In order to improve the mechanical properties of SiO_2 aerogel-glass fiber composites, effects of different solvents(cyclohexane, n-hexane, ethanol, acetone) and different dispersing modes(planetary ball milling, ultr...In order to improve the mechanical properties of SiO_2 aerogel-glass fiber composites, effects of different solvents(cyclohexane, n-hexane, ethanol, acetone) and different dispersing modes(planetary ball milling, ultrasonic dispersion and mechanical stirring) and dispersing duration(10-40 min) on the dispersion of chopped alkali-free glass fiber bundles were studied to determine the best dispersion process. On this basis, the materials were batched according to the mass fraction of SiO_2 aerogel powder to chopped alkali free glass fiber bundles of 90:10, and a certain amount of zinc oxide light-screening agent and phenolic resin binder were added. SiO_2 aerogel glass fiber composite specimens were prepared by direct adding chopped alkali free glass fiber bundles and pre-dispersed chopped alkali free glass fiber bundles, respectively. The cold crushing strength and the thermal conductivity at different surface temperatures(300, 400, 500 and 600 ℃, respectively)of the specimens were measured. The results show that:(1) the optimum dispersion process of chopped alkali-free glass fiber bundles is using ethanol as solvent and mechanical stirring for 30 min;(2) pre-dispersion of chopped alkali-free glass fiber bundles has little effect on the thermal conductivity of SiO_2 aerogel-glass fiber composites but can improve the cold crushing strength.展开更多
Replacing heavy oil with petrol coke can greatly reduce the cost of glass production,but obviously shorten the service life of refractories used in the regenerator checker body of glass tanks.To prolong the service li...Replacing heavy oil with petrol coke can greatly reduce the cost of glass production,but obviously shorten the service life of refractories used in the regenerator checker body of glass tanks.To prolong the service life of the regenerator checker body,the slag chemical composition and alkali-sulfur ratio of glass tanks after using petrol coke and the damage mechanism of the residual magnesia bricks in the regenerator checker body were studied,as well as the corrosion resistance of three magnesia based bricks(direct bonded magnesia chrome bricks,fused rebonded magnesia chrome bricks,and fused rebonded high-purity magnesium aluminate spinel bricks).On this basis,a series of targeted countermeasures were adopted to optimize the configuration of refractories,significantly improving the service life of checker bricks and meeting the requirements of glass industry development.展开更多
基金financial supports from the National Key R&D Program of China (2016YFB0601301 and 2018YFB0605904)The National Natural Science Foundation of China (51672256)Henan Science and Technology Research Program (162102210343)
文摘In order to improve the mechanical properties of SiO_2 aerogel-glass fiber composites, effects of different solvents(cyclohexane, n-hexane, ethanol, acetone) and different dispersing modes(planetary ball milling, ultrasonic dispersion and mechanical stirring) and dispersing duration(10-40 min) on the dispersion of chopped alkali-free glass fiber bundles were studied to determine the best dispersion process. On this basis, the materials were batched according to the mass fraction of SiO_2 aerogel powder to chopped alkali free glass fiber bundles of 90:10, and a certain amount of zinc oxide light-screening agent and phenolic resin binder were added. SiO_2 aerogel glass fiber composite specimens were prepared by direct adding chopped alkali free glass fiber bundles and pre-dispersed chopped alkali free glass fiber bundles, respectively. The cold crushing strength and the thermal conductivity at different surface temperatures(300, 400, 500 and 600 ℃, respectively)of the specimens were measured. The results show that:(1) the optimum dispersion process of chopped alkali-free glass fiber bundles is using ethanol as solvent and mechanical stirring for 30 min;(2) pre-dispersion of chopped alkali-free glass fiber bundles has little effect on the thermal conductivity of SiO_2 aerogel-glass fiber composites but can improve the cold crushing strength.
文摘Replacing heavy oil with petrol coke can greatly reduce the cost of glass production,but obviously shorten the service life of refractories used in the regenerator checker body of glass tanks.To prolong the service life of the regenerator checker body,the slag chemical composition and alkali-sulfur ratio of glass tanks after using petrol coke and the damage mechanism of the residual magnesia bricks in the regenerator checker body were studied,as well as the corrosion resistance of three magnesia based bricks(direct bonded magnesia chrome bricks,fused rebonded magnesia chrome bricks,and fused rebonded high-purity magnesium aluminate spinel bricks).On this basis,a series of targeted countermeasures were adopted to optimize the configuration of refractories,significantly improving the service life of checker bricks and meeting the requirements of glass industry development.