The ferrites of Cuo-ZnO-Fe2o3 solid solution series near the molar ratio of ZnxCu1-x were prepared by direct heating of their coprecipitated hydroxides using NH4OH as precipitating agent where x=0.0, 0.2, 0.5, 0.8 and...The ferrites of Cuo-ZnO-Fe2o3 solid solution series near the molar ratio of ZnxCu1-x were prepared by direct heating of their coprecipitated hydroxides using NH4OH as precipitating agent where x=0.0, 0.2, 0.5, 0.8 and 1.0. Additional amounts of Cu and Zn sulphates were added to compensate the loss during the coprecipitation of the hydroxides. The ferritized samples were characterized by chemical analysis, XRD. DTA, TGA and SEM. XRD of both Zn0.2Cu0.8Fe2O4 and Zn0.5Cu0.5 Fe2O4 that indicates the formation of a heterogeneous ferrite material of ZnFe2O4 and CuFe2O4 mixed with variable amounts of α-Fe2O3. Zn and Cu ferrites were observed only in Zn0.8Cu0.2Fe2O4.From TGA-time relation, the activation energy of the different transformation phases were calculated. It is found that, the activation energy of ZnFe2O4 is slightly equal to 3/2 of that for CuFe2O4. Dielectric measurements show that the electrical behaviour depends on the ordering and disordering of the phases.展开更多
A solid ternary mixture consisting of NaF,silicon and one metal oxide such as La2O3,CeO2,Pr6O11,Nd2O3,and Y2O3 was prepared and usedas de-fluorinated reagent for CF4 decomposition.The results show that 90% conversion ...A solid ternary mixture consisting of NaF,silicon and one metal oxide such as La2O3,CeO2,Pr6O11,Nd2O3,and Y2O3 was prepared and usedas de-fluorinated reagent for CF4 decomposition.The results show that 90% conversion of CF4 can be reached initially over NaF-Si-La2O3,NaF-Si-CeO2,NaF-Si-Nd2O3,and NaF-Si-Y2O3 at 850 C.The fresh and used reagents were characterized using XRD and XPS techniques.It was found that the active components of NaF and metal oxides in NaF-Si-CeO2,NaF-Si-Pr6O11,NaF-Si-Nd2O3,and NaF-Si-Y2O3 weretransformed into inert phases of mixed metal fluorides and silicates,respectively,resulting in an ineffective utilization of these de-fluorinatedreagents,whereas no inert phases from NaF and La2O3 can be observed in the used NaF-Si-La2O3,indicating the NaF-Si-La2O3 reagent couldbe utilized more efficiently than the other reagents in CF4 decomposition.展开更多
The conditions of ZnO-Al2O3 aqueous suspensions and slip casting were optimized to obtain dense green compacts and further to obtain high density ZnO-Al2O3 ceramic composites.The Zeta potential of raw powders was meas...The conditions of ZnO-Al2O3 aqueous suspensions and slip casting were optimized to obtain dense green compacts and further to obtain high density ZnO-Al2O3 ceramic composites.The Zeta potential of raw powders was measured.ZnO and Al2O3 powders have lower Zeta potential than-45 mV commonly at pH 8-10.3 with polyacrylic acid(PAA)added.The influence of pH and the mass fraction of the additives on the stability and fluidity of the suspensions added with PAA and polyethylene glycol(PEG) was investigated by experiments of viscosity and sedimentation.The suspensions have the lowest viscosity and the best stability at pH 9 with 0.2%PAA(mass fraction).The maximum density of green compacts is 66.6%of theoretical density(TD)with compacting and homogeneous green particles.An ultrahigh density sintered compact(>99.6%TD)could be obtained after pressureless sintering at 1 400℃for 2 h.展开更多
A glass crusher was developed to improve the waste glass crushing process.The waste glass was recycled,crushed and sieved to different particle sizes as glass aggregates,and the surface of glass aggregates was treated...A glass crusher was developed to improve the waste glass crushing process.The waste glass was recycled,crushed and sieved to different particle sizes as glass aggregates,and the surface of glass aggregates was treated by nano-Fe2O3 suspension to improve the anti-striping property.The glasphalt mixture made by partly replacing mineral aggregates with glass aggregates was designed and evaluated.The sizes of glass aggregates were selected to be 2.36 and 4.75 mm,and the optimum concentration of nano-Fe2O3 suspension was determined to be 10%.The optimum asphalt content(OAC)was determined by the Marshall method and the glass aggregate content.The influence of the glass aggregate content on the technical properties of glasphalt mixtures were analyzed by the rutting test,three-point bending test,freeze-thaw splitting test and skid resistance test.The results show that the optimal content of glass aggregates and OAC are recommended to be 15%and 4.4%,respectively.These environmentally-friendly glasphalt mixtures can solve the problem of environmental pollution caused by waste glass,as well as reducing the cost of pavement materials and construction.展开更多
