The effects of SiO_(2) content on the preparation process and metallurgical properties of acid oxidized pellets, including compressive strength, reduction, and softening–melting behaviors, were systematically investi...The effects of SiO_(2) content on the preparation process and metallurgical properties of acid oxidized pellets, including compressive strength, reduction, and softening–melting behaviors, were systematically investigated.Mineralogical structures, elemental distribution, and pore size distribution were varied to analyze the mechanism of the effects.The results show that with an increase in SiO_(2) content from 3.51 wt%to 7.18 wt%, compressive strength decreases from 3150 N/pellet to 2100 N/pellet and reducibility decreases from 76.5% to 71.4%.The microstructure showed that pellets with high SiO_(2) content contained more magnetite in the mineralogical structures.Additionally, some liquid phases appeared, which hindered the continuous crystallization of hematite.Also, the softening–melting properties of the pellets clearly deteriorated as the SiO_(2) content increased.With increasing SiO_(2) content, the temperature range of the softening–melting zone decreased, and the maximum differential pressure and the comprehensive permeability index increased significantly.When acid oxidized pellets are used as the raw materials for blast furnace smelting, it should be combined with high basicity sinters to improve the softening–melting behaviors of the comprehensive charge.展开更多
基金financially supported by the Key Program of the National Natural Science Foundation of China (No.U1360205)the Natural Science Foundation of Hebei Province of China (No.E2019209424)。
文摘The effects of SiO_(2) content on the preparation process and metallurgical properties of acid oxidized pellets, including compressive strength, reduction, and softening–melting behaviors, were systematically investigated.Mineralogical structures, elemental distribution, and pore size distribution were varied to analyze the mechanism of the effects.The results show that with an increase in SiO_(2) content from 3.51 wt%to 7.18 wt%, compressive strength decreases from 3150 N/pellet to 2100 N/pellet and reducibility decreases from 76.5% to 71.4%.The microstructure showed that pellets with high SiO_(2) content contained more magnetite in the mineralogical structures.Additionally, some liquid phases appeared, which hindered the continuous crystallization of hematite.Also, the softening–melting properties of the pellets clearly deteriorated as the SiO_(2) content increased.With increasing SiO_(2) content, the temperature range of the softening–melting zone decreased, and the maximum differential pressure and the comprehensive permeability index increased significantly.When acid oxidized pellets are used as the raw materials for blast furnace smelting, it should be combined with high basicity sinters to improve the softening–melting behaviors of the comprehensive charge.