The influence of Zr content on the microstructure and mechanical properties of implant Ti-35Nb-4Sn-6Mo-xZr （x=0, 3, 6, 9, 12, 15; mass fraction） alloys was investigated. It is shown that Ti-35Nb-4Sn-6Mo-xZr alloys a...The influence of Zr content on the microstructure and mechanical properties of implant Ti-35Nb-4Sn-6Mo-xZr （x=0, 3, 6, 9, 12, 15; mass fraction） alloys was investigated. It is shown that Ti-35Nb-4Sn-6Mo-xZr alloys appear to have equiaxed single β microstructure after solution treatment at 1023 K. It is found that the grains are refined first and then coarsened with the increase of Zr content. It is also found that Zr element added to titanium alloys has both the solution strengthening and fine-grain strengthening effect, and affects the lattice parameters. With increasing the Zr content of the alloys, the strength increases, the elongation decreases, whereas the elastic modulus firstly increases and then decreases. The mechanical properties of Ti-35Nb-4Sn-6Mo-9Zr alloy are as follows： σb=785 MPa, δ=11%, E=68 GPa, which is more suitable for acting as human implant materials compared to the traditional implant Ti-6Al-4V alloy.展开更多
对应口腔环境中 p H值发生明显变化以及形成龋齿的自然现象 ,采用加速试验法研究了新型钛合金在不同 p H值乳酸中浸泡的耐腐蚀性能。研究表明当 p H=4即酸性略高于龋齿发病时酸性条件下 ,新型牙科钛合金能够完全耐乳酸腐蚀。在乳酸中腐...对应口腔环境中 p H值发生明显变化以及形成龋齿的自然现象 ,采用加速试验法研究了新型钛合金在不同 p H值乳酸中浸泡的耐腐蚀性能。研究表明当 p H=4即酸性略高于龋齿发病时酸性条件下 ,新型牙科钛合金能够完全耐乳酸腐蚀。在乳酸中腐蚀形式以点蚀为主 ,且随酸性增强有向晶间腐蚀转变的趋势。ICP分析表明合金在乳酸中的溶解析出物主要是 Fe,Fe的加入不利于合金的耐腐蚀性能。热力学计算表明设计的新型钛合金氧化膜含有 Mn2 O3、Nb2 O5、Zr O2 和 Ti O2 中的全部或部分 ,XPS分析表明氧化膜中的确含有 Mn2 O3、Nb2 O5和 Ti O2 ,主要是 Ti O2 。这三种氧化物致密且 Ti O2 和 Nb2 O5耐腐蚀 ,有利于合金的耐腐蚀性能。展开更多
The precipitation behaviours of Al3Zr precipitate in the Al-Cu-Zr and Al-Cu-Zr-Ti-V alloys were studied by transmission electron microscopy. Metastable Al3Zr precipitates are homogeneously nucleated in dendrite centre...The precipitation behaviours of Al3Zr precipitate in the Al-Cu-Zr and Al-Cu-Zr-Ti-V alloys were studied by transmission electron microscopy. Metastable Al3Zr precipitates are homogeneously nucleated in dendrite centres resulting in homogeneous distribution. However, the precipitation in the interdendritic regions is complex and the precipitation morphologies, helical-like and stripe-like shapes, were observed, which are composed of many spherical Al3Zr precipitates. The stripe-like precipitate clusters have preferential orientations along with the -100- Al directions, which is inferred to be related to θ′（Al2Cu） and θ phases. Addition of Cu can accelerate the L12→D023 structural transformation of the Al3Zr precipitate.展开更多
基金Project(BE2011778)supported by Science and Technology Support Program of Jiangsu Province,ChinaProject(CE20115036)supported by Science and Technology Support Program of Changzhou City,China
文摘The influence of Zr content on the microstructure and mechanical properties of implant Ti-35Nb-4Sn-6Mo-xZr （x=0, 3, 6, 9, 12, 15; mass fraction） alloys was investigated. It is shown that Ti-35Nb-4Sn-6Mo-xZr alloys appear to have equiaxed single β microstructure after solution treatment at 1023 K. It is found that the grains are refined first and then coarsened with the increase of Zr content. It is also found that Zr element added to titanium alloys has both the solution strengthening and fine-grain strengthening effect, and affects the lattice parameters. With increasing the Zr content of the alloys, the strength increases, the elongation decreases, whereas the elastic modulus firstly increases and then decreases. The mechanical properties of Ti-35Nb-4Sn-6Mo-9Zr alloy are as follows： σb=785 MPa, δ=11%, E=68 GPa, which is more suitable for acting as human implant materials compared to the traditional implant Ti-6Al-4V alloy.
文摘对应口腔环境中 p H值发生明显变化以及形成龋齿的自然现象 ,采用加速试验法研究了新型钛合金在不同 p H值乳酸中浸泡的耐腐蚀性能。研究表明当 p H=4即酸性略高于龋齿发病时酸性条件下 ,新型牙科钛合金能够完全耐乳酸腐蚀。在乳酸中腐蚀形式以点蚀为主 ,且随酸性增强有向晶间腐蚀转变的趋势。ICP分析表明合金在乳酸中的溶解析出物主要是 Fe,Fe的加入不利于合金的耐腐蚀性能。热力学计算表明设计的新型钛合金氧化膜含有 Mn2 O3、Nb2 O5、Zr O2 和 Ti O2 中的全部或部分 ,XPS分析表明氧化膜中的确含有 Mn2 O3、Nb2 O5和 Ti O2 ,主要是 Ti O2 。这三种氧化物致密且 Ti O2 和 Nb2 O5耐腐蚀 ,有利于合金的耐腐蚀性能。
基金Project (CDJZR12130048) supported by the Fundamental Research Funds for the Central Universities, ChinaProject supported by a Grant from the French Norwegian Foundation for Scientific and Technological Research and Industrial Development
文摘The precipitation behaviours of Al3Zr precipitate in the Al-Cu-Zr and Al-Cu-Zr-Ti-V alloys were studied by transmission electron microscopy. Metastable Al3Zr precipitates are homogeneously nucleated in dendrite centres resulting in homogeneous distribution. However, the precipitation in the interdendritic regions is complex and the precipitation morphologies, helical-like and stripe-like shapes, were observed, which are composed of many spherical Al3Zr precipitates. The stripe-like precipitate clusters have preferential orientations along with the -100- Al directions, which is inferred to be related to θ′（Al2Cu） and θ phases. Addition of Cu can accelerate the L12→D023 structural transformation of the Al3Zr precipitate.