Since the discovery in 2011,MXenes have become the rising star in the field of two-dimensional materials.Benefiting from the metallic-level conductivity,large and adjustable gallery spacing,low ion diffusion barrier,r...Since the discovery in 2011,MXenes have become the rising star in the field of two-dimensional materials.Benefiting from the metallic-level conductivity,large and adjustable gallery spacing,low ion diffusion barrier,rich surface chemistry,superior mechanical strength,MXenes exhibit great application prospects in energy storage and conversion,sensors,optoelectronics,electromagnetic interference shielding and biomedicine.Nevertheless,two issues seriously deteriorate the further development of MXenes.One is the high experimental risk of common preparation methods such as HF etching,and the other is the difficulty in obtaining MXenes with controllable surface groups.Recently,Lewis acidic etching,as a brand-new preparation strategy for MXenes,has attracted intensive attention due to its high safety and the ability to endow MXenes with uniform terminations.However,a comprehensive review of Lewis acidic etching method has not been reported yet.Herein,we first introduce the Lewis acidic etching from the following four aspects:etching mechanism,terminations regulation,in-situ formed metals and delamination of multi-layered MXenes.Further,the applications of MXenes and MXene-based hybrids obtained by Lewis acidic etching route in energy storage and conversion,sensors and microwave absorption are carefully summarized.Finally,some challenges and opportunities of Lewis acidic etching strategy are also presented.展开更多
Recently,SnPS_(3) has gained attention as an impressive sodium-ion battery anode material because of its significant theoretical specific capacity derived from the conversion-alloying reaction mechanism.Nevertheless,i...Recently,SnPS_(3) has gained attention as an impressive sodium-ion battery anode material because of its significant theoretical specific capacity derived from the conversion-alloying reaction mechanism.Nevertheless,its practical applicability is restricted by insufficient rate ability,and severe capacity loss due to inadequate electrical conductivity and dramatic volume expansion.Inspired by the electrochemical enhancement effect of MXene substrates and the innovative Lewis acidic etching for MXene preparation,SnPS_(3)/Ti_(3)C_(2)T_(x) MXene(T=-Cl and-O) is constructed by synchronously phospho-sulfurizing Sn/Ti_(3)C_(2)T_(x) precursor.Benefiting from the boosted Na^(+) diffusion and electron transfer rates,as well as the mitigated stress expansion,the synthesized SnPS_(3/)Ti_(3)C_(2)T_(x) composite demonstrates enhanced rate capability(647 mA h g^(-1) at 10 A g^(-1)) alongside satisfactory long-term cycling stability(capacity retention of 94.6% after 2000 cycles at 5 A g^(-1)).Importantly,the assembled sodium-ion full cell delivers an impressive capacity retention of 97.7% after undergoing 1500 cycles at 2 A g^(-1).Moreover,the sodium storage mechanism of the SnPS_(3/)Ti_(3)C_(2)T_(x) electrode is elucidated through in-situ and ex-situ characterizations.This work proposes a novel approach to ameliorate the energy storage performance of thiophosphites by facile in-situ construction of composites with MXene.展开更多
The present investigation assessed the effect of acid etching on marginal adaptation of white- and gray-colored mineral trioxide aggregate （MTA） to apical dentin using microcomputed tomography （micro-CT） and scann...The present investigation assessed the effect of acid etching on marginal adaptation of white- and gray-colored mineral trioxide aggregate （MTA） to apical dentin using microcomputed tomography （micro-CT） and scanning electron microscopy （SEM）. Sixty-four extracted single-rooted human maxillary teeth were used. Following root-end resection and apical preparation, the teeth were equally divided into four groups according to the following root end filling materials： （i） white-colored MTA （WMTA）, （ii） etched WMTA （EWMTA）, （iii） gray-colored MTA （GMTA） and （iv） etched GMTA （EGMTA）. After 48 h, the interface between root-end filling materials and the dentinal walls was assessed using micro-CT and SEM. Data were statistically