The effect of hydrochloric acid concentration on stainless steel (Fe6956) at temperature range 303 - 333 ± 1 K has been studied using weight loss, thermometric and electrochemical polarization techniques. The cor...The effect of hydrochloric acid concentration on stainless steel (Fe6956) at temperature range 303 - 333 ± 1 K has been studied using weight loss, thermometric and electrochemical polarization techniques. The corrosion rate of the stainless steel was found to be dependent on both temperature variation and acid concentration. The potentiostatic study showed that the active passive transition depends strongly on acid concentration while the weight loss measurements revealed that 2 M HCl at temperature 333 K had an appreciable corrosion rate which corresponds to 14.04 × 10﹣3 reaction number (RN) got from thermometric monitoring. Arrhenius equation and transition state theory were used to calculate kinetic and thermodynamic parameter such as Ea, ΔH* and ΔS*. Results obtained showed that corrosion reaction of Fe6956 in HCl is spontaneous and there is good agreement between the data got from the techniques employed.展开更多
Studies on the corrosion behaviour of mild steel electrodes in inhibited hydrochloric acid are described. Conventional weight loss measurements show that a maximum concentration of 140 ppm of tannin from Rhizophora ra...Studies on the corrosion behaviour of mild steel electrodes in inhibited hydrochloric acid are described. Conventional weight loss measurements show that a maximum concentration of 140 ppm of tannin from Rhizophora racemosa is required to achieve 72% corrosion inhibition. Similar concentration of tannin: H3PO4 in ratio 1:1 gave 61% inhibition efficiency, whereas efficiency obtained for phosphoric acid as inhibitor in the same environment was 55%. Corrosion rates obtained over six hours of exposure in 1M HCl solution at inhibitor concentrations of 140 ppm are 2 mA/cm2, 2.4 mA/cm2, 2.6 mA/cm2 and 6 mA/cm2 for tannin, tannin/H3PO4 and H3PO4-inhibited and uninhibited specimens respectively. Natural atmospheric exposure studies revealed that specimens treated in H3PO4 resisted corrosion for three weeks, while tannin treated specimens suffered corrosion attack after one week of exposure tests.展开更多
Effect of flow rate perturbations has been studied using the modified computer program CPAIR-P for time dependent corrosion rates in Pressurized Water Reactors (PWRs) having extended cycles. In these simulations, a de...Effect of flow rate perturbations has been studied using the modified computer program CPAIR-P for time dependent corrosion rates in Pressurized Water Reactors (PWRs) having extended cycles. In these simulations, a decrease in the corresponding saturation values of corrosion product activity (CPA) is observed for higher pH values. Comparison of CPA’s behavior has been done for constant flow-rate case as well as for transients with elevated 10B levels (~40%) in dissolved boric acid in coolant in two operating cycles. When the flow rate is decreased in the first cycle, the saturation value of CPA attains new higher values. Also, in the second operating cycle, the saturation values are about 12% higher when compared with the values in the first cycle.展开更多
文摘The effect of hydrochloric acid concentration on stainless steel (Fe6956) at temperature range 303 - 333 ± 1 K has been studied using weight loss, thermometric and electrochemical polarization techniques. The corrosion rate of the stainless steel was found to be dependent on both temperature variation and acid concentration. The potentiostatic study showed that the active passive transition depends strongly on acid concentration while the weight loss measurements revealed that 2 M HCl at temperature 333 K had an appreciable corrosion rate which corresponds to 14.04 × 10﹣3 reaction number (RN) got from thermometric monitoring. Arrhenius equation and transition state theory were used to calculate kinetic and thermodynamic parameter such as Ea, ΔH* and ΔS*. Results obtained showed that corrosion reaction of Fe6956 in HCl is spontaneous and there is good agreement between the data got from the techniques employed.
文摘Studies on the corrosion behaviour of mild steel electrodes in inhibited hydrochloric acid are described. Conventional weight loss measurements show that a maximum concentration of 140 ppm of tannin from Rhizophora racemosa is required to achieve 72% corrosion inhibition. Similar concentration of tannin: H3PO4 in ratio 1:1 gave 61% inhibition efficiency, whereas efficiency obtained for phosphoric acid as inhibitor in the same environment was 55%. Corrosion rates obtained over six hours of exposure in 1M HCl solution at inhibitor concentrations of 140 ppm are 2 mA/cm2, 2.4 mA/cm2, 2.6 mA/cm2 and 6 mA/cm2 for tannin, tannin/H3PO4 and H3PO4-inhibited and uninhibited specimens respectively. Natural atmospheric exposure studies revealed that specimens treated in H3PO4 resisted corrosion for three weeks, while tannin treated specimens suffered corrosion attack after one week of exposure tests.
文摘Effect of flow rate perturbations has been studied using the modified computer program CPAIR-P for time dependent corrosion rates in Pressurized Water Reactors (PWRs) having extended cycles. In these simulations, a decrease in the corresponding saturation values of corrosion product activity (CPA) is observed for higher pH values. Comparison of CPA’s behavior has been done for constant flow-rate case as well as for transients with elevated 10B levels (~40%) in dissolved boric acid in coolant in two operating cycles. When the flow rate is decreased in the first cycle, the saturation value of CPA attains new higher values. Also, in the second operating cycle, the saturation values are about 12% higher when compared with the values in the first cycle.
基金supported by the National Natural Science Foundation of China (Nos. 52071278, 51827801)the National Key Research and Development Program of China (No. 2018YFA0703603)。