2Y-PSZ/TRIP steel composites have been sintered by hot-pressing method. Their microstructure and mechanical properties were investigated by means of SEM, TEM, XRD and static tension, split Hopkinson pressure bar metho...2Y-PSZ/TRIP steel composites have been sintered by hot-pressing method. Their microstructure and mechanical properties were investigated by means of SEM, TEM, XRD and static tension, split Hopkinson pressure bar method. The results showed that the strength and elastic modulus of 2Y-PSZ/TRIP steel composites at room temperature decreased with the increase of 2Y-PSZ content. The main reason was that the combining strength was quite weak between the grains of ZrO2. Distortion induced martensite transformation and plasticity during the dynamic loading increased the strength and distortion capability of the composites. The transformation was carried out mainly through twins formation. The shape of martensite induced by distortion was lamellate with substructures of twins. The habit plane was near {259}T with no mid-ridge and no explosion phenomena. The interface was straight between the austenite and martensite induced by distortion. The increase of 2Y-PSZ content, on the one hand, made the composite dynamic flow stress improved. Thereby, the fracture strength was improved. On the other hand, it depressed both the distortion capability and the martensite transformation induced by distortion. This resulted in the decrease of dynamic fracture strength.展开更多
The cermet composites WC-20wt%Co/ZrO2（E6）with four different comtents of ZrO2（3Y）were prepared by normal vacuum sinter processing;the optical microscope and SEMwere used to characterize their microstructures.The h...The cermet composites WC-20wt%Co/ZrO2（E6）with four different comtents of ZrO2（3Y）were prepared by normal vacuum sinter processing;the optical microscope and SEMwere used to characterize their microstructures.The hardness.bending strength and impact toughness of the specimens were determined.The experimental results show that ZrO2（3Y） particles in WC-20wt%Co matrix are sphcrical particles in different sizes which are distributed uniformly in Co phases and WC phases,the bending strength and impact toughness of the WC-20wt%Co cermet composites added ZrO2（3Y）improve remarkably.but the hardness values have little change.展开更多
Four composites, MoSi 2+ZrO 2, MoSi 2+ZrO 2(Y 2O 3), MoSi 2+ZrO 2+SiC and MoSi 2+ZrO 2(Y 2O 3)+SiC are fabricated by mechanical alloying. It is clear that cracks produced on the MoSi 2 matrix composites during hardnes...Four composites, MoSi 2+ZrO 2, MoSi 2+ZrO 2(Y 2O 3), MoSi 2+ZrO 2+SiC and MoSi 2+ZrO 2(Y 2O 3)+SiC are fabricated by mechanical alloying. It is clear that cracks produced on the MoSi 2 matrix composites during hardness testing belong to the Palmquist crack system. The value of highest fracture toughness of MoSi 2+ZrO 2+SiC composite is 7.58?MPa·m 1/2 , which is nearly three times that of monolithic MoSi 2. This can be attributed to well distributed ZrO 2 and SiC particles along the boundaries of very fine MoSi 2 grains.展开更多
ZrO 2 and 40Cr steel were brazed by inserting buffer Ni,4J33,Ti and Cu separately. The chemical composition of 4J33 and Ni will damage the wetting property of Ag 66 Cu 30 Ti 4 filler metal to ceramic and h...ZrO 2 and 40Cr steel were brazed by inserting buffer Ni,4J33,Ti and Cu separately. The chemical composition of 4J33 and Ni will damage the wetting property of Ag 66 Cu 30 Ti 4 filler metal to ceramic and hinder the interface reaction between the active filler metal and ZrO 2, so ZrO 2/40Cr steel can not be bonded. Cu and Ti can efficiently release the residual stresses in the ceramic without injuring the wettabilty of filler metal, so the high joining strength can be obtained by inserting Cu and Ti.展开更多
文摘2Y-PSZ/TRIP steel composites have been sintered by hot-pressing method. Their microstructure and mechanical properties were investigated by means of SEM, TEM, XRD and static tension, split Hopkinson pressure bar method. The results showed that the strength and elastic modulus of 2Y-PSZ/TRIP steel composites at room temperature decreased with the increase of 2Y-PSZ content. The main reason was that the combining strength was quite weak between the grains of ZrO2. Distortion induced martensite transformation and plasticity during the dynamic loading increased the strength and distortion capability of the composites. The transformation was carried out mainly through twins formation. The shape of martensite induced by distortion was lamellate with substructures of twins. The habit plane was near {259}T with no mid-ridge and no explosion phenomena. The interface was straight between the austenite and martensite induced by distortion. The increase of 2Y-PSZ content, on the one hand, made the composite dynamic flow stress improved. Thereby, the fracture strength was improved. On the other hand, it depressed both the distortion capability and the martensite transformation induced by distortion. This resulted in the decrease of dynamic fracture strength.
文摘The cermet composites WC-20wt%Co/ZrO2（E6）with four different comtents of ZrO2（3Y）were prepared by normal vacuum sinter processing;the optical microscope and SEMwere used to characterize their microstructures.The hardness.bending strength and impact toughness of the specimens were determined.The experimental results show that ZrO2（3Y） particles in WC-20wt%Co matrix are sphcrical particles in different sizes which are distributed uniformly in Co phases and WC phases,the bending strength and impact toughness of the WC-20wt%Co cermet composites added ZrO2（3Y）improve remarkably.but the hardness values have little change.
文摘Four composites, MoSi 2+ZrO 2, MoSi 2+ZrO 2(Y 2O 3), MoSi 2+ZrO 2+SiC and MoSi 2+ZrO 2(Y 2O 3)+SiC are fabricated by mechanical alloying. It is clear that cracks produced on the MoSi 2 matrix composites during hardness testing belong to the Palmquist crack system. The value of highest fracture toughness of MoSi 2+ZrO 2+SiC composite is 7.58?MPa·m 1/2 , which is nearly three times that of monolithic MoSi 2. This can be attributed to well distributed ZrO 2 and SiC particles along the boundaries of very fine MoSi 2 grains.
文摘ZrO 2 and 40Cr steel were brazed by inserting buffer Ni,4J33,Ti and Cu separately. The chemical composition of 4J33 and Ni will damage the wetting property of Ag 66 Cu 30 Ti 4 filler metal to ceramic and hinder the interface reaction between the active filler metal and ZrO 2, so ZrO 2/40Cr steel can not be bonded. Cu and Ti can efficiently release the residual stresses in the ceramic without injuring the wettabilty of filler metal, so the high joining strength can be obtained by inserting Cu and Ti.