Al2O3 - SiC - C castables with 2% pitch or 2%, 4% and 6% treated graphite, respectively, were prepared based on the basic formulation of traditional Al2O3 - SiC - C castables. The flowability of castables, and bulk d...Al2O3 - SiC - C castables with 2% pitch or 2%, 4% and 6% treated graphite, respectively, were prepared based on the basic formulation of traditional Al2O3 - SiC - C castables. The flowability of castables, and bulk density, volume stability, strength, oxidation resistance and slag resistance of specimens fired at 110 ℃, 1 100 ℃, and 1 500 9Z respectively were comparatively studied. The results showed that： （1） With carbon source changing from pitch to treated graphite and the increase of treated graphite addition, water addition of castables increased, bulk density of specimens fired at different temperatures increased firstly and then decreased, strength after drying decreased obviously, strength after firing and oxidation resistance changed slightly, hot modulus of rupture increased obviously; （2） Slag resistance of specimen with treated graphite was worse than that of specimen with the same amount of pitch, but the former was obviously improved with the increase of treated graphite addition.展开更多
Al2O3 - SiC - C castables with pelletized graphite addition of 0. 2%, 4% or 6% （by mass, the same hereinafter ） were prepared using brown fused corundum （8 - 5, 5 - 3 and 3 - 1 mm ） , dense fused corundum （ ≤1 a...Al2O3 - SiC - C castables with pelletized graphite addition of 0. 2%, 4% or 6% （by mass, the same hereinafter ） were prepared using brown fused corundum （8 - 5, 5 - 3 and 3 - 1 mm ） , dense fused corundum （ ≤1 and 0. 045 mm） and SiC （ ≤1 and ≤0. 064 mm） its main starting materials with mass ratio of aggregate： matrix = 71： 29, 2% silicon powder and 0. 4% B4C as antioxidants, and pelletized graphite as carbon source, Effect of pelletized graphite addition on physical properties, oxidation resistance, slag resistance arid thermal shock resistance of Al2O3 -SiC- C eastables was researched. The results show that： with the in.crease of pelletized graphite addition, the required water amount of castables increases, the bulk density and strength reduce; with 4% pelletized graphite, the eastable performs the best oxidation resistance; the increase of graphite is beneficial to the improvement of slag penetration resistance and corrosion resistance; with 6% pelletized graphite, the thermal shock resistance is the best.展开更多
Three different kinds of corundum aggregates-tabular sintered alumina, dense sintered alumina, and fused dense corundum-were introduced into the silica fume .free or silica fume containing Al2O3 -SiC - C iron runner c...Three different kinds of corundum aggregates-tabular sintered alumina, dense sintered alumina, and fused dense corundum-were introduced into the silica fume .free or silica fume containing Al2O3 -SiC - C iron runner castables to investigate their influences on the flow ability, linear change on heating, bulk density, apparent porosity, cold strength, hot modulus of rupture, therm, al shock resistance, slag resistance, oxidation resistance as well as wear resistance of Al2O3 - SiC - C iron runner castables. The results show that （ 1 ） compared with the specimens with fused dense corundum, the specimens with dense sintered alumina have equivalent installation property, slag resistance and oxidation resistance, equivalent or even higher cold modulus of rupture, cold crushing strength and hot modulus of rupture, exhibiting better thermal shock resistance and cold wear resistance ; （2） adopting bimodal alumina micropowder LISAL22RABL as well as water reducers ZX2 and ZD2 can well reduce the water requirement of silica fume free castables, solving the problem of deteriorated flow ability resulted from the lack of silica fume; since the lack of silica fume avoids the formation of low melting point liquid, the hot modulus of rupture and the thermal shock resistance of the silica fume free castables are both better than those of the silica fume containing castables ; （3） the density of the castable specimens with dense sintered alumina is 4% -6% lower than that of the castable specimens with Jhsed dense corundum so the refractories consumption of one iron runner reduces by 5% by using the tastable with dense sintered alumina, which obviously reduces the cost of refractories.展开更多
The Al2O3 -SiC-C bricks for iron ladles were pre-pared asing bauxite, fused corundum,pyrophyllite, SiC powder and flake graphite as main starting materials, and phenolic resin as binder. The effect of pyroph,yllite pa...The Al2O3 -SiC-C bricks for iron ladles were pre-pared asing bauxite, fused corundum,pyrophyllite, SiC powder and flake graphite as main starting materials, and phenolic resin as binder. The effect of pyroph,yllite particle size on permanent change in dimensions, cold crushing strength, oxidation resistance, and corrosion resistance of Al2O3 - SiC - C bricks was investigated. The results show that with the decrease of the pyrophyllite particle size, the permanent change in dimensions of Al2O3 - SiC - C bricks decreases, cold crushing strength increases, the oxidation resistance at 1400 ℃ increases, and the corrosion resistance at 1500℃ decreases.展开更多
Simple three-point bending test at ambient tempera- ture characterized the mechanical behavior of burned Al2O3 -C refractories before and after thermal shock in association with the processing parameters （graphite co...Simple three-point bending test at ambient tempera- ture characterized the mechanical behavior of burned Al2O3 -C refractories before and after thermal shock in association with the processing parameters （graphite content and coking temperature, etc. ）. The results showed that non-linear plastic-elastic behavior under load lower than cold modulus of rupture （CMOR） was registered in all specimens and real linear elastic behavior could be identified after the first load, The total deformation could be divided into two parts, plastic and elastic areas. The graphite content and joint bonding system of carbon and ceramic phases were responsible for mechanical behavior of Al2O3 - C refractories.展开更多
文摘Al2O3 - SiC - C castables with 2% pitch or 2%, 4% and 6% treated graphite, respectively, were prepared based on the basic formulation of traditional Al2O3 - SiC - C castables. The flowability of castables, and bulk density, volume stability, strength, oxidation resistance and slag resistance of specimens fired at 110 ℃, 1 100 ℃, and 1 500 9Z respectively were comparatively studied. The results showed that： （1） With carbon source changing from pitch to treated graphite and the increase of treated graphite addition, water addition of castables increased, bulk density of specimens fired at different temperatures increased firstly and then decreased, strength after drying decreased obviously, strength after firing and oxidation resistance changed slightly, hot modulus of rupture increased obviously; （2） Slag resistance of specimen with treated graphite was worse than that of specimen with the same amount of pitch, but the former was obviously improved with the increase of treated graphite addition.
