In order to remove or reduce the negative effect of MgO in calcium aluminate slags, the method of adding Na2O into calcium aluminate slags was studied and its effect on leaching mechanism was also analyzed. The result...In order to remove or reduce the negative effect of MgO in calcium aluminate slags, the method of adding Na2O into calcium aluminate slags was studied and its effect on leaching mechanism was also analyzed. The results show that the alumina leaching efficiency of the calcium aluminate slag increases from 68.73% to 80.86% with Na2O content increasing from 0 to 4% when MgO content is 3%. The XRD results show that the quaternary compound C20A13M3S3 disappears when Na2O content increases to 4%. The addition of Na2O cannot remove the negative effect of MgO on leachability completely. XRD and EDS results indicate that Na2O can come into the lattice of 12CaO·7Al2O3 and promote the formation of 12CaO·7Al2O3展开更多
An approach was developed to upgrade the bauxite ore by molecular hydrogen and hydrogen plasma. A gibbsite-type bauxite sample was obtained from National Aluminium Company（NALCO）, Odisha, India. The obtained sample ...An approach was developed to upgrade the bauxite ore by molecular hydrogen and hydrogen plasma. A gibbsite-type bauxite sample was obtained from National Aluminium Company（NALCO）, Odisha, India. The obtained sample was crushed and sieved（to 100 μm） prior to the chemical analysis and grain-size distribution study. The bauxite sample was calcined in the temperature range from 500 to 700°C for different time intervals to optimize the conditions for maximum moisture removal. This process was followed by the reduction of the calcined ore by molecular hydrogen and hydrogen plasma. Extraction of alumina from the reduced ore was carried out via acid leaching in chloride media for 2 h at 60°C. X-ray diffraction, scanning electron microscopy, thermogravimetry in conjunction with differential scanning calorimetry, and Fourier transform infrared spectroscopy were used to determine the physicochemical characteristics of the material before and after extraction. Alumina extracted from the reduced ore at the optimum calcination temperature of 700°C and the optimum calcination time of 4 h is found to be 90% pure.展开更多
基金Project (51104053) supported by the National Natural Science Foundation of ChinaProject (XL200921) supported by the Foundation Research funds for Hebei University of Science and Technology, China
文摘In order to remove or reduce the negative effect of MgO in calcium aluminate slags, the method of adding Na2O into calcium aluminate slags was studied and its effect on leaching mechanism was also analyzed. The results show that the alumina leaching efficiency of the calcium aluminate slag increases from 68.73% to 80.86% with Na2O content increasing from 0 to 4% when MgO content is 3%. The XRD results show that the quaternary compound C20A13M3S3 disappears when Na2O content increases to 4%. The addition of Na2O cannot remove the negative effect of MgO on leachability completely. XRD and EDS results indicate that Na2O can come into the lattice of 12CaO·7Al2O3 and promote the formation of 12CaO·7Al2O3
基金National Aluminium Company (NALCO) for financial support
文摘An approach was developed to upgrade the bauxite ore by molecular hydrogen and hydrogen plasma. A gibbsite-type bauxite sample was obtained from National Aluminium Company（NALCO）, Odisha, India. The obtained sample was crushed and sieved（to 100 μm） prior to the chemical analysis and grain-size distribution study. The bauxite sample was calcined in the temperature range from 500 to 700°C for different time intervals to optimize the conditions for maximum moisture removal. This process was followed by the reduction of the calcined ore by molecular hydrogen and hydrogen plasma. Extraction of alumina from the reduced ore was carried out via acid leaching in chloride media for 2 h at 60°C. X-ray diffraction, scanning electron microscopy, thermogravimetry in conjunction with differential scanning calorimetry, and Fourier transform infrared spectroscopy were used to determine the physicochemical characteristics of the material before and after extraction. Alumina extracted from the reduced ore at the optimum calcination temperature of 700°C and the optimum calcination time of 4 h is found to be 90% pure.