The viscosities for the selected CaO-MgO-SiO2 and CaO-MgO Al2 O3-SiO2 slags were measured by rota- ting cylinder method in a wide temperature range from 1608 K to 1 823 K. The effects of temperature, slag basicity and...The viscosities for the selected CaO-MgO-SiO2 and CaO-MgO Al2 O3-SiO2 slags were measured by rota- ting cylinder method in a wide temperature range from 1608 K to 1 823 K. The effects of temperature, slag basicity and Al2 O3 content were studied. The results indicated that the viscosity decreased with increasing the slag basicity at the same temperature. And the viscosities of the slag initially increased linearly with increasing Al2 O3 content in the slags and then decreased as the Al2 O3 content in the slags continued to increase. Al2 O3 addition has a more signifi- cant effect on the viscosity than slag basicity in the selected slags. Based on the experimental data and the fraction of solid phases calculated by the thermodynamic software, the effect of solid phases on slag viscosity was evaluated. The results indicated that the relationship between the relative viscosity and the volume fraction of solid phases esti- mated from the slag composition can be reasonable by allowing the inverse maximum fraction of solid particles to vary.展开更多
In this paper,a novel copper-based catalyst for FCC gasoline improving the ability of removal the sulfur and avoiding the loss of the octane number from olefin saturation by reactive adsorption desulfurization(RADS) w...In this paper,a novel copper-based catalyst for FCC gasoline improving the ability of removal the sulfur and avoiding the loss of the octane number from olefin saturation by reactive adsorption desulfurization(RADS) was investigated.The series of Cu/Zn O-Al_2 O_3 catalysts were characterized by X-ray powder diffraction(XRD),N_2 adsorption analysis and temperature-programmed reduction(TPR) studies,X-ray photoelectron spectroscopy(XPS),scanning electron microscope(SEM) and transmission electron microscopy(TEM).The experiment results showed that the catalysts had an optimum desulfurization ability with copper loading 6 wt%,which the sulfur contents of product decreased less than 10 μg/g and olefin contents decreased from 16.19% to 14.14% for the long period operation.The appropriate Cu loading content could lead to the high active and low apparent activation energy(E_a).Therefore,the Cu-based catalyst may become a novel catalyst for second-generation for reactive adsorption desulfurization,which achieves the high desulfurization active and low olefins saturation to satisfy the upgrading the product.展开更多
文摘The ferrites of Cuo-ZnO-Fe2o3 solid solution series near the molar ratio of ZnxCu1-x were prepared by direct heating of their coprecipitated hydroxides using NH4OH as precipitating agent where x=0.0, 0.2, 0.5, 0.8 and 1.0. Additional amounts of Cu and Zn sulphates were added to compensate the loss during the coprecipitation of the hydroxides. The ferritized samples were characterized by chemical analysis, XRD. DTA, TGA and SEM. XRD of both Zn0.2Cu0.8Fe2O4 and Zn0.5Cu0.5 Fe2O4 that indicates the formation of a heterogeneous ferrite material of ZnFe2O4 and CuFe2O4 mixed with variable amounts of α-Fe2O3. Zn and Cu ferrites were observed only in Zn0.8Cu0.2Fe2O4.From TGA-time relation, the activation energy of the different transformation phases were calculated. It is found that, the activation energy of ZnFe2O4 is slightly equal to 3/2 of that for CuFe2O4. Dielectric measurements show that the electrical behaviour depends on the ordering and disordering of the phases.
基金supported by the National Natural Science Foundation of China (No. 20976149)
文摘A solid ternary mixture consisting of NaF,silicon and one metal oxide such as La2O3,CeO2,Pr6O11,Nd2O3,and Y2O3 was prepared and usedas de-fluorinated reagent for CF4 decomposition.The results show that 90% conversion of CF4 can be reached initially over NaF-Si-La2O3,NaF-Si-CeO2,NaF-Si-Nd2O3,and NaF-Si-Y2O3 at 850 C.The fresh and used reagents were characterized using XRD and XPS techniques.It was found that the active components of NaF and metal oxides in NaF-Si-CeO2,NaF-Si-Pr6O11,NaF-Si-Nd2O3,and NaF-Si-Y2O3 weretransformed into inert phases of mixed metal fluorides and silicates,respectively,resulting in an ineffective utilization of these de-fluorinatedreagents,whereas no inert phases from NaF and La2O3 can be observed in the used NaF-Si-La2O3,indicating the NaF-Si-La2O3 reagent couldbe utilized more efficiently than the other reagents in CF4 decomposition.
基金Project(50477044)supported by the National Natural Science Foundation of China
文摘The conditions of ZnO-Al2O3 aqueous suspensions and slip casting were optimized to obtain dense green compacts and further to obtain high density ZnO-Al2O3 ceramic composites.The Zeta potential of raw powders was measured.ZnO and Al2O3 powders have lower Zeta potential than-45 mV commonly at pH 8-10.3 with polyacrylic acid(PAA)added.The influence of pH and the mass fraction of the additives on the stability and fluidity of the suspensions added with PAA and polyethylene glycol(PEG) was investigated by experiments of viscosity and sedimentation.The suspensions have the lowest viscosity and the best stability at pH 9 with 0.2%PAA(mass fraction).The maximum density of green compacts is 66.6%of theoretical density(TD)with compacting and homogeneous green particles.An ultrahigh density sintered compact(>99.6%TD)could be obtained after pressureless sintering at 1 400℃for 2 h.
基金The Project of the Department of Science&Technology of Shaanxi Province(No.2016KJXX-69,2016ZDJC-24,2017KCT-13)China Postdoctoral Science Foundation(No.2017M620434)the Special Fund for Basic Scientific Research of Central College of Chang’an University(No.310821153502,310821173501)
文摘A glass crusher was developed to improve the waste glass crushing process.The waste glass was recycled,crushed and sieved to different particle sizes as glass aggregates,and the surface of glass aggregates was treated by nano-Fe2O3 suspension to improve the anti-striping property.The glasphalt mixture made by partly replacing mineral aggregates with glass aggregates was designed and evaluated.The sizes of glass aggregates were selected to be 2.36 and 4.75 mm,and the optimum concentration of nano-Fe2O3 suspension was determined to be 10%.The optimum asphalt content(OAC)was determined by the Marshall method and the glass aggregate content.The influence of the glass aggregate content on the technical properties of glasphalt mixtures were analyzed by the rutting test,three-point bending test,freeze-thaw splitting test and skid resistance test.The results show that the optimal content of glass aggregates and OAC are recommended to be 15%and 4.4%,respectively.These environmentally-friendly glasphalt mixtures can solve the problem of environmental pollution caused by waste glass,as well as reducing the cost of pavement materials and construction.
基金Item Sponsored by National Natural Science Foundation of China(50874072)Natural Science Foundation of Jiangsu Province of China(BK20130308)China Postdoctoral Science Foundation(2014M561710)
文摘The viscosities for the selected CaO-MgO-SiO2 and CaO-MgO Al2 O3-SiO2 slags were measured by rota- ting cylinder method in a wide temperature range from 1608 K to 1 823 K. The effects of temperature, slag basicity and Al2 O3 content were studied. The results indicated that the viscosity decreased with increasing the slag basicity at the same temperature. And the viscosities of the slag initially increased linearly with increasing Al2 O3 content in the slags and then decreased as the Al2 O3 content in the slags continued to increase. Al2 O3 addition has a more signifi- cant effect on the viscosity than slag basicity in the selected slags. Based on the experimental data and the fraction of solid phases calculated by the thermodynamic software, the effect of solid phases on slag viscosity was evaluated. The results indicated that the relationship between the relative viscosity and the volume fraction of solid phases esti- mated from the slag composition can be reasonable by allowing the inverse maximum fraction of solid particles to vary.
基金financially support by the National Natural Science Foundation (Grants No.2117625821676300)the Fundamental Research Funds for the Central Universities (Grants No.15CX06051A)
文摘In this paper,a novel copper-based catalyst for FCC gasoline improving the ability of removal the sulfur and avoiding the loss of the octane number from olefin saturation by reactive adsorption desulfurization(RADS) was investigated.The series of Cu/Zn O-Al_2 O_3 catalysts were characterized by X-ray powder diffraction(XRD),N_2 adsorption analysis and temperature-programmed reduction(TPR) studies,X-ray photoelectron spectroscopy(XPS),scanning electron microscope(SEM) and transmission electron microscopy(TEM).The experiment results showed that the catalysts had an optimum desulfurization ability with copper loading 6 wt%,which the sulfur contents of product decreased less than 10 μg/g and olefin contents decreased from 16.19% to 14.14% for the long period operation.The appropriate Cu loading content could lead to the high active and low apparent activation energy(E_a).Therefore,the Cu-based catalyst may become a novel catalyst for second-generation for reactive adsorption desulfurization,which achieves the high desulfurization active and low olefins saturation to satisfy the upgrading the product.