This paper reports high temperature liquid phase synthesis of Pd nanowires using chemically modified porous anodic aluminium oxide as template. In this synthesis process, oleic acid is used to modify the inner wall of...This paper reports high temperature liquid phase synthesis of Pd nanowires using chemically modified porous anodic aluminium oxide as template. In this synthesis process, oleic acid is used to modify the inner wall of the pores and Pd^2+ complex with oleylamine is filled into the channel of the template. The complex is then reduced to give oleylamine-capped Pd nanowires. This paper suggests that oleic acid can improve the environment of inner wall of the pores, leading to the formation of uniform Pd nanowires. The synthetic process can be extended to make other types of nanowires.展开更多
This study investigated the deterioration of a lubricant-infused anodic aluminium oxide surface in a 1M NaCl solution for~200 days.Direct observation by cryo-SEM and quantitative analyses by UV spectroscopy and EIS re...This study investigated the deterioration of a lubricant-infused anodic aluminium oxide surface in a 1M NaCl solution for~200 days.Direct observation by cryo-SEM and quantitative analyses by UV spectroscopy and EIS revealed that the long-term deterioration of the lubricant-infused surface was divided into two stages:the surface-adhered lubricant layer gradually dissolved at a constant rate until the substrate was exposed;afterwards the lubricant infused in the nanochannels began to diffuse and was depleted after~200 days.The EIS results also revealed that the defects reduced the corrosion resistance of the lubricant-infused surface considerably.展开更多
基金Project supported by the National Natural Science Foundation of China (Grant Nos 60571045 and 60328102)
文摘This paper reports high temperature liquid phase synthesis of Pd nanowires using chemically modified porous anodic aluminium oxide as template. In this synthesis process, oleic acid is used to modify the inner wall of the pores and Pd^2+ complex with oleylamine is filled into the channel of the template. The complex is then reduced to give oleylamine-capped Pd nanowires. This paper suggests that oleic acid can improve the environment of inner wall of the pores, leading to the formation of uniform Pd nanowires. The synthetic process can be extended to make other types of nanowires.
基金supported by the National Key Research and Development Program of China(No.2016YFE0203600)the National Natural Science Foundation of China(No.51771029)+1 种基金the Beijing Nova Program(Z171100001117076)the 111 Project(B17003)。
文摘This study investigated the deterioration of a lubricant-infused anodic aluminium oxide surface in a 1M NaCl solution for~200 days.Direct observation by cryo-SEM and quantitative analyses by UV spectroscopy and EIS revealed that the long-term deterioration of the lubricant-infused surface was divided into two stages:the surface-adhered lubricant layer gradually dissolved at a constant rate until the substrate was exposed;afterwards the lubricant infused in the nanochannels began to diffuse and was depleted after~200 days.The EIS results also revealed that the defects reduced the corrosion resistance of the lubricant-infused surface considerably.