） nm, b=0.724 28（9） nm, c=0.880 87（11） nm, β= 105.345（3）°, V=1.091 9（2） nm 3, Z=4, Dc=1^907 Mg/m 3, R1=0.022 9, wR2=0.058 8.展开更多
A novel three dimensional fluorinated gallium phosphate has been hydrothermally synthesized by using diethylenetriamine as an organic structure directing agent. X ray single crystal structure analysis indicates this c...A novel three dimensional fluorinated gallium phosphate has been hydrothermally synthesized by using diethylenetriamine as an organic structure directing agent. X ray single crystal structure analysis indicates this compound crystallizes in the orthorhombic space group Pbca, a =1.605 6(7) nm, b = 1 011 4 (4) nm, c =1.854 6(5) nm, V =3.011 6(19) nm 3, Z =4. The three dimensional framework based on linkage of corner sharing polyhedron PO 4, GaO 4F and GaO 4F 2 delimit ten ring channels along b axis in which the triply protonated amines are located serving as charge compensating guests and supporters.展开更多
A novel one-dimensional chain complex [Zn(dafo)2(H2O)2](NO3)2 was synthesized. It has been characterized by IR, UV, TGA, Elemental analysis and X-ray diffraction analysis. The crystal belongs to triclinic system, P1 s...A novel one-dimensional chain complex [Zn(dafo)2(H2O)2](NO3)2 was synthesized. It has been characterized by IR, UV, TGA, Elemental analysis and X-ray diffraction analysis. The crystal belongs to triclinic system, P1 space group. The Crystallographic data are: a = 0.702 7(14) nm, b = 0.828 95(17) nm, c = 10.225(2) nm, α = 95.02(3)°, β = 91.45(3)°, γ = 99.85(3)°. The crystal structure data indicate that the Zn(Ⅱ) ion was coordinated with the four nitrogen atoms of two dafo and two oxygen atoms of two coordination water molecules, respectively. The complex has a one-dimensional chain structure, which is formed by hydrogen bonds.展开更多
A new two dimensional 8 ring network nickle phosphate Ni 3(PO 4) 2·8H 2O was synthesized hydrothermally and its structure was determined by means of single crystal X ray diffraction. The Ni 3(PO 4) 2·8H 2O c...A new two dimensional 8 ring network nickle phosphate Ni 3(PO 4) 2·8H 2O was synthesized hydrothermally and its structure was determined by means of single crystal X ray diffraction. The Ni 3(PO 4) 2·8H 2O crystal crystallizes in the monoclinic system, space group C2/m , with M=128.13, a =0\^994 7(2) nm, b =1.321 7(3) nm; c =0.463 6(1) nm; β=104.80(3)°, V =0.589 3(2) nm 3, Z=2, R=0.027 2 and wR =0.057 5. The network structure consists of vertex sharing which results in the formation of undulating 4 ring chains and 8 ring sheets.展开更多
The novel polyoxometalate, 32[Mo8ⅣMo4ⅤV2ⅣO38(PO4)], was synthesized and characterized by elementary analysis, EPR, IR spectra and X ray diffraction. The compoundcrystallizes in triclinic system, space group with a=...The novel polyoxometalate, 32[Mo8ⅣMo4ⅤV2ⅣO38(PO4)], was synthesized and characterized by elementary analysis, EPR, IR spectra and X ray diffraction. The compoundcrystallizes in triclinic system, space group with a= 1.41999(2)nm, b=1.43467(2)nm, c=1.694610(10)nm, α=95.7250(10)°, β=92.2110(10)°, γ=92.6060(10)°, V=3.42829(7)nm3, Z=2, Dc=2.388g·cm-3, Mr=2465.10g·mol-1, μ=2.489mm-1, F(000)=2388, R1=0.0584, wR2=0.1461, S=1.164. The heteropolyanion is a bi capped pseudo Keggin complex. CCDC: 186645.展开更多
A\} novel two-dimensional coordination polymer Zn 3(PTC) 2(H 2O) 8·4H 2O was formed by \{Zn(CH 3COO) 2·\}2H 2O and 2-pyridine-1,3,5-tricarboxylate(H 3PTC) under the hydrothermal condition at 417 K and charac...A\} novel two-dimensional coordination polymer Zn 3(PTC) 2(H 2O) 8·4H 2O was formed by \{Zn(CH 3COO) 2·\}2H 2O and 2-pyridine-1,3,5-tricarboxylate(H 3PTC) under the hydrothermal condition at 417 K and characterized by fluorescence. The crystal structure of the compound was determined by single-crystal X-ray diffraction analyses. The six-coordinated Zinc(Ⅱ) center displays an octahedral geometry . The crystal is monoclinic and space group is P2(1)/c with a=0.722 70(14) nm, b= 1.866 7(4) nm , \{c=\}1.072 6(3) nm, α=90°, β=103.198(19)°, γ=90°, V=1.408 7(6) nm 3, Z=4, D c= 2.474 Mg/m 3, M r=828.536, μ=3.099 mm -1 , F(000)=1 060, GOF=0.892, R=0.061 3, wR= 0.133 9 .展开更多
