The chemical composition, structure and thermal stability of the spent FCC equilibrium catalyst from an oil refinery were characterized by XRD, FT-IR, DTA-TG, BET, complete chemical analysis, SEM, and XRF. The spent F...The chemical composition, structure and thermal stability of the spent FCC equilibrium catalyst from an oil refinery were characterized by XRD, FT-IR, DTA-TG, BET, complete chemical analysis, SEM, and XRF. The spent FCC equilibrium catalyst, clay, barium carbonate, and talc were used as the main raw materials to prepare the alumina abrasion-resistant ceramic balls to be used in the powder grinding mill for manufacture of architecture tiles. The results showed that after proper formulation study, the spent FCC equilibrium catalyst could replace industrial alumina to prepare high performance grinding balls. Meanwhile, the various performance indices of the grinding ball could meet the quality standard for similar products, and additionally, the energy saving effect was achieved in the operation of the grinding section, resulting in a successful comprehensive utilization of solid wastes.展开更多
Base on a vast amount of testing and calculations for the welding thermal cycling curves of different testing points in fusion welding (TIG welding, gas welding) HAZ of zinc-based alloy with low melting points, this p...Base on a vast amount of testing and calculations for the welding thermal cycling curves of different testing points in fusion welding (TIG welding, gas welding) HAZ of zinc-based alloy with low melting points, this paper defines the welding thermal cycle parameters of microstructure stimulation of HAZ by zinc-based alloy fusion welding process. On the principle of which the microstrnct,are and harkness of the testing points in simulation specimens are basically correspondence with that of actual welding HAZ, the microstructure simulation of testing points Tm=370O℃. 305℃) of ZA12 alloy by fusion welding is carried out by the means of omhic-heating welding thermal simulation tester. The study results of the abrasion-resistance of simulation specimens HAZ by fusion welding process indicates that the abmsion-resistance is closely related to the form of eutectoid microstructure in or in the structure.展开更多
基金the funding provided by the Fujian Provincial Education Department Project(JA09054)the Project administered by the Fujian Normal University(XG-004)+4 种基金the Fujian Provincial Eco- nomic and Trade Commission Project(HE0536)the Open Project of the MOE's Key Laboratory for Medical and Photoelectrical Science and Technology(JYG0821)the Open Project of Hubei Province,the State Nationalities Committee,and the MOE Joint Key Laboratory for Catalytic Material Science(CHCL08008)the Fujian Provincial Testing Fund Project for the Key Laboratory of Highmolecular Materials(FJKL-POLY2010-17)the Training for Excellence Youth Skeleton Teacher of Fujian Normal University(No.2008100228).
文摘The chemical composition, structure and thermal stability of the spent FCC equilibrium catalyst from an oil refinery were characterized by XRD, FT-IR, DTA-TG, BET, complete chemical analysis, SEM, and XRF. The spent FCC equilibrium catalyst, clay, barium carbonate, and talc were used as the main raw materials to prepare the alumina abrasion-resistant ceramic balls to be used in the powder grinding mill for manufacture of architecture tiles. The results showed that after proper formulation study, the spent FCC equilibrium catalyst could replace industrial alumina to prepare high performance grinding balls. Meanwhile, the various performance indices of the grinding ball could meet the quality standard for similar products, and additionally, the energy saving effect was achieved in the operation of the grinding section, resulting in a successful comprehensive utilization of solid wastes.
文摘Base on a vast amount of testing and calculations for the welding thermal cycling curves of different testing points in fusion welding (TIG welding, gas welding) HAZ of zinc-based alloy with low melting points, this paper defines the welding thermal cycle parameters of microstructure stimulation of HAZ by zinc-based alloy fusion welding process. On the principle of which the microstrnct,are and harkness of the testing points in simulation specimens are basically correspondence with that of actual welding HAZ, the microstructure simulation of testing points Tm=370O℃. 305℃) of ZA12 alloy by fusion welding is carried out by the means of omhic-heating welding thermal simulation tester. The study results of the abrasion-resistance of simulation specimens HAZ by fusion welding process indicates that the abmsion-resistance is closely related to the form of eutectoid microstructure in or in the structure.