The hydrophilic ZSM-5 zeolite membranes are applied to separate the inorganic acid solutions and inorganic acid/inorganic salt mixtures by pervaporation,and the membrane presents good stability,dehydration,and desalin...The hydrophilic ZSM-5 zeolite membranes are applied to separate the inorganic acid solutions and inorganic acid/inorganic salt mixtures by pervaporation,and the membrane presents good stability,dehydration,and desalination performance.Influences of inorganic acid type(H_(2)SO_(4),H_(3)PO_(4),HNO_(3),and HCl),H_(2)SO_(4)concentration(1-6 mol·L^(-1)),test temperature(60-90℃)and inorganic acid/inorganic salt type(2 mol·L^(-1)H_(2)SO_(4)and sulfate,2 mol·L^(-1)H3PO4 and phosphate)on the pervaporation performance are investigated in this work.Either for concentrating 3%(mass)H_(2)SO_(4)solution or consecutive dehydrating 20%(mass)H_(2)SO_(4)solution,the hydrophilic ZSM-5 zeolite membrane has a good dehydration performance and stability.Even though the H_(2)SO_(4)concentration and test temperature are increased to 6 M and 90℃,only H_(2)O molecules could pass through the membrane and pH value of the permeation is kept neutral.Besides,the membrane has good dehydration and desalination performance for H_(2)SO_(4)/sulfates and H_(3)PO_(4)/phosphate mixtures,and the rejection of natrium salt,molysite,and magnesium is almost 100%.展开更多
Template-free nanosized ZSM-5 seeds with an average size of 15 nm were prepared from a synthesis solution with the composition 12Na2O∶100SiO2∶2Al2O3∶2500H2O. By the use of these seeds, thin ZSM-5 zeolite membranes ...Template-free nanosized ZSM-5 seeds with an average size of 15 nm were prepared from a synthesis solution with the composition 12Na2O∶100SiO2∶2Al2O3∶2500H2O. By the use of these seeds, thin ZSM-5 zeolite membranes were prepared on the outer surface of a porous α-alumina tube with a pore size of 2 μm in a gel system by varying-concentration synthesis with organic-free template. The first composition synthesis sol-gel was the same as seeds of molar composition and the second one was 12Na2O∶100SiO2∶2Al2O3∶5000H2O at 180 ℃ for 10 h, respectively. XRD shows that the film consists of well-crystallized ZSM-5 zeolite. SEM investigation indicats that the zeolite films on the supports are defect free and the film thickness is approximately 8 μm. The permeances for H2, N2, CH4 and CO2 are 8.94×10-7, 3.27×10-7, 3.9×10-7, 3.14×10-7 and 0.874×10-7 mol·m2·s-1·Pa-1, respectively. The ideal selectivity of membrane at room temperature for H2/CO2, H2/N2, H2/CH4 are 2.84, 2.73 and 2.29, respectively.展开更多
基金supported by the National Natural Science Foundation of China(21868012 and 22368025)Jiangxi Provincial Department of Science and Technology(20171BCB24005 and 20202BAB203011).
文摘The hydrophilic ZSM-5 zeolite membranes are applied to separate the inorganic acid solutions and inorganic acid/inorganic salt mixtures by pervaporation,and the membrane presents good stability,dehydration,and desalination performance.Influences of inorganic acid type(H_(2)SO_(4),H_(3)PO_(4),HNO_(3),and HCl),H_(2)SO_(4)concentration(1-6 mol·L^(-1)),test temperature(60-90℃)and inorganic acid/inorganic salt type(2 mol·L^(-1)H_(2)SO_(4)and sulfate,2 mol·L^(-1)H3PO4 and phosphate)on the pervaporation performance are investigated in this work.Either for concentrating 3%(mass)H_(2)SO_(4)solution or consecutive dehydrating 20%(mass)H_(2)SO_(4)solution,the hydrophilic ZSM-5 zeolite membrane has a good dehydration performance and stability.Even though the H_(2)SO_(4)concentration and test temperature are increased to 6 M and 90℃,only H_(2)O molecules could pass through the membrane and pH value of the permeation is kept neutral.Besides,the membrane has good dehydration and desalination performance for H_(2)SO_(4)/sulfates and H_(3)PO_(4)/phosphate mixtures,and the rejection of natrium salt,molysite,and magnesium is almost 100%.
基金This work was financially supported by the Specialized Research Fund for the Doctoral Program of High Education (SRFDP)(No.B20020288015).
文摘Template-free nanosized ZSM-5 seeds with an average size of 15 nm were prepared from a synthesis solution with the composition 12Na2O∶100SiO2∶2Al2O3∶2500H2O. By the use of these seeds, thin ZSM-5 zeolite membranes were prepared on the outer surface of a porous α-alumina tube with a pore size of 2 μm in a gel system by varying-concentration synthesis with organic-free template. The first composition synthesis sol-gel was the same as seeds of molar composition and the second one was 12Na2O∶100SiO2∶2Al2O3∶5000H2O at 180 ℃ for 10 h, respectively. XRD shows that the film consists of well-crystallized ZSM-5 zeolite. SEM investigation indicats that the zeolite films on the supports are defect free and the film thickness is approximately 8 μm. The permeances for H2, N2, CH4 and CO2 are 8.94×10-7, 3.27×10-7, 3.9×10-7, 3.14×10-7 and 0.874×10-7 mol·m2·s-1·Pa-1, respectively. The ideal selectivity of membrane at room temperature for H2/CO2, H2/N2, H2/CH4 are 2.84, 2.73 and 2.29, respectively.