analyzed using the KruskaI-Wallis and Dunn tests. Micro-CT analysis revealed gap volumes between the apical cavity dentin walls and EGMTA, GMTA, EWMTA and WMTA of （0.007 1±0.004） mm3, （0.053±0.002） mm3, （0.003 6±0.001） mm3 and （0.005 9±0.002） mm3 respectively. SEM analysis revealed gap sizes for EGMTA, WMTA, EWMTA and GMTA to be （492.3±13.8） μm, （594.5±17.12）μm, （543.1±15.33） μm and （910.7±26.2）μm respectively. A significant difference in gap size between root end preparations filled with GMTA and EGMTA was found （P〈O.05）. No significance difference in gap size between WMTA and EWMTA were found in either SEM or micro-CT analysis. In conclusion, pre-etching of apical dentin can provide a better seal for GMTA but not for WMTA.展开更多
In order to investigate how to enhance the teeth fracture resistance after the post and core treatment, an in vitro study was conducted to measure the fracture resistance of endodontically treated teeth restored with ...In order to investigate how to enhance the teeth fracture resistance after the post and core treatment, an in vitro study was conducted to measure the fracture resistance of endodontically treated teeth restored with cast post and core with two kinds of surface treatment technology and acid etching preparation on the dentinal surface. Sixty-four recently extracted human single-rooted first premolars were endodontically treated and sectioned approximately 1.5 mm above the cementoenamel junction to remove the coronal portion. Each specimen received a cast post, core build-up and a metal alloy crown restoration. All teeth were randomly divided into the smooth surface post, core repair group, the sand blasting surface post, and core repair group, each group was divided into 10 s, 30 s, 60 s acid corrosion treatment group and control group. In acid test groups, an acid etching solution was applied for 10, 30 and 60 seconds, respectively, to the root canal wall surface. Each specimen was embedded in acrylic resin block and tested in an electronic universal testing machine. Fracture loads results showed that canal acid etching could increase teeth fracture resistance strength both in smooth groups and sandblasting group, and achieved the best effect when acid etching for 30 s. Sand spray treatment on the surface of the cast metal post can improve the flexural strength of the teeth after postcrown restoration. Acid etching on the root canal wall surfaces and sand spray treatment on the surface of the cast metal post can improve the flexural strength of the root after post-crown restoration. Therefore, these two methods could be used to strengthen the tooth fracture resistance, and maintain the long-term therapeutic effect of cast post and core restoration.展开更多
基金supported by the Highstar Corporation HSD20210118Taihu Electric Corporation 0001。
文摘Since the discovery in 2011,MXenes have become the rising star in the field of two-dimensional materials.Benefiting from the metallic-level conductivity,large and adjustable gallery spacing,low ion diffusion barrier,rich surface chemistry,superior mechanical strength,MXenes exhibit great application prospects in energy storage and conversion,sensors,optoelectronics,electromagnetic interference shielding and biomedicine.Nevertheless,two issues seriously deteriorate the further development of MXenes.One is the high experimental risk of common preparation methods such as HF etching,and the other is the difficulty in obtaining MXenes with controllable surface groups.Recently,Lewis acidic etching,as a brand-new preparation strategy for MXenes,has attracted intensive attention due to its high safety and the ability to endow MXenes with uniform terminations.However,a comprehensive review of Lewis acidic etching method has not been reported yet.Herein,we first introduce the Lewis acidic etching from the following four aspects:etching mechanism,terminations regulation,in-situ formed metals and delamination of multi-layered MXenes.Further,the applications of MXenes and MXene-based hybrids obtained by Lewis acidic etching route in energy storage and conversion,sensors and microwave absorption are carefully summarized.Finally,some challenges and opportunities of Lewis acidic etching strategy are also presented.