文摘Al2O3 - SiC - C castables with pelletized graphite addition of 0. 2%, 4% or 6% （by mass, the same hereinafter ） were prepared using brown fused corundum （8 - 5, 5 - 3 and 3 - 1 mm ） , dense fused corundum （ ≤1 and 0. 045 mm） and SiC （ ≤1 and ≤0. 064 mm） its main starting materials with mass ratio of aggregate： matrix = 71： 29, 2% silicon powder and 0. 4% B4C as antioxidants, and pelletized graphite as carbon source, Effect of pelletized graphite addition on physical properties, oxidation resistance, slag resistance arid thermal shock resistance of Al2O3 -SiC- C eastables was researched. The results show that： with the in.crease of pelletized graphite addition, the required water amount of castables increases, the bulk density and strength reduce; with 4% pelletized graphite, the eastable performs the best oxidation resistance; the increase of graphite is beneficial to the improvement of slag penetration resistance and corrosion resistance; with 6% pelletized graphite, the thermal shock resistance is the best.
文摘Three different kinds of corundum aggregates-tabular sintered alumina, dense sintered alumina, and fused dense corundum-were introduced into the silica fume .free or silica fume containing Al2O3 -SiC - C iron runner castables to investigate their influences on the flow ability, linear change on heating, bulk density, apparent porosity, cold strength, hot modulus of rupture, therm, al shock resistance, slag resistance, oxidation resistance as well as wear resistance of Al2O3 - SiC - C iron runner castables. The results show that （ 1 ） compared with the specimens with fused dense corundum, the specimens with dense sintered alumina have equivalent installation property, slag resistance and oxidation resistance, equivalent or even higher cold modulus of rupture, cold crushing strength and hot modulus of rupture, exhibiting better thermal shock resistance and cold wear resistance ; （2） adopting bimodal alumina micropowder LISAL22RABL as well as water reducers ZX2 and ZD2 can well reduce the water requirement of silica fume free castables, solving the problem of deteriorated flow ability resulted from the lack of silica fume; since the lack of silica fume avoids the formation of low melting point liquid, the hot modulus of rupture and the thermal shock resistance of the silica fume free castables are both better than those of the silica fume containing castables ; （3） the density of the castable specimens with dense sintered alumina is 4% -6% lower than that of the castable specimens with Jhsed dense corundum so the refractories consumption of one iron runner reduces by 5% by using the tastable with dense sintered alumina, which obviously reduces the cost of refractories.
文摘The Al2O3 -SiC-C bricks for iron ladles were pre-pared asing bauxite, fused corundum,pyrophyllite, SiC powder and flake graphite as main starting materials, and phenolic resin as binder. The effect of pyroph,yllite particle size on permanent change in dimensions, cold crushing strength, oxidation resistance, and corrosion resistance of Al2O3 - SiC - C bricks was investigated. The results show that with the decrease of the pyrophyllite particle size, the permanent change in dimensions of Al2O3 - SiC - C bricks decreases, cold crushing strength increases, the oxidation resistance at 1400 ℃ increases, and the corrosion resistance at 1500℃ decreases.
文摘Simple three-point bending test at ambient tempera- ture characterized the mechanical behavior of burned Al2O3 -C refractories before and after thermal shock in association with the processing parameters （graphite content and coking temperature, etc. ）. The results showed that non-linear plastic-elastic behavior under load lower than cold modulus of rupture （CMOR） was registered in all specimens and real linear elastic behavior could be identified after the first load, The total deformation could be divided into two parts, plastic and elastic areas. The graphite content and joint bonding system of carbon and ceramic phases were responsible for mechanical behavior of Al2O3 - C refractories.