Doping Effect of Co at Ag Sites in Antiperovskite Mn3AgN Compounds

Antiperovskite compounds Mn3Ag1-xCoxN （x =0.2, 0.5 and 0.8） are synthesized and the doping effect of the magnetic element Co at the Ag site is investigated. The crystal structure is not changed by the introduction of Co. However, with the increase of the content of Co, the spin reorientation gradually disappears and the antiferromagnetic transition changes to the ferromagnetic transition at the elevated temperature when x = 0.8. In addition, all of the magnetic phase transitions at the elevated temperature are always accompanied by the abnormal thermal expansion behaviors and an entropy change. Moreover, when x = 0.8, the coefficient of linear expansion is -1.89 × 10^-6 K^-1 （290-310K, △T =20 K）, which is generally considered as the low thermal expansion.

Properties analysis of a new type of solder paste SACBN07

In this work, the wettability, aging and shear properties of a new type of lead-free solder paste Sn-01Ag-Q5Cu ＋ BiNi （SACBNQ7） was investigated by conducting a series of comparison experiments with SAC305 and SAC0307 solder paste. The results show that wettability of SACBNQ1 is almost equal to SAC3Q5,and better than that of SACQ3Q1 solder paste. The thickness of intermetallic compound （IMC） layer in SACBNQl/Cu is lower than that o f other two types o f solder joint after aging. And Cu3Sn layer of SACBNQl/Cu is thinner than that of SAC3Q5 and SAC0307. In addition, the SACBNQ7 solder joints perform the best shear strength among these three types of solder pastes.

Synthesis,Crystal Structure and Luminescent Properties of a 1D Loop-chain Coordination Polymer [Ag(3,3-pybz)(3,3-Hpybz)]_n

A new coordination polymer, [Ag（3,3-pybz）（3,3-Hpybz）]n （1, 3,3-Hpybz = 3-pyri- din-3-yl-benzoic acid）, has been synthesized and characterized by elemental analysis, IR spectra, PXRD, and single-crystal X-ray diffraction. In complex 1, the Ag（1）ions are linked by the paired 3,3-pybz ligands to generate an infinite 1D loop chain, and further through π-π stacking interactions to form a 2D supramolecular architecture. Crystal data for 1： triclinic, space group P1, a = 10.2635（17）, b = 10.3041（12）, c = 10.8060（13） A, V= 1679.1（5）A3, α = 62.028（11）, β = 80.325（15）, γ = 78.738（14）°, Z = 2, C24H17AgN2O4, Mr = 505.27, Dc= 1.698 g/cm3, μ= 1.058 mm--, F（000） = 506, S = 1.012 and T = 293（2） K. The final R = 0.0293 and wR = 0.0667 for 3435 observed reflections with I〉 2a（/）, and R = 0.0350 and wR = 0.0688 for all data.

Synthesis,Crystal Structure and Photoluminescence Property of Ag(I)with N,N-dimethyl-4-(pyridine-4-yldiazenyl)aniline

A 2D plane coordination compound [Ag_2（Dpya）_2.（NO_3）_2]n was synthesized and characterized by FT-IR,elemental analysis and TG analysis.The red crystal was obtained via solvent diffusion method at room temperature and is slightly soluble in organic solvents.Its structure was determined by single-crystal X-ray diffraction analysis.It crystallizes in monoclinic,space group P1 with a = 10.7995（13）,b = 7.4748（8）,c = 18.364（2） A,β = 98.916（4）o,V = 1464.5（3） A^3,Z = 2,C_（26）H_（28）Ag_2N_（10）O_6,M_r = 792.32,Dc = 1.302 Mg/m^3,F（000） = 792,μ（Mo Ka） = 1.356 mm^-1,R = 0.0575 and w R = 0.0826.The compound [Ag_2（Dpya）_2.（NO_3）_2]_n is a two-dimensional structure and there are two kinds of coordination configurations about the Ag atoms in the compound.The Ag（1） center is tetrahedrally coordinated with two O atoms of NO_3^-and two N atoms from the ligand Dpya.Meanwhile,the Ag（2） is five-coordinated by five O atoms from three NO_3^-anions.The Ag centers（Ag（1） and Ag（2）） connect to themselves as well as with each other by the bridging NO_3^-anions.And the coordination compound shows photoluminescence with an emission peak at 530 nm（λex = 450 nm） as the ligand Dpya.