Dense zirconium coatings on copper substrates were obtained in an alumina crucible and a stainless steel crucible from FLiNaK-K_(2)ZrF_(6)molten salt at 1023 K.Due to the potential difierences between copper and zirco...Dense zirconium coatings on copper substrates were obtained in an alumina crucible and a stainless steel crucible from FLiNaK-K_(2)ZrF_(6)molten salt at 1023 K.Due to the potential difierences between copper and zirconium,zirconium can difiuse into the copper substrate to form zirconium alloys on the surface of copper substrates in the course of deposition.The coating deposited in a stainless steel crucible has a gray surface.The components of the coating are mainly CuZr2alloy and Cu_(10)Zr_(7)alloy,and,the outermost layer of the coating is a layer of amorphous pure zirconium.The coating deposited in an alumina crucible has a silvery white metallic luster.The components of the coating are mainly Cu-Zr-Al intermetallic compounds,AlCu_(2)Zr,ZrAl,AlCu and CuZr.Furthermore,two types of zirconium coatings can greatly increase the hardness of the substrate.展开更多
The unusual glass-forming ability（GFA） of the Zr48Cu36Ag8Al8 alloy and the high ductility of the Zr48Cu36Ag8Al8 metallic glass-matrix composites containing Ta powder were reported.The bulk metallic glass rod with a ...The unusual glass-forming ability（GFA） of the Zr48Cu36Ag8Al8 alloy and the high ductility of the Zr48Cu36Ag8Al8 metallic glass-matrix composites containing Ta powder were reported.The bulk metallic glass rod with a diameter of 25 mm was successfully synthesized using copper mold casting for the Zr48Cu36Ag8Al8 alloy.High GFA of this alloy was found to be related to a large supercooled liquid region and a quaternary eutectic point with low melting temperature.The bulk metallic glass matrix composites were prepared by introducing extra Ta particles into the Zr48Cu36Ag8Al8 melt.The composites consist of Ta particles homogenously distributed in the Zr48Cu36Ag8Al8 metallic glass matrix.The optimum content of Ta powder is 10at%for the composite with the highest plasticity,which shows a plastic strain of 31%.展开更多
基金Funded by National MCF Energy R&D Program(No.2019YFE03130002)。
文摘Dense zirconium coatings on copper substrates were obtained in an alumina crucible and a stainless steel crucible from FLiNaK-K_(2)ZrF_(6)molten salt at 1023 K.Due to the potential difierences between copper and zirconium,zirconium can difiuse into the copper substrate to form zirconium alloys on the surface of copper substrates in the course of deposition.The coating deposited in a stainless steel crucible has a gray surface.The components of the coating are mainly CuZr2alloy and Cu_(10)Zr_(7)alloy,and,the outermost layer of the coating is a layer of amorphous pure zirconium.The coating deposited in an alumina crucible has a silvery white metallic luster.The components of the coating are mainly Cu-Zr-Al intermetallic compounds,AlCu_(2)Zr,ZrAl,AlCu and CuZr.Furthermore,two types of zirconium coatings can greatly increase the hardness of the substrate.
基金supported by Grant-In-Aid for Scientific Research(C)(No.19560689)
文摘The unusual glass-forming ability（GFA） of the Zr48Cu36Ag8Al8 alloy and the high ductility of the Zr48Cu36Ag8Al8 metallic glass-matrix composites containing Ta powder were reported.The bulk metallic glass rod with a diameter of 25 mm was successfully synthesized using copper mold casting for the Zr48Cu36Ag8Al8 alloy.High GFA of this alloy was found to be related to a large supercooled liquid region and a quaternary eutectic point with low melting temperature.The bulk metallic glass matrix composites were prepared by introducing extra Ta particles into the Zr48Cu36Ag8Al8 melt.The composites consist of Ta particles homogenously distributed in the Zr48Cu36Ag8Al8 metallic glass matrix.The optimum content of Ta powder is 10at%for the composite with the highest plasticity,which shows a plastic strain of 31%.