基金financially National Natural Science Foundation of China (Grant Number: 22265018)Key Project of Natural Science Foundation of Jiangxi Province (Grant Number: 20232ACB204010)。
文摘Recently,SnPS_(3) has gained attention as an impressive sodium-ion battery anode material because of its significant theoretical specific capacity derived from the conversion-alloying reaction mechanism.Nevertheless,its practical applicability is restricted by insufficient rate ability,and severe capacity loss due to inadequate electrical conductivity and dramatic volume expansion.Inspired by the electrochemical enhancement effect of MXene substrates and the innovative Lewis acidic etching for MXene preparation,SnPS_(3)/Ti_(3)C_(2)T_(x) MXene(T=-Cl and-O) is constructed by synchronously phospho-sulfurizing Sn/Ti_(3)C_(2)T_(x) precursor.Benefiting from the boosted Na^(+) diffusion and electron transfer rates,as well as the mitigated stress expansion,the synthesized SnPS_(3/)Ti_(3)C_(2)T_(x) composite demonstrates enhanced rate capability(647 mA h g^(-1) at 10 A g^(-1)) alongside satisfactory long-term cycling stability(capacity retention of 94.6% after 2000 cycles at 5 A g^(-1)).Importantly,the assembled sodium-ion full cell delivers an impressive capacity retention of 97.7% after undergoing 1500 cycles at 2 A g^(-1).Moreover,the sodium storage mechanism of the SnPS_(3/)Ti_(3)C_(2)T_(x) electrode is elucidated through in-situ and ex-situ characterizations.This work proposes a novel approach to ameliorate the energy storage performance of thiophosphites by facile in-situ construction of composites with MXene.
文摘The present investigation assessed the effect of acid etching on marginal adaptation of white- and gray-colored mineral trioxide aggregate （MTA） to apical dentin using microcomputed tomography （micro-CT） and scanning electron microscopy （SEM）. Sixty-four extracted single-rooted human maxillary teeth were used. Following root-end resection and apical preparation, the teeth were equally divided into four groups according to the following root end filling materials： （i） white-colored MTA （WMTA）, （ii） etched WMTA （EWMTA）, （iii） gray-colored MTA （GMTA） and （iv） etched GMTA （EGMTA）. After 48 h, the interface between root-end filling materials and the dentinal walls was assessed using micro-CT and SEM. Data were statistically analyzed using the KruskaI-Wallis and Dunn tests. Micro-CT analysis revealed gap volumes between the apical cavity dentin walls and EGMTA, GMTA, EWMTA and WMTA of （0.007 1±0.004） mm3, （0.053±0.002） mm3, （0.003 6±0.001） mm3 and （0.005 9±0.002） mm3 respectively. SEM analysis revealed gap sizes for EGMTA, WMTA, EWMTA and GMTA to be （492.3±13.8） μm, （594.5±17.12）μm, （543.1±15.33） μm and （910.7±26.2）μm respectively. A significant difference in gap size between root end preparations filled with GMTA and EGMTA was found （P〈O.05）. No significance difference in gap size between WMTA and EWMTA were found in either SEM or micro-CT analysis. In conclusion, pre-etching of apical dentin can provide a better seal for GMTA but not for WMTA.
基金Funded by the Construction Engineering Special Fund of Taishan Scholars(No.201511106)the Youth Scientific Research Funds of School of Stomatology,Shandong University(No.2018QNJJ01)+1 种基金Shandong Medical and Health Science and Technology Development Plan(No.2017WS112)National Key Research and Development Program of China(No.2016YFC1102705)
文摘In order to investigate how to enhance the teeth fracture resistance after the post and core treatment, an in vitro study was conducted to measure the fracture resistance of endodontically treated teeth restored with cast post and core with two kinds of surface treatment technology and acid etching preparation on the dentinal surface. Sixty-four recently extracted human single-rooted first premolars were endodontically treated and sectioned approximately 1.5 mm above the cementoenamel junction to remove the coronal portion. Each specimen received a cast post, core build-up and a metal alloy crown restoration. All teeth were randomly divided into the smooth surface post, core repair group, the sand blasting surface post, and core repair group, each group was divided into 10 s, 30 s, 60 s acid corrosion treatment group and control group. In acid test groups, an acid etching solution was applied for 10, 30 and 60 seconds, respectively, to the root canal wall surface. Each specimen was embedded in acrylic resin block and tested in an electronic universal testing machine. Fracture loads results showed that canal acid etching could increase teeth fracture resistance strength both in smooth groups and sandblasting group, and achieved the best effect when acid etching for 30 s. Sand spray treatment on the surface of the cast metal post can improve the flexural strength of the teeth after postcrown restoration. Acid etching on the root canal wall surfaces and sand spray treatment on the surface of the cast metal post can improve the flexural strength of the root after post-crown restoration. Therefore, these two methods could be used to strengthen the tooth fracture resistance, and maintain the long-term therapeutic effect of cast post and core restoration.