Influence of thermal history on conversion of aluminate species in sodium aluminate solution

It is necessary to clarify the influence of thermal history on the conversion of aluminate species in sodium aluminate solution in order to optimize Bayer alumina production. The interconversion of various solution species in the systems was investigated by measuring the infrared spectra of sodium aluminate solution with different compositions after separate heat treatment, dilution and concentration. The results show that increasing temperature or prolonging holding time favors the transformation of Al2O（OH）2- to Al—OH vibration（condensed Al O4 tetrahedral aluminate ion） at about 880 cm-1 and Al（OH）-4. A12O（OH）2-66 and Al—OH tetrahedral dimer ions convert rapidly to Al（OH）-4 during the dilution process; however, the back transformation of Al（OH）-4 to the Al—OH tetrahedral dimer ions can occur in diluted sodium aluminate solution. As for the concentration process, the transformation of Al（OH）-4 to A12O（OH）2-6 and Al—OH tetrahedral dimer ions can take place, while it is relatively difficult to transform to A12O（OH）2-6.

Hot Corrosion Behavior of a Cr-Modified Aluminide Coating on a Ni-Based Superalloy

A Cr-modified aluminide coating is prepared on a Ni-based superalloy using arc ion plating and subsequent pack cementation aluminizing.Hot corrosion behavior of the Cr-modified aluminide coating exposed to molten Na2SO4/K2SO4（3：1） or Na2SO4/NaCl（3：1） salts at 900 °C in static air are evaluated as well as the aluminide coating.The results indicate that compared with the aluminide coating,the anti-corrosion properties of the Cr-modified aluminide coating in the both salts are improved,which should be attributed to the beneficial effect of the Cr in the coating.The corrosion mechanism of the Cr-modified aluminide coating,especially the role of Cr in the mixture salt corrosion,is discussed.