The steel corrosion in concrete is widely reported over the last two to three decades. Much effort has been devoted to researching the causes and mechanisms of reinforcement corrosion and to the questions of durabilit...The steel corrosion in concrete is widely reported over the last two to three decades. Much effort has been devoted to researching the causes and mechanisms of reinforcement corrosion and to the questions of durability for concrete structures, but relatively little attention has been devoted to the problem of assessing the effect of bond loss due to corrosion on the structural behavior of corroded elements. From the test results on corroded specimens, the mechanism of degradation in bond behavior between corroded bars and concrete, and the effects of bond loss on structural performances are summarized. Results show that corrosion level, cover depth-W-bar diameter ratio, surface condition of re/nforcement, stirrups, etc. can influence the bond behavior of corroded bars. In addition, the deterioration in bond due to corrosion may induce reduction in bearing capacity, degradation of serviceability, and the loss in ductility for steel-corroded concrete members.展开更多
An anchorage reliability analysis approach for simply supported reinforced concrete beams under corrosion attack in the anchorage zone is developed.The first-order second-moment method is employed to analyze the effec...An anchorage reliability analysis approach for simply supported reinforced concrete beams under corrosion attack in the anchorage zone is developed.The first-order second-moment method is employed to analyze the effects of various factors on the anchorage reliability.These factors include both the length and width of cover cracking due to reinforcement corrosion,the cover thickness,the anchorage length,and the stirrup ratio.The results show that the effect of corrosion-induced crack length on the reliability index for anchorage,β0,is negligible when the crack on the concrete surface is just appearing,but with the crack widening,the β0 value is reduced significantly;the considerable changes in β0 result from a variation in cover depth and anchorage length;the effect of changes in the diameter or space of stirrups on the anchorage resistance is very limited,and the variation in β0 is also very low.展开更多
为研究预制混凝土结构的钢筋连接方法,设计制作了81个预制混凝土插入式预留孔灌浆钢筋锚固拉拔试件,考虑钢筋直径、混凝土强度、锚固长度等主要影响参数.连续加荷拉拔试验结果表明:灌浆锚固试件的最终破坏状态都是外部钢筋屈服或被拉断...为研究预制混凝土结构的钢筋连接方法,设计制作了81个预制混凝土插入式预留孔灌浆钢筋锚固拉拔试件,考虑钢筋直径、混凝土强度、锚固长度等主要影响参数.连续加荷拉拔试验结果表明:灌浆锚固试件的最终破坏状态都是外部钢筋屈服或被拉断,没有发生异常锚固破坏,而且在基本锚固长度基础上分别减小为0.9、0.8倍时还有较大安全储备.根据试验数据结果给出插入式预留孔灌浆钢筋的基本锚固长度为0.8 l a.展开更多
基金The Liaoning Province CommunicationDepartment Key Science Foundation (No.0101)
文摘The steel corrosion in concrete is widely reported over the last two to three decades. Much effort has been devoted to researching the causes and mechanisms of reinforcement corrosion and to the questions of durability for concrete structures, but relatively little attention has been devoted to the problem of assessing the effect of bond loss due to corrosion on the structural behavior of corroded elements. From the test results on corroded specimens, the mechanism of degradation in bond behavior between corroded bars and concrete, and the effects of bond loss on structural performances are summarized. Results show that corrosion level, cover depth-W-bar diameter ratio, surface condition of re/nforcement, stirrups, etc. can influence the bond behavior of corroded bars. In addition, the deterioration in bond due to corrosion may induce reduction in bearing capacity, degradation of serviceability, and the loss in ductility for steel-corroded concrete members.
基金The Key Science Foundation of Liaoning ProvincialCommunications Department (No.0101).
文摘An anchorage reliability analysis approach for simply supported reinforced concrete beams under corrosion attack in the anchorage zone is developed.The first-order second-moment method is employed to analyze the effects of various factors on the anchorage reliability.These factors include both the length and width of cover cracking due to reinforcement corrosion,the cover thickness,the anchorage length,and the stirrup ratio.The results show that the effect of corrosion-induced crack length on the reliability index for anchorage,β0,is negligible when the crack on the concrete surface is just appearing,but with the crack widening,the β0 value is reduced significantly;the considerable changes in β0 result from a variation in cover depth and anchorage length;the effect of changes in the diameter or space of stirrups on the anchorage resistance is very limited,and the variation in β0 is also very low.
文摘为研究预制混凝土结构的钢筋连接方法,设计制作了81个预制混凝土插入式预留孔灌浆钢筋锚固拉拔试件,考虑钢筋直径、混凝土强度、锚固长度等主要影响参数.连续加荷拉拔试验结果表明:灌浆锚固试件的最终破坏状态都是外部钢筋屈服或被拉断,没有发生异常锚固破坏,而且在基本锚固长度基础上分别减小为0.9、0.8倍时还有较大安全储备.根据试验数据结果给出插入式预留孔灌浆钢筋的基本锚固长度为0.8 l a.