Effects of interlayer composition on bonding strength and interfacial microstructure of green joined CePO_4-ZrO_2 ceramics were studied. Green bodies of 25%CePO_4/ZrO_2 and ZrO_2 ceramics were joined by using interlay...Effects of interlayer composition on bonding strength and interfacial microstructure of green joined CePO_4-ZrO_2 ceramics were studied. Green bodies of 25%CePO_4/ZrO_2 and ZrO_2 ceramics were joined by using interlayer composed of CePO_4 and ZrO_2 at 1450 ℃ for 120 min without applied pressure.The effects of CePO_4/(CePO_4+ZrO_2) ratio on the bond strength of the joints were investigated. Under the experimental conditions, the grain size of the particles grown in the joint is smaller than those in joined ceramics. The microstructure of the joint is more homogeneous than that of the matrix and without obvious cracks, pores and other defects.展开更多
The partially stabilized ZrO2 (PSZ) particles were introduced into TiB2 ceramics to improve its density and mechanical properties. The results show that the addition of PSZ is very effective not only in bettering the ...The partially stabilized ZrO2 (PSZ) particles were introduced into TiB2 ceramics to improve its density and mechanical properties. The results show that the addition of PSZ is very effective not only in bettering the sinterability but also in enhancing the flexural strength and fracture toughness of TiB2.展开更多
A dynamic process of the martensitic transformation in(Y,Mg)-PSZ ceramics was observed in situ using TEM.Under the effect of contact stress between tetragonal(t)-ZrO_2 precipi- tates,a group of substructural martensit...A dynamic process of the martensitic transformation in(Y,Mg)-PSZ ceramics was observed in situ using TEM.Under the effect of contact stress between tetragonal(t)-ZrO_2 precipi- tates,a group of substructural martensite variants may occur priorly and then another one was induced by the elastic strain relaxation,both form(100)_m twins further.In addition,the crystallography of the martensitic transformation was also discussed.展开更多
文摘Effects of interlayer composition on bonding strength and interfacial microstructure of green joined CePO_4-ZrO_2 ceramics were studied. Green bodies of 25%CePO_4/ZrO_2 and ZrO_2 ceramics were joined by using interlayer composed of CePO_4 and ZrO_2 at 1450 ℃ for 120 min without applied pressure.The effects of CePO_4/(CePO_4+ZrO_2) ratio on the bond strength of the joints were investigated. Under the experimental conditions, the grain size of the particles grown in the joint is smaller than those in joined ceramics. The microstructure of the joint is more homogeneous than that of the matrix and without obvious cracks, pores and other defects.
文摘The partially stabilized ZrO2 (PSZ) particles were introduced into TiB2 ceramics to improve its density and mechanical properties. The results show that the addition of PSZ is very effective not only in bettering the sinterability but also in enhancing the flexural strength and fracture toughness of TiB2.
文摘A dynamic process of the martensitic transformation in(Y,Mg)-PSZ ceramics was observed in situ using TEM.Under the effect of contact stress between tetragonal(t)-ZrO_2 precipi- tates,a group of substructural martensite variants may occur priorly and then another one was induced by the elastic strain relaxation,both form(100)_m twins further.In addition,the crystallography of the martensitic transformation was also discussed.
基金National Natural Science Foundation of China (52032011)State Key Laboratory of New Ceramic and Fine Processing Tsinghua University (KF 202007)Youth Fund of China Building Materials Academy (ZD-16)。