In situ adsorption-catalysis system for the removal of o-xylene over an activated carbon supported Pd catalyst

An activated carbon （AC） supported Pd catalyst was used to develop a highly efficient in situ adsorption-catalysis system for the removal of low concentrations of o-xylene. In this study, three kinds of Pd/AC catalysts were prepared and tested to investigate the synergistic efficiency between adsorption and catalysis for o-xylene removal. The Pd/AC catalyst was first used as an adsorbent to concentrate dilute o-xylene at low temperature. After saturated adsorption, the adsorbed o-xylene was oxidized to CO2 and H20 by raising the temperature of the catalyst bed. The results showed that more than 99% of the adsorbed o-xylene was completely oxidized to CO2 over a 5% Pd/AC catalyst at 140℃. Brunauer-Emmett-Teller （BET） analysis, scanning electron microscopy （SEM）, temperatureprogrammed desorption （TPD）, and temperature-programmed oxidation （TPO） were applied to investigate the physical properties of o-xylene adsorption-desorption and the in situ adsorption-catalysis activity of the AC support and Pd/AC catalyst. A synergistic relationship between the AC support and the active Pd species for the removal of low concentrations of o-xylene was established.

Recyclable cobalt-molybdenum bimetallic carbide modified separator boosts the polysulfide adsorption-catalysis of lithium sulfur battery

The polysulfide shuttling and sluggish redox kinetics,due to the notorious adsorption-catalysis underperformance,are the ultimate obstacles of the practical application of lithium-sulfur(Li-S)batteries.Conventional carbon-based and transition metal compound-based material solutions generally suffer from poor catalysis and adsorption,respectively,despite the performance gain in terms of the other.Herein,we have enhanced polysulfide adsorptioncatalytic capability and protected the Li anode using a complementary bimetallic carbide electrocatalyst,Co3 Mo3 C,modified commercial separator.With this demonstration,the potentials of bimetal compounds,which have been well recognized in other environmental catalysis,are also extended to Li-S batteries.Coupled with this modified separator,a simple cathode(S/Super P composite)can deliver high sulfur utilization,high rate performance,and excellent cycle stability with a low capacity decay rate of^0.034%per cycle at 1 C up to1000 cycles.Even at a high S-loading of 8.0 mg cm^-2 with electrolyte/sulfur ratio=6 m L g^-1,the cathode still exhibits high areal capacity of^6.8 m A h cm^-2.The experimental analysis and the first-principles calculations proved that the bimetallic carbide Co3 Mo3 C provides more binding sites for adsorbing polysulfides and catalyzing the multiphase conversion of sulfur/polysulfide/sulfide than monometallic carbide Mo2 C.Moreover,the modified separator can be reutilized with comparable electrochemical performance.We also showed other bimetallic carbides with similar catalytic effects on Li-S batteries and this material family has great promise indifferent energy electrocatalytic systems.