Mixed mode Ⅰ/Ⅱ fracture erperiments of LC4-CS aluminum alloy were conductedby using tension--shear specimens with thicknesses of 2, 4, 8 and 14mm. Fracturemechanisms of thickness effect on mixed mode Ⅰ/Ⅱ fracture ...Mixed mode Ⅰ/Ⅱ fracture erperiments of LC4-CS aluminum alloy were conductedby using tension--shear specimens with thicknesses of 2, 4, 8 and 14mm. Fracturemechanisms of thickness effect on mixed mode Ⅰ/Ⅱ fracture were first examined fromfracture surface morphology to correlate with the macroscopic fracture behavior andstress state. It is found that specimen thickness has a strong influence on mixed modefracture. As thickness varies from thin to thick the macroscopic fracture surfacesappear the characteristics of plane stress state (2mm, 4mm--thick specimen), three--dimensional stress state (8mm--thick specimens), and plane strain state (14mm--thickspecimens), respectively. The specimens of all kinds of thicknesses are typical of ten-sile type failure under mode Ⅰ loading condition and shear type failure under mode Ