Two-dimensional ZrS2 materials have potential for applications in nanoelectronics because of their theoretically predicted high mobility and sheet current density. Herein, we report the thickness and temperature depen...Two-dimensional ZrS2 materials have potential for applications in nanoelectronics because of their theoretically predicted high mobility and sheet current density. Herein, we report the thickness and temperature dependent transport properties of ZrS2 multilayers that were directly deposited on hexagonal boron nitride (h-BN) by chemical vapor deposition. Hysteresis-free gate sweeping, metal- insulator transition, and T-γ (γ- 0.82-1.26) temperature dependent mobility were observed in the ZrS2 films.展开更多
A passively Q-switched erbium-doped fiber(EDF) laser is proposed and demonstrated utilizing a zirconium disulfide(ZrS2)-based saturable absorber(SA). ZrS2 nanosheets are prepared, whose modulation depth,saturation int...A passively Q-switched erbium-doped fiber(EDF) laser is proposed and demonstrated utilizing a zirconium disulfide(ZrS2)-based saturable absorber(SA). ZrS2 nanosheets are prepared, whose modulation depth,saturation intensity, and nonsaturable absorbance are measured to be 14.7%, 0.34 MW/cm^2, and 17.4%, respectively. Then, a Q-switched EDF laser is implemented by the ZrS2-SA. The pulse repetition rate varies from 40.65 to 87.1 k Hz when the pump power changes from 55 to 345 mW. The shortest pulse width is 1.49 μs with pulse energy of 33.5 nJ. As far as we know, this is the shortest pulse width obtained by a ZrS2-SA so far.展开更多
The effect of 0.5wt.%Zn addition on the microstructure and mechanical properties of Mg-3Y-2Nd-0.5Zr(WE32)alloy was investigated.The results indicate that WE32-0.5Zn alloy takes 48 h to reach peak hardness after solid ...The effect of 0.5wt.%Zn addition on the microstructure and mechanical properties of Mg-3Y-2Nd-0.5Zr(WE32)alloy was investigated.The results indicate that WE32-0.5Zn alloy takes 48 h to reach peak hardness after solid solution treatment at 525℃and aging at 200℃,10 h earlier than WE32 alloy,which implies an accelerated aging precipitation kinetics owing to the addition of 0.5wt.%Zn.A large quantity of finerod and rectangular block-like Zn-Zr precipitates in theα-Mg matrix are formed in the WE32-0.5Zn alloy,and numerous needle-likeβ1phases are distributed at both ends of the Zn-Zr precipitates at peak-aged condition.In peak-aged condition,the ultimate tensile strength considerably increases from 263.2 MPa(WE32)to 309.6 MPa(WE32-0.5Zn),and the elongation dramatically increases from 4.3%(WE32)to 8.9%(WE32-0.5Zn).Theβ’andβ1phases are the main precipitates of the WE32-0.5Zn alloy peak-aged at 200℃.Theβ’andβ1phases easily nucleate at the Zn-Zr precipitates,and theβ1phases are particularly likely to nucleate and grow at the interface between the two ends of the Zn-Zr precipitates,which accelerates aging precipitation kinetics and leads to a shorter time to achieve peak aging.展开更多
Creep aging forming(CAF) is a potential process used to manufacture large integral components of magnesium(Mg) alloys. The selected stress plays a crucial role in creep aging processes but the mechanism by which stres...Creep aging forming(CAF) is a potential process used to manufacture large integral components of magnesium(Mg) alloys. The selected stress plays a crucial role in creep aging processes but the mechanism by which stress loading method affects creep aging of Mg alloys is still unclear. In this paper, the microstructural evolution of precipitated phases and precipitation-free zones(PFZ) at grain boundaries with different stress loading modes(unstressed, unidirectional tensile stress, and cyclic stress) at 250 ℃ were investigated along with changes in mechanical properties. The results showed that the addition of stress during aging effectively promoted the precipitation of precipitated phases, while unaffecting grain size. Unidirectional tensile stress caused directional growth of β phase([1010]), as well as rotation of weave towards the basal plane texture, resulting in namely stress orientation effect. Solute atoms diffused in the direction of tensile stress while vacancies moved perpendicular to the direction of tensile stress, resulting in PFZ at grain boundaries(157.06 nm). By contrast, cyclic stresses led to the growth of β phase in three directions([1010], [1100] and [0110]). The solute atoms and vacancies were uniformly distributed in the Mg matrix instead of directional diffusion, effectively reducing the width of PFZ(112.39 nm) at the grain boundary. These features significantly improved the mechanical properties of alloy specimens after cyclic stress creep aging when compared to unidirectional stress creep aging, with yield strength(YS), ultimate tensile strength(UTS), and elongation(EL) enhanced from 171.6 MPa, 305.5 MPa, and 4.4%to 174.8 MPa, 326.3 MPa, and 6.9%, respectively.展开更多
基金L. M. X. acknowledges support from National Natural Science Foundation of China (Nos. 21373066 and 11304052), Beijing Nova programme (No. Z151100000315081) and Beijing Talents Fund (No. 2015000021223ZK17). C. Z. C. acknowledges support from the Program for New Century Excellent Talents in University of China (No. NCET-07-0903).
文摘Two-dimensional ZrS2 materials have potential for applications in nanoelectronics because of their theoretically predicted high mobility and sheet current density. Herein, we report the thickness and temperature dependent transport properties of ZrS2 multilayers that were directly deposited on hexagonal boron nitride (h-BN) by chemical vapor deposition. Hysteresis-free gate sweeping, metal- insulator transition, and T-γ (γ- 0.82-1.26) temperature dependent mobility were observed in the ZrS2 films.
基金supported by the National Natural Science Foundation of China (No. 11304184)partially supported by the National Natural Science Foundation of China (No. 11704226)the Natural Science Foundation of Shandong Province (No. ZR2017MA051)
文摘A passively Q-switched erbium-doped fiber(EDF) laser is proposed and demonstrated utilizing a zirconium disulfide(ZrS2)-based saturable absorber(SA). ZrS2 nanosheets are prepared, whose modulation depth,saturation intensity, and nonsaturable absorbance are measured to be 14.7%, 0.34 MW/cm^2, and 17.4%, respectively. Then, a Q-switched EDF laser is implemented by the ZrS2-SA. The pulse repetition rate varies from 40.65 to 87.1 k Hz when the pump power changes from 55 to 345 mW. The shortest pulse width is 1.49 μs with pulse energy of 33.5 nJ. As far as we know, this is the shortest pulse width obtained by a ZrS2-SA so far.
基金financially supported by the Natural Science Foundation of Inner Mongolia under Grant No.2022MS05045the Science and Technology Planning of Inner Mongolia under Grant No.2020GG0175the Project of State Key Laboratory of Baiyunobo Rare Earth Resource Researches and Comprehensive Utilization under Grant No.2021Z2351。
文摘The effect of 0.5wt.%Zn addition on the microstructure and mechanical properties of Mg-3Y-2Nd-0.5Zr(WE32)alloy was investigated.The results indicate that WE32-0.5Zn alloy takes 48 h to reach peak hardness after solid solution treatment at 525℃and aging at 200℃,10 h earlier than WE32 alloy,which implies an accelerated aging precipitation kinetics owing to the addition of 0.5wt.%Zn.A large quantity of finerod and rectangular block-like Zn-Zr precipitates in theα-Mg matrix are formed in the WE32-0.5Zn alloy,and numerous needle-likeβ1phases are distributed at both ends of the Zn-Zr precipitates at peak-aged condition.In peak-aged condition,the ultimate tensile strength considerably increases from 263.2 MPa(WE32)to 309.6 MPa(WE32-0.5Zn),and the elongation dramatically increases from 4.3%(WE32)to 8.9%(WE32-0.5Zn).Theβ’andβ1phases are the main precipitates of the WE32-0.5Zn alloy peak-aged at 200℃.Theβ’andβ1phases easily nucleate at the Zn-Zr precipitates,and theβ1phases are particularly likely to nucleate and grow at the interface between the two ends of the Zn-Zr precipitates,which accelerates aging precipitation kinetics and leads to a shorter time to achieve peak aging.
基金supported by Natural Science Foundation of Shanxi province (20210302123135,20210302123163)Science and Technology Major Project of Shanxi province (20191102008)+6 种基金Scientific and Technological Achievements Transformation Guidance Special Project of Shanxi province (202104021301022)The Ministry of Science and Higher Education of the Russian Federation for financial support under the Megagrant (No.075-15-2022-1133)the National Research Foundation (NRF) grant funded by the Ministry of Science and ICT (2015R1A2A1A01006795) of Korea through the Research Institute of Advanced MaterialsThe central government guided local science and technology development projects (YDZJSX2021A010)China Postdoctoral Science Foundation (2022M710541)the projects of International Cooperation in Shanxi (201803D421086)Research Project Supported by Shanxi Scholarship Council of China (2022- 038)。
文摘Creep aging forming(CAF) is a potential process used to manufacture large integral components of magnesium(Mg) alloys. The selected stress plays a crucial role in creep aging processes but the mechanism by which stress loading method affects creep aging of Mg alloys is still unclear. In this paper, the microstructural evolution of precipitated phases and precipitation-free zones(PFZ) at grain boundaries with different stress loading modes(unstressed, unidirectional tensile stress, and cyclic stress) at 250 ℃ were investigated along with changes in mechanical properties. The results showed that the addition of stress during aging effectively promoted the precipitation of precipitated phases, while unaffecting grain size. Unidirectional tensile stress caused directional growth of β phase([1010]), as well as rotation of weave towards the basal plane texture, resulting in namely stress orientation effect. Solute atoms diffused in the direction of tensile stress while vacancies moved perpendicular to the direction of tensile stress, resulting in PFZ at grain boundaries(157.06 nm). By contrast, cyclic stresses led to the growth of β phase in three directions([1010], [1100] and [0110]). The solute atoms and vacancies were uniformly distributed in the Mg matrix instead of directional diffusion, effectively reducing the width of PFZ(112.39 nm) at the grain boundary. These features significantly improved the mechanical properties of alloy specimens after cyclic stress creep aging when compared to unidirectional stress creep aging, with yield strength(YS), ultimate tensile strength(UTS), and elongation(EL) enhanced from 171.6 MPa, 305.5 MPa, and 4.4%to 174.8 MPa, 326.3 MPa, and 6.9%, respectively.