The heterogeneously copper-catalyzed oxidative cleavage of styrene was studied using copper-doped mesoporous KIT-6（CU-KIT-6_x） prepared via pH adjustment（where x is the pH：1.43,2.27,3.78,3.97,4.24 or 6.62）.Variat...The heterogeneously copper-catalyzed oxidative cleavage of styrene was studied using copper-doped mesoporous KIT-6（CU-KIT-6_x） prepared via pH adjustment（where x is the pH：1.43,2.27,3.78,3.97,4.24 or 6.62）.Variations in the catalyst structure and morphology with pH values were characterized by X-ray power diffraction,nitrogen adsorption-desorption analysis,transmission electron microscopy and X-ray photoelectron spectroscopy.As the pH value applied during the initial synthesis,the resulting Cu-KIT-6_x exhibited different structural,textural and surface characteristics,especially in terms of specific copper species and copper content At a pH value of 3.78,approximately 4.6 wt%copper（Ⅱ） was successfully incorporated into the framework of the initial KIT-6,in the form of-Cu-O-Si- groups.The catalytic performance of each catalyst was evaluated by following the epoxidation of styrene,employing tert-butyl hydroperoxide as the oxidant and CH_3CN as the solvent.A significant styrene conversion of 43.5%with 86.6%selectivity for the desired styrene epoxide was obtained over the Cu-KIT-63.78.A higher Cu content,an ordered cubic laid mesoporous architecture and various specific textural characteristics all combined to endow the Cu-KIT-63.78 with high catalytic activity and good stability.展开更多
Zirconium doped mesoporous KIT-6 samples with different Si/Zr ratios were synthesized by the direct hydrothermal method.Various characterization techniques confirm that highly distributed ZrO_2 nanoparticles and multi...Zirconium doped mesoporous KIT-6 samples with different Si/Zr ratios were synthesized by the direct hydrothermal method.Various characterization techniques confirm that highly distributed ZrO_2 nanoparticles and multicoordinated Zr^(4+) species are incorporated in the mesoporous composites.One-pot synthesis of 5-hydroxymethylfurfura(HMF) from glucose was examined in the presence of Zr-KIT-6(20) the molar ratio of Si to Zr is 20 under aqueous system.The effects of temperature,reaction time,catalyst dosage and biphasic solvent system on the conversion of glucose and the HMF yield were investigated.It was found that the glucose conversion and the HMF yield have been improved from 54.8% to 79.0% and from 19.5% to 34.5% in the biphasic MIBK-water system,respectively.Both the acidity of Zr-KIT-6(20) and the biphasic MIBK-water system are responsible for the improved performance of glucose dehydration to HMF.展开更多
基金supported by Guangdong Science and Technology Planning Project(2015A020216002)Guangdong Natural Science Foundation(2014A030313259)the National Natural Science Foundation of China(21543014,21173086,U1301245)~~
文摘The heterogeneously copper-catalyzed oxidative cleavage of styrene was studied using copper-doped mesoporous KIT-6（CU-KIT-6_x） prepared via pH adjustment（where x is the pH：1.43,2.27,3.78,3.97,4.24 or 6.62）.Variations in the catalyst structure and morphology with pH values were characterized by X-ray power diffraction,nitrogen adsorption-desorption analysis,transmission electron microscopy and X-ray photoelectron spectroscopy.As the pH value applied during the initial synthesis,the resulting Cu-KIT-6_x exhibited different structural,textural and surface characteristics,especially in terms of specific copper species and copper content At a pH value of 3.78,approximately 4.6 wt%copper（Ⅱ） was successfully incorporated into the framework of the initial KIT-6,in the form of-Cu-O-Si- groups.The catalytic performance of each catalyst was evaluated by following the epoxidation of styrene,employing tert-butyl hydroperoxide as the oxidant and CH_3CN as the solvent.A significant styrene conversion of 43.5%with 86.6%selectivity for the desired styrene epoxide was obtained over the Cu-KIT-63.78.A higher Cu content,an ordered cubic laid mesoporous architecture and various specific textural characteristics all combined to endow the Cu-KIT-63.78 with high catalytic activity and good stability.
基金Supported by the National Natural Science Foundation of China(21476267)the China–Japan International Cooperation Project(2013DFG50150)the Hunan Provincial Science and Technology Department Plan Project(2016TP1007)
文摘Zirconium doped mesoporous KIT-6 samples with different Si/Zr ratios were synthesized by the direct hydrothermal method.Various characterization techniques confirm that highly distributed ZrO_2 nanoparticles and multicoordinated Zr^(4+) species are incorporated in the mesoporous composites.One-pot synthesis of 5-hydroxymethylfurfura(HMF) from glucose was examined in the presence of Zr-KIT-6(20) the molar ratio of Si to Zr is 20 under aqueous system.The effects of temperature,reaction time,catalyst dosage and biphasic solvent system on the conversion of glucose and the HMF yield were investigated.It was found that the glucose conversion and the HMF yield have been improved from 54.8% to 79.0% and from 19.5% to 34.5% in the biphasic MIBK-water system,respectively.Both the acidity of Zr-KIT-6(20) and the biphasic MIBK-water system are responsible for the improved performance of glucose dehydration to HMF.