B_2O_3-SiO_2-ZnO-BaO-Al_2O_3 glass with different Al_2O_3 contents（1mol%, 3mol%, 5mol%, and 7mol%） was prepared, and it was intended to be used as lead-free and low-melting glass sealants for solid oxide fuel cells....B_2O_3-SiO_2-ZnO-BaO-Al_2O_3 glass with different Al_2O_3 contents（1mol%, 3mol%, 5mol%, and 7mol%） was prepared, and it was intended to be used as lead-free and low-melting glass sealants for solid oxide fuel cells. The effects of Al_2O_3 content on the structures, thermal properties, and sintering behaviors of the B_2O_3-SiO_2-ZnO-BaO-Al_2O_3 glass were investigated in detail. The Al_2O_3 content largely influenced the structures and thermal properties of the glass. When the Al_2O_3 content 5mol%, the transition temperature of the glass decreased with the Al_2O_3 content, while the crystallization temperature increased with the Al_2O_3 content. However, higher Al_2O_3 content degraded the stability of the glass. The B_2O_3-SiO_2-ZnO-BaO-Al_2O_3 glass with 5 mol% Al_2O_3 content exhibits the optimal sintering densification characteristics and can be used as glass sealants for solid oxide fuel cells.展开更多
In order to investigate the effect of the La2O3 on the phase separation and crystallization of ZnO-B2O3-SiO2 glass, after the occurence of the phase separation and crystallization of glasses by heat treatment, the mic...In order to investigate the effect of the La2O3 on the phase separation and crystallization of ZnO-B2O3-SiO2 glass, after the occurence of the phase separation and crystallization of glasses by heat treatment, the microstructure morphology and distribution of elements in different sample areas were characterized by the scanning electron microscopy(SEM) and energy dispersive spectroscopy(EDS);the non-isothermal crystallization kinetics of the glass samples was studied by using a differential scanning calorimeter(DSC) and the precipitated crystals of crystallized glass were determined by the X-ray diffraction(XRD). The results suggest that the phase separation and crystallization of 60ZnO-30 B2O3-10SiO2 glass occur at glass surface, and the incorporation of small amount(<4 mol%) of La2O3 significantly inhibits the glass phase separation and consequently improves the thermal stability of glass.Doping of La2O3 accelerates the glass crystallization at the elevated temperature(660 ℃), making the depth of crystal layer thicker and diffraction intensity in XRD patterns stronger. However, due to the precipitation of several crystals that occur simultaneously when La2O3 doping amount is 4 mol%, crystallization of the 60ZnO-30B2O3-10SiO2 glass is obviously depressed, the crystallization activation energy Ec and the relative crystallinity Xc of the glass reach the maximum and the minimum values, respectively.Although transition from one-dimensional growth of crystals to two-dimensional growth of crystals results from La2O3 addition, the one-dimensional growth of crystals remains dominant in crystallization process. This work can provide some useful information for preparing glass ceramics with nano-crystals precipitated in the glass surface.展开更多
Through measuring the coefficient of linear expansion, the structure and properties of the Li2O-Al2O3-SiO2 low expansion glass ceramics containing B2O3 are studied by JR and XRD. It is shoutn that the IR method is eff...Through measuring the coefficient of linear expansion, the structure and properties of the Li2O-Al2O3-SiO2 low expansion glass ceramics containing B2O3 are studied by JR and XRD. It is shoutn that the IR method is efficient in the study of the glass-ceramics structure. There is a " Boron abnormality" in the system which has an important influence on the properties of the glass-ceramics.展开更多
基金Funded by the Jiangxi Provincial Department of Education(KJLD13008)the National Natural Science Foundation of China(number 51362020)the Research Fund for the Doctoral Program of Higher Education(20123601110006)
文摘B_2O_3-SiO_2-ZnO-BaO-Al_2O_3 glass with different Al_2O_3 contents（1mol%, 3mol%, 5mol%, and 7mol%） was prepared, and it was intended to be used as lead-free and low-melting glass sealants for solid oxide fuel cells. The effects of Al_2O_3 content on the structures, thermal properties, and sintering behaviors of the B_2O_3-SiO_2-ZnO-BaO-Al_2O_3 glass were investigated in detail. The Al_2O_3 content largely influenced the structures and thermal properties of the glass. When the Al_2O_3 content 5mol%, the transition temperature of the glass decreased with the Al_2O_3 content, while the crystallization temperature increased with the Al_2O_3 content. However, higher Al_2O_3 content degraded the stability of the glass. The B_2O_3-SiO_2-ZnO-BaO-Al_2O_3 glass with 5 mol% Al_2O_3 content exhibits the optimal sintering densification characteristics and can be used as glass sealants for solid oxide fuel cells.
基金Project supported by National Natural Science Foundation of China(51662033,51362019)Natural Science Foundation of the Inner Mongolia Autonomous Region(2016JQ05)
文摘In order to investigate the effect of the La2O3 on the phase separation and crystallization of ZnO-B2O3-SiO2 glass, after the occurence of the phase separation and crystallization of glasses by heat treatment, the microstructure morphology and distribution of elements in different sample areas were characterized by the scanning electron microscopy(SEM) and energy dispersive spectroscopy(EDS);the non-isothermal crystallization kinetics of the glass samples was studied by using a differential scanning calorimeter(DSC) and the precipitated crystals of crystallized glass were determined by the X-ray diffraction(XRD). The results suggest that the phase separation and crystallization of 60ZnO-30 B2O3-10SiO2 glass occur at glass surface, and the incorporation of small amount(<4 mol%) of La2O3 significantly inhibits the glass phase separation and consequently improves the thermal stability of glass.Doping of La2O3 accelerates the glass crystallization at the elevated temperature(660 ℃), making the depth of crystal layer thicker and diffraction intensity in XRD patterns stronger. However, due to the precipitation of several crystals that occur simultaneously when La2O3 doping amount is 4 mol%, crystallization of the 60ZnO-30B2O3-10SiO2 glass is obviously depressed, the crystallization activation energy Ec and the relative crystallinity Xc of the glass reach the maximum and the minimum values, respectively.Although transition from one-dimensional growth of crystals to two-dimensional growth of crystals results from La2O3 addition, the one-dimensional growth of crystals remains dominant in crystallization process. This work can provide some useful information for preparing glass ceramics with nano-crystals precipitated in the glass surface.
文摘Through measuring the coefficient of linear expansion, the structure and properties of the Li2O-Al2O3-SiO2 low expansion glass ceramics containing B2O3 are studied by JR and XRD. It is shoutn that the IR method is efficient in the study of the glass-ceramics structure. There is a " Boron abnormality" in the system which has an important influence on the properties of the glass-ceramics.