A new compound 2 6[Co(H 2O) 2(VO) 8(OH) 4(PO 4) 8] has been hydrothermally synthesized. Single crystal X-ray analysis indicates that this compound crystallizes in a monoclinic system, space group P2 1/n with a=1.438 5...A new compound 2 6[Co(H 2O) 2(VO) 8(OH) 4(PO 4) 8] has been hydrothermally synthesized. Single crystal X-ray analysis indicates that this compound crystallizes in a monoclinic system, space group P2 1/n with a=1.438 5(3) nm, b=1.012 2(2) nm, c=1.832 5(4) nm, β=90.21°, V=2\^668 2(9) nm 3, Z=2, D c=2.112 g/cm 3, R=0.055, wR=0.149 7, S=1.037. The structure of 2 6[Co(H 2O) 2(VO) 8(OH) 4(PO 4) 8] is characterized by P-V-O layers constructed by [(VO) 4(OH) 2(PO 4) 4] 6- non-symmetric units. The P-V-O layers are pillared by [Co(H 2O) 2] 2+ group, resulting in the channels within which the protonated diaminoethane and H 3O + are located.展开更多
Ga 3(PO 4) 4](H 3NCH 2CH 2) 2NH 2(abbr. to GaP 1) has been synthesized by a hydrothermal method. X ray crystal structure analysis indicates GaP 1 crystallizes in monoclinic, with space group C2/c , a =2 079 3(5) nm, b...Ga 3(PO 4) 4](H 3NCH 2CH 2) 2NH 2(abbr. to GaP 1) has been synthesized by a hydrothermal method. X ray crystal structure analysis indicates GaP 1 crystallizes in monoclinic, with space group C2/c , a =2 079 3(5) nm, b =1 194 2(2) nm, c =1 648 0(4) nm, β =117 064(14)°, V =3 644 2(13) nm 3, Z =6, D c=1 901 g/cm 3, I ≥2 σ(I )=2 274, R =0 055 6, R w=0 134 8. GaP 1 is characteristic of the intercalation of disordered fully protonated diethylenetriamine among two dimensional inorganic framework built up from PO 4, GaO 5 and GaO 6 primary structure units. The framework features 3 , 4 , 5 and 8 ring topological connectivity.展开更多
By using inorganic salts as raw materials and citric acid as complexing agent, α-Zn 3(PO 4) 2 and Eu 3+ doped α-Zn 3(PO 4) 2 phosphor powders were prepared by a citrate-gel process. X-ray diffraction (XRD), T...By using inorganic salts as raw materials and citric acid as complexing agent, α-Zn 3(PO 4) 2 and Eu 3+ doped α-Zn 3(PO 4) 2 phosphor powders were prepared by a citrate-gel process. X-ray diffraction (XRD), TG-DTA, FT-IR and luminescence excitation and emission spectra were used to characterize the resulting products. The results of XRD reveal that the powders begin to crystallize at 500 ℃ and pure α-Zn 3(PO 4) 2 phase is obtained at 800 ℃. And the results of XRD reveal that Eu 3+ exists as EuPO 4 in the powder. In the phosphor powders, the Eu 3+ shows its characteristic red-orange (592 nm, 5D 0- 7F 1) emission and has no quenching concentration.展开更多
文摘A new zinc hydrogen phosphite C4H8N2H4·Zn（HPO3）2 was prepared by hydrothermal method in the presence of piperazine as a structure-directing agent and the crystal structure was determined by single-crystal X-ray diffraction analysis and further characterized by X-ray powder diffraction, IR, ICP, elemental analysis and TG analysis. This compound has one-dimensional anionic chains containing four-membered rings built from corner-sharing linked alternating ZnO4 tetrahedra and HPO3 pseudo pyramids. The zinc hydrogen phosphite chains are interacted with the templates of diprotonated piperazine by N—H…O hydrogen bond. Crystal data for C4H8N2H4·Zn（HPO3）2∶monoclinic, space group C2/c. a=1.774 8（2） nm, b=0.724 28（9） nm, c=0.880 87（11） nm, β= 105.345（3）°, V=1.091 9（2） nm 3, Z=4, Dc=1^907 Mg/m 3, R1=0.022 9, wR2=0.058 8.
文摘A novel three dimensional fluorinated gallium phosphate has been hydrothermally synthesized by using diethylenetriamine as an organic structure directing agent. X ray single crystal structure analysis indicates this compound crystallizes in the orthorhombic space group Pbca, a =1.605 6(7) nm, b = 1 011 4 (4) nm, c =1.854 6(5) nm, V =3.011 6(19) nm 3, Z =4. The three dimensional framework based on linkage of corner sharing polyhedron PO 4, GaO 4F and GaO 4F 2 delimit ten ring channels along b axis in which the triply protonated amines are located serving as charge compensating guests and supporters.
文摘A novel one-dimensional chain complex [Zn(dafo)2(H2O)2](NO3)2 was synthesized. It has been characterized by IR, UV, TGA, Elemental analysis and X-ray diffraction analysis. The crystal belongs to triclinic system, P1 space group. The Crystallographic data are: a = 0.702 7(14) nm, b = 0.828 95(17) nm, c = 10.225(2) nm, α = 95.02(3)°, β = 91.45(3)°, γ = 99.85(3)°. The crystal structure data indicate that the Zn(Ⅱ) ion was coordinated with the four nitrogen atoms of two dafo and two oxygen atoms of two coordination water molecules, respectively. The complex has a one-dimensional chain structure, which is formed by hydrogen bonds.
文摘A new two dimensional 8 ring network nickle phosphate Ni 3(PO 4) 2·8H 2O was synthesized hydrothermally and its structure was determined by means of single crystal X ray diffraction. The Ni 3(PO 4) 2·8H 2O crystal crystallizes in the monoclinic system, space group C2/m , with M=128.13, a =0\^994 7(2) nm, b =1.321 7(3) nm; c =0.463 6(1) nm; β=104.80(3)°, V =0.589 3(2) nm 3, Z=2, R=0.027 2 and wR =0.057 5. The network structure consists of vertex sharing which results in the formation of undulating 4 ring chains and 8 ring sheets.
文摘The novel polyoxometalate, 32[Mo8ⅣMo4ⅤV2ⅣO38(PO4)], was synthesized and characterized by elementary analysis, EPR, IR spectra and X ray diffraction. The compoundcrystallizes in triclinic system, space group with a= 1.41999(2)nm, b=1.43467(2)nm, c=1.694610(10)nm, α=95.7250(10)°, β=92.2110(10)°, γ=92.6060(10)°, V=3.42829(7)nm3, Z=2, Dc=2.388g·cm-3, Mr=2465.10g·mol-1, μ=2.489mm-1, F(000)=2388, R1=0.0584, wR2=0.1461, S=1.164. The heteropolyanion is a bi capped pseudo Keggin complex. CCDC: 186645.
文摘A\} novel two-dimensional coordination polymer Zn 3(PTC) 2(H 2O) 8·4H 2O was formed by \{Zn(CH 3COO) 2·\}2H 2O and 2-pyridine-1,3,5-tricarboxylate(H 3PTC) under the hydrothermal condition at 417 K and characterized by fluorescence. The crystal structure of the compound was determined by single-crystal X-ray diffraction analyses. The six-coordinated Zinc(Ⅱ) center displays an octahedral geometry . The crystal is monoclinic and space group is P2(1)/c with a=0.722 70(14) nm, b= 1.866 7(4) nm , \{c=\}1.072 6(3) nm, α=90°, β=103.198(19)°, γ=90°, V=1.408 7(6) nm 3, Z=4, D c= 2.474 Mg/m 3, M r=828.536, μ=3.099 mm -1 , F(000)=1 060, GOF=0.892, R=0.061 3, wR= 0.133 9 .
文摘A new compound 2 6[Co(H 2O) 2(VO) 8(OH) 4(PO 4) 8] has been hydrothermally synthesized. Single crystal X-ray analysis indicates that this compound crystallizes in a monoclinic system, space group P2 1/n with a=1.438 5(3) nm, b=1.012 2(2) nm, c=1.832 5(4) nm, β=90.21°, V=2\^668 2(9) nm 3, Z=2, D c=2.112 g/cm 3, R=0.055, wR=0.149 7, S=1.037. The structure of 2 6[Co(H 2O) 2(VO) 8(OH) 4(PO 4) 8] is characterized by P-V-O layers constructed by [(VO) 4(OH) 2(PO 4) 4] 6- non-symmetric units. The P-V-O layers are pillared by [Co(H 2O) 2] 2+ group, resulting in the channels within which the protonated diaminoethane and H 3O + are located.
文摘Ga 3(PO 4) 4](H 3NCH 2CH 2) 2NH 2(abbr. to GaP 1) has been synthesized by a hydrothermal method. X ray crystal structure analysis indicates GaP 1 crystallizes in monoclinic, with space group C2/c , a =2 079 3(5) nm, b =1 194 2(2) nm, c =1 648 0(4) nm, β =117 064(14)°, V =3 644 2(13) nm 3, Z =6, D c=1 901 g/cm 3, I ≥2 σ(I )=2 274, R =0 055 6, R w=0 134 8. GaP 1 is characteristic of the intercalation of disordered fully protonated diethylenetriamine among two dimensional inorganic framework built up from PO 4, GaO 5 and GaO 6 primary structure units. The framework features 3 , 4 , 5 and 8 ring topological connectivity.
文摘By using inorganic salts as raw materials and citric acid as complexing agent, α-Zn 3(PO 4) 2 and Eu 3+ doped α-Zn 3(PO 4) 2 phosphor powders were prepared by a citrate-gel process. X-ray diffraction (XRD), TG-DTA, FT-IR and luminescence excitation and emission spectra were used to characterize the resulting products. The results of XRD reveal that the powders begin to crystallize at 500 ℃ and pure α-Zn 3(PO 4) 2 phase is obtained at 800 ℃. And the results of XRD reveal that Eu 3+ exists as EuPO 4 in the powder. In the phosphor powders, the Eu 3+ shows its characteristic red-orange (592 nm, 5D 0- 7F 1) emission and has no quenching concentration.