The seeded semicontinuous emulsion multi-copolymerization of butyl acrylate (BA), 2-ethylhexyl acrylate (2EHA), methyl methacrylate (MMA), 2-hydroxyl propyl acrylate (HOPA) and acrylic acid (AA) was used to prepare th...The seeded semicontinuous emulsion multi-copolymerization of butyl acrylate (BA), 2-ethylhexyl acrylate (2EHA), methyl methacrylate (MMA), 2-hydroxyl propyl acrylate (HOPA) and acrylic acid (AA) was used to prepare the acrylic latexes with high-solid content. The effects of monomer emulsion feed rates (R(a)) and (R/E)(E) values, the ratio of emulsifier amount between the initial charge (R) and the addition monomer emulsion (E), on the polymerization reaction features, the viscosities, surface tensions,particle sizes and particle sizes distributions of latexes, T-g and the insoluble fractions of films, the 180 degrees peel strength, tack and holding power of pressure-sensitive adhesive (PSA) tapes, prepared from the latexes, were studied. Experimental study shows that the grafting and crosslinking fraction in the PSA tapes must be controlled within a suitable range to keep the balance of the 180 degrees peel strength, tack and holding power.展开更多
基金This work was supported by the National Natural Science Foundation of China
文摘The seeded semicontinuous emulsion multi-copolymerization of butyl acrylate (BA), 2-ethylhexyl acrylate (2EHA), methyl methacrylate (MMA), 2-hydroxyl propyl acrylate (HOPA) and acrylic acid (AA) was used to prepare the acrylic latexes with high-solid content. The effects of monomer emulsion feed rates (R(a)) and (R/E)(E) values, the ratio of emulsifier amount between the initial charge (R) and the addition monomer emulsion (E), on the polymerization reaction features, the viscosities, surface tensions,particle sizes and particle sizes distributions of latexes, T-g and the insoluble fractions of films, the 180 degrees peel strength, tack and holding power of pressure-sensitive adhesive (PSA) tapes, prepared from the latexes, were studied. Experimental study shows that the grafting and crosslinking fraction in the PSA tapes must be controlled within a suitable range to keep the balance of the 180 degrees peel strength, tack and holding power.