The characteristics of surface appearances,mass loss,relative dynamic modulus of elasticity and strength loss of different recycled aggregate concretes(RAC) exposed to freeze-thaw cycles were analyzed.It was found tha...The characteristics of surface appearances,mass loss,relative dynamic modulus of elasticity and strength loss of different recycled aggregate concretes(RAC) exposed to freeze-thaw cycles were analyzed.It was found that the freeze-thaw resistance of RAC could be determined by the recycled aggregate compositions and admixtures.Both the saturation degree and the air void structure were the key factors influencing the freeze-thaw damage on concrete.Some major proposed freeze-thaw deterioration mechanisms were utilized to interpret the freeze-thaw damage on recycled aggregate concrete.Meanwhile,some potential measures to enhance the freeze-thaw resistance of concrete were summarized and discussed.展开更多
基金Funded by the National Key Research and Development Program of China during the“13th Five-Year Plan”(No.2018 YFD1101001)。
文摘The characteristics of surface appearances,mass loss,relative dynamic modulus of elasticity and strength loss of different recycled aggregate concretes(RAC) exposed to freeze-thaw cycles were analyzed.It was found that the freeze-thaw resistance of RAC could be determined by the recycled aggregate compositions and admixtures.Both the saturation degree and the air void structure were the key factors influencing the freeze-thaw damage on concrete.Some major proposed freeze-thaw deterioration mechanisms were utilized to interpret the freeze-thaw damage on recycled aggregate concrete.Meanwhile,some potential measures to enhance the freeze-thaw resistance of concrete were summarized and discussed.