The aggregation characteristics and formation mechanism of nanoparticles in ductile shear zone

1 Introduction Nanoparticles are widely found in the ductile shear zone and it is considered to have a close relation with faulting.The sizes of these nanoparticles are generallyless than 100 nm.They have a variety of morphologies like globular structure rod-like and tubular,by the order aggregating of these nanoparticles various aggregations

Mechanical Properties and ITZ Microstructure of Recycled Aggregate Concrete Using Carbonated Recycled Coarse Aggregate

The effect of carbonation treatment and mixing method on the mechanical properties and interfacial transition zone（ITZ） properties of recycled aggregate concrete（RAC） was investigated. Properties of recycled concrete aggregate（RCA） were tested firstly. Then, five types of concretes were made and slump of fresh concrete was measured immediately after mixing. Compressive strength and splitting tensile strength of hardened concrete were measured at 28 d. Meanwhile, the microstructure of RAC was analyzed by backscattered electron（BSE） image. It was found that the water absorption ratio of carbonated recycled concrete aggregate（CRCA） was much lower when compared to the untreated RCA. Comparatively, the apparent density of CRCA was not significantly modified. The concrete strength results indicate that the mix CRAC-2 prepared with CRCA by adopting two-stage mixing approach shows the highest compressive strength value compared to the other mixes. The microstructural analysis demonstrate that the mix CRAC-2 has a much denser old ITZ than the untreated RAC because of the chemical reaction between CO2 and the hydration products of RCA. This study confirms that the ITZ microstructure of RAC can be efficiently modified by carbonation treatment of RCA and encourages broadening the application of construction and demolition wastes.

Properties and Microstructures of Full Graded Concrete Containing Varied Impurity Aggregate

We investigated mechanical properties of concretes made with impurity aggregates of different combinations. Besides the mechanisms were explored by EDS, CT, and hardness testing. The results showed that fully rust-stained and surface rust-stained sandstone aggregate had significant adverse impact on the compressive strength of concrete while sandstone aggregate had a much more obvious impact on the ultimate tension of concrete. Concrete crack was more prone to expand along surfaces and the micro-hardness of interfacial transition zone of different aggregates was ranked in decreasing trend as sandstone, slate, SR sandstone, marble, and FR sandstone. The cluster growth of long needle-like ettringite crystal and strong preferential growth trend of Ca（OH）2 crystals would result in wider interfacial transition zone range of concretes made with fully rust-stained sandstone and marble aggregate, respectively. Therefore, the impurity aggregate content should be strictly controlled during aggregate selection.