The synthetic method of nickel borate acylate (NBA), a kind of rubber steel cord adhesion promoter (AP), through nickel carbonate, borate and mixed carboxylic acid was studied. The preparation of nickel carbonate coul...The synthetic method of nickel borate acylate (NBA), a kind of rubber steel cord adhesion promoter (AP), through nickel carbonate, borate and mixed carboxylic acid was studied. The preparation of nickel carbonate could be performed through reaction of nickel sulfate with sodium carbonate in aqueous solution, in which fractional conversion of nickel was more than 99.9%. The mixed nickel carboxylate was prepared by the reaction of nickel carbonate with isooctanoic acid and acetic acid, under strong stirring for 2 h, the mole ratio of these chemicals were 1∶1∶1.1 respectively, and water should be removed completely by adding of inert organic solvent after reaction was finished so as to avoid hydrolysis of tributyl borate in the second reaction. NBA was synthesized by reaction of mixed nickel carboxylate with tributyl borate under strong stirring at 200 250 ℃ for 6 h. By detection and comparison with 680C product from Manobond Company of England, the NBA synthesized through isooctanoic acid and tributyl borate was very similar to product 680C in IR data, 300% fixed extension strength, tensile strength, hardness and cure curve, and was slightly lower than those of product 680C in tensile failure extensibility and hot air aging. The experimental results show that the prepared NBA can be used as rubber steel cord AP.展开更多
The synthesis of nickel borate acylate (NBA), a kind of rubber steel cord adhesion promoter (AP), through nickel carbonate, borate and mixed carboxylic acid was studied. Nickel carbonate could be prepared by the react...The synthesis of nickel borate acylate (NBA), a kind of rubber steel cord adhesion promoter (AP), through nickel carbonate, borate and mixed carboxylic acid was studied. Nickel carbonate could be prepared by the reaction of nickel sulfate with sodium carbonate in aqueous solution. After strong stirring for 2?h, the mixed nickel carboxylate could be synthesized by the reaction of nickel carbonate with isooctanoic acid and acetic acid. The mole ratio of these chemicals was 1∶1∶1.1. NBA was synthesized by reaction of mixed nickel carboxylate with tributyl borate under strong stirring at 200 ～ 250?℃ for 6?h. By detecting and comparing with 680?C product from Manobond Company of England, the NBA synthesized through isooctanoic acid and tributyl borate is very similar with 680?C in IR data, 300% fixed extension strength, tensile strength, hardness and cure curve. However, tensile failure extensibility and hot air aging of NBA are a little lower than those of 680?C. The experimental results show that NBA can be used as rubber steel cord AP.展开更多
We improved the adhesion between silicon based insulating materials and epoxy resin composites by adding the adhesion promoter cycloborosiloxane(BSi,cyclo-1,3,3,5,7,7-hexaphenyl-1,5-diboro-3,7-disiloxane).The experime...We improved the adhesion between silicon based insulating materials and epoxy resin composites by adding the adhesion promoter cycloborosiloxane(BSi,cyclo-1,3,3,5,7,7-hexaphenyl-1,5-diboro-3,7-disiloxane).The experimental results show that the addition of BSi in the silicone rubber(SR)system significantly increases the tensile shear strength between BSi and epoxy resin(EP),reaching 309%of the original value.On this basis,the mechanism of BSi to enhance the adhesion effect was discussed.The electron deficient B in BSi attracted the electron rich N and O in EP to enhance the chemical interaction,combined with the interfacial migration behavior in the curing process,to improve the adhesion strength.This study provides the design and synthesis ideas of adhesive aids,and a reference for further exploring the interface mechanism of epoxy resin matrix composites.展开更多
文摘The synthetic method of nickel borate acylate (NBA), a kind of rubber steel cord adhesion promoter (AP), through nickel carbonate, borate and mixed carboxylic acid was studied. The preparation of nickel carbonate could be performed through reaction of nickel sulfate with sodium carbonate in aqueous solution, in which fractional conversion of nickel was more than 99.9%. The mixed nickel carboxylate was prepared by the reaction of nickel carbonate with isooctanoic acid and acetic acid, under strong stirring for 2 h, the mole ratio of these chemicals were 1∶1∶1.1 respectively, and water should be removed completely by adding of inert organic solvent after reaction was finished so as to avoid hydrolysis of tributyl borate in the second reaction. NBA was synthesized by reaction of mixed nickel carboxylate with tributyl borate under strong stirring at 200 250 ℃ for 6 h. By detection and comparison with 680C product from Manobond Company of England, the NBA synthesized through isooctanoic acid and tributyl borate was very similar to product 680C in IR data, 300% fixed extension strength, tensile strength, hardness and cure curve, and was slightly lower than those of product 680C in tensile failure extensibility and hot air aging. The experimental results show that the prepared NBA can be used as rubber steel cord AP.
文摘The synthesis of nickel borate acylate (NBA), a kind of rubber steel cord adhesion promoter (AP), through nickel carbonate, borate and mixed carboxylic acid was studied. Nickel carbonate could be prepared by the reaction of nickel sulfate with sodium carbonate in aqueous solution. After strong stirring for 2?h, the mixed nickel carboxylate could be synthesized by the reaction of nickel carbonate with isooctanoic acid and acetic acid. The mole ratio of these chemicals was 1∶1∶1.1. NBA was synthesized by reaction of mixed nickel carboxylate with tributyl borate under strong stirring at 200 ～ 250?℃ for 6?h. By detecting and comparing with 680?C product from Manobond Company of England, the NBA synthesized through isooctanoic acid and tributyl borate is very similar with 680?C in IR data, 300% fixed extension strength, tensile strength, hardness and cure curve. However, tensile failure extensibility and hot air aging of NBA are a little lower than those of 680?C. The experimental results show that NBA can be used as rubber steel cord AP.
基金the Core Research Facilities of College of Chemistry and Molecular Sciences and Wuhan University Test Center and Open Fund of Hubei Key Laboratory of Aerospace Power Advanced Technologythe Open Fund of Hubei Key Laboratory of Aerospace Power Advanced Technologythe Special Fund for Industrial and informatization Industry Foundation Reconstruction and High Quality Development of Manufacturing Industry(No.TC220H068)。
文摘We improved the adhesion between silicon based insulating materials and epoxy resin composites by adding the adhesion promoter cycloborosiloxane(BSi,cyclo-1,3,3,5,7,7-hexaphenyl-1,5-diboro-3,7-disiloxane).The experimental results show that the addition of BSi in the silicone rubber(SR)system significantly increases the tensile shear strength between BSi and epoxy resin(EP),reaching 309%of the original value.On this basis,the mechanism of BSi to enhance the adhesion effect was discussed.The electron deficient B in BSi attracted the electron rich N and O in EP to enhance the chemical interaction,combined with the interfacial migration behavior in the curing process,to improve the adhesion strength.This study provides the design and synthesis ideas of adhesive aids,and a reference for further exploring the interface mechanism of epoxy resin matrix composites.