A series of nominal compositions MgAl_(2-x)(Li_(1/3)Ti_(2/3))_(x)O_(4)(x=0,0.04,0.08,0.12,0.16,and 0.20)ceramics were successfully prepared via the conventional solid-state reaction route.The phase compositions,micros...A series of nominal compositions MgAl_(2-x)(Li_(1/3)Ti_(2/3))_(x)O_(4)(x=0,0.04,0.08,0.12,0.16,and 0.20)ceramics were successfully prepared via the conventional solid-state reaction route.The phase compositions,microstructures,and microwave dielectric properties were investigated.The results of x-ray diffraction(XRD)and scanning electron microscopy(SEM)showed that a single phase of MgAl_(2-x)(Li_(1/3)Ti_(2/3))_(x)O_(4)ceramics with a spinel structure was obtained at x≤0.12,whereas the second phase of MgTi_(2)O_(5)appeared when x>0.12.The cell parameters were obtained by XRD refinement.As the x values increased,the unit cell volume kept expanding.This phenomenon could be attributed to the partial substitution of(Li_(1/3)Ti_(2/3))^(3+)for Al^(3+).Results showed that(Li_(1/3)Ti_(2/3))^(3+)doping into MgAl_(2)O_(4)spinel ceramics effectively reduced the sintering temperature and improved the quality factor(Q_f)values.Good microwave dielectric properties were achieved for a sample at x=0.20 sintering at 1500℃in air for 4 h:dielectric constantε_(r)=8.78,temperature coefficient of resonant frequencyτ_(f)=-85 ppm/℃,and Q_(f)=62300 GHz.The Q_(f)value of the x=0.20 sample was about 2 times higher than that of pure MgAl_(2)O_(4)ceramics(31600 GHz).Thus,MgAl_(2-x)(Li_(1/3)Ti_(2/3))_(x)O_(4)ceramics with excellent microwave dielectric properties can be applied to 5G communications.展开更多
Direct conversion of syngas to aromatics(STA)over oxide-zeolite composite catalysts is promising as an alternative method for aromatics production.However,the structural effect of the oxide component in composite cata...Direct conversion of syngas to aromatics(STA)over oxide-zeolite composite catalysts is promising as an alternative method for aromatics production.However,the structural effect of the oxide component in composite catalysts is still ambiguous.Herein,we investigate the size effect by selecting ZnCr_(2)O_(4)spinel,as a probe oxide,mixing with H-ZSM-5 zeolite as a composite catalyst for STA reaction.The CO conversion,aromatics selectivity and space-time yield(STY)of aromatics are all significantly improved with the crystal size of ZnCr_(2)O_(4)oxide decreases,which can mainly attribute to the higher oxygen vacancy concentration and thus the rapid generation of more C1oxygenated intermediate species.Based on the understanding of the size-performance relationship,ZnCr_(2)O_(4)-400 with a smaller size mixing with H-ZSM-5 can achieve32.6%CO conversion with 76%aromatics selectivity.The STY of aromatics reaches as high as 4.79 mmol g_(cat)^(-1)h^(-1),which outperforms the previously reported some typical catalysts.This study elucidates the importance of regulating the size of oxide to design more efficient oxidezeolite composite catalysts for conversion of syngas to value-added chemicals.展开更多
基金the Chengdu University of Technology(Grant No.KYQD201907728)。
文摘A series of nominal compositions MgAl_(2-x)(Li_(1/3)Ti_(2/3))_(x)O_(4)(x=0,0.04,0.08,0.12,0.16,and 0.20)ceramics were successfully prepared via the conventional solid-state reaction route.The phase compositions,microstructures,and microwave dielectric properties were investigated.The results of x-ray diffraction(XRD)and scanning electron microscopy(SEM)showed that a single phase of MgAl_(2-x)(Li_(1/3)Ti_(2/3))_(x)O_(4)ceramics with a spinel structure was obtained at x≤0.12,whereas the second phase of MgTi_(2)O_(5)appeared when x>0.12.The cell parameters were obtained by XRD refinement.As the x values increased,the unit cell volume kept expanding.This phenomenon could be attributed to the partial substitution of(Li_(1/3)Ti_(2/3))^(3+)for Al^(3+).Results showed that(Li_(1/3)Ti_(2/3))^(3+)doping into MgAl_(2)O_(4)spinel ceramics effectively reduced the sintering temperature and improved the quality factor(Q_f)values.Good microwave dielectric properties were achieved for a sample at x=0.20 sintering at 1500℃in air for 4 h:dielectric constantε_(r)=8.78,temperature coefficient of resonant frequencyτ_(f)=-85 ppm/℃,and Q_(f)=62300 GHz.The Q_(f)value of the x=0.20 sample was about 2 times higher than that of pure MgAl_(2)O_(4)ceramics(31600 GHz).Thus,MgAl_(2-x)(Li_(1/3)Ti_(2/3))_(x)O_(4)ceramics with excellent microwave dielectric properties can be applied to 5G communications.
基金National Natural Science Foundation of China(12175254,U1832119)National Key R&D Program of China(2021YFE0104800)+2 种基金International Partnership Program of Chinese Academy of Sciences(121631KYSB20200039)International Cooperation Project of Shanghai Science and Technology Commission(20520750200)National Centre for Research and Development(WPC2/1/SCAPOL/2021)。
基金financial support from the National Natural Science Foundation of China(Grant No.21978285,21991093,21991090)the“Transformational Technologies for Clean Energy and Demonstration”,Strategic Priority Research Program of the Chinese Academy of Sciences(Grant No.XDA21030100)。
文摘Direct conversion of syngas to aromatics(STA)over oxide-zeolite composite catalysts is promising as an alternative method for aromatics production.However,the structural effect of the oxide component in composite catalysts is still ambiguous.Herein,we investigate the size effect by selecting ZnCr_(2)O_(4)spinel,as a probe oxide,mixing with H-ZSM-5 zeolite as a composite catalyst for STA reaction.The CO conversion,aromatics selectivity and space-time yield(STY)of aromatics are all significantly improved with the crystal size of ZnCr_(2)O_(4)oxide decreases,which can mainly attribute to the higher oxygen vacancy concentration and thus the rapid generation of more C1oxygenated intermediate species.Based on the understanding of the size-performance relationship,ZnCr_(2)O_(4)-400 with a smaller size mixing with H-ZSM-5 can achieve32.6%CO conversion with 76%aromatics selectivity.The STY of aromatics reaches as high as 4.79 mmol g_(cat)^(-1)h^(-1),which outperforms the previously reported some typical catalysts.This study elucidates the importance of regulating the size of oxide to design more efficient oxidezeolite composite catalysts for conversion of syngas to value-added chemicals.
基金Project(SKL-SPM-202021) supported by the State Key Laboratory of Advanced Technologies for Comprehensive Utilization of Platinum Metals,ChinaProject(2023YFQ0082) supported by Sichuan Science and Technology Program,ChinaProject(EFMD2022005Z) supported by Guangdong Provincial Key Laboratory of Electronic Functional Materials and Devices,China。
基金National Key R&D Program of China(2016YFB0402101,2017YFB0310500)Key Research Project of the Frontier Science of the Chinese Academy of Sciences(QYZDB-SSW-JSC022)。