The effect of thermal cycling and aging in martensitic state in Ti-Pd-Ni alloys were investigated by DSC and TEM observations. It is shown that the thermal cycling causes the decreases in M, and Af temperatures in Ti5...The effect of thermal cycling and aging in martensitic state in Ti-Pd-Ni alloys were investigated by DSC and TEM observations. It is shown that the thermal cycling causes the decreases in M, and Af temperatures in Ti50Pd50-xNix (x=10, 20, 30) alloys, but no obvious thermal cycling effect was observed in Ti50Pd50Pd40Ni10 alloys and the aging effect shows a curious feature, i.e., the Af temperature does not saturate even after relatively long time aging, which is considered to be due to the occurrence of recovery recrystallization during aging.展开更多
The effects of thickness and types of gold plating on the resistance to hightemperature discoloration of gold plating on cavity surface of ceramic package were investigated. Itwas found that the thicker gold plating, ...The effects of thickness and types of gold plating on the resistance to hightemperature discoloration of gold plating on cavity surface of ceramic package were investigated. Itwas found that the thicker gold plating, the less discoloration degree for ceramic packages.Non-cyanide gold plating performed better resistance to high-temperature aging than cyanide goldplating. The relationship between the gold plating thickness and the amount of diffused Ni to thegold plating of ceramic packages with Au/Ni and Au/Ni-Co platings after heating at 420℃ for 15 minwas also studied. When the gold plating thickness reach 2.0 μm and 1.6 μm for Au/Ni and Au/Ni-Coplating systems, respectively, no discoloration was observed on the gold plating surface of cavity,and the corresponding diffused Ni amounts (mass fraction) are 1.0% and 0.4%, while the diffused Coto the gold plating is 0.04%.展开更多
The effects of thickness and types of gold plating on the resistance to high temperature discoloration of gold plating on cavity surface of ceramic package were investigated. It was found that the thicker gold plating...The effects of thickness and types of gold plating on the resistance to high temperature discoloration of gold plating on cavity surface of ceramic package were investigated. It was found that the thicker gold plating, the less discoloration degree for ceramic packages. Non-cyanide gold plating performed better resistance to high-temperature aging than cyanide gold plating. The relationship between the gold plating thickness and the amount of diffused Ni to the gold plating of ceramic packages with Au/Ni and Au/Ni-Co platings after heating at 420℃for 15 min was also studied. When the gold plating thickness reach 2.0 μm and 1.6 μm for Au/Ni and Au/Ni-Co plating systems, respectively, no discoloration was observed on the gold plating surface of cavity, and the corresponding diffused Ni amounts (mass fraction) are 1.0% and 0.4%, while the diffused Co to the gold plating is 0.04%.展开更多
基金This work was supported by a Grant-in-Aid fOrEncouragement of Young Scientists (W.C.) (l998-1999) from the Ministry of Educat
文摘The effect of thermal cycling and aging in martensitic state in Ti-Pd-Ni alloys were investigated by DSC and TEM observations. It is shown that the thermal cycling causes the decreases in M, and Af temperatures in Ti50Pd50-xNix (x=10, 20, 30) alloys, but no obvious thermal cycling effect was observed in Ti50Pd50Pd40Ni10 alloys and the aging effect shows a curious feature, i.e., the Af temperature does not saturate even after relatively long time aging, which is considered to be due to the occurrence of recovery recrystallization during aging.
文摘The effects of thickness and types of gold plating on the resistance to hightemperature discoloration of gold plating on cavity surface of ceramic package were investigated. Itwas found that the thicker gold plating, the less discoloration degree for ceramic packages.Non-cyanide gold plating performed better resistance to high-temperature aging than cyanide goldplating. The relationship between the gold plating thickness and the amount of diffused Ni to thegold plating of ceramic packages with Au/Ni and Au/Ni-Co platings after heating at 420℃ for 15 minwas also studied. When the gold plating thickness reach 2.0 μm and 1.6 μm for Au/Ni and Au/Ni-Coplating systems, respectively, no discoloration was observed on the gold plating surface of cavity,and the corresponding diffused Ni amounts (mass fraction) are 1.0% and 0.4%, while the diffused Coto the gold plating is 0.04%.
文摘The effects of thickness and types of gold plating on the resistance to high temperature discoloration of gold plating on cavity surface of ceramic package were investigated. It was found that the thicker gold plating, the less discoloration degree for ceramic packages. Non-cyanide gold plating performed better resistance to high-temperature aging than cyanide gold plating. The relationship between the gold plating thickness and the amount of diffused Ni to the gold plating of ceramic packages with Au/Ni and Au/Ni-Co platings after heating at 420℃for 15 min was also studied. When the gold plating thickness reach 2.0 μm and 1.6 μm for Au/Ni and Au/Ni-Co plating systems, respectively, no discoloration was observed on the gold plating surface of cavity, and the corresponding diffused Ni amounts (mass fraction) are 1.0% and 0.4%, while the diffused Co to the gold plating is 0.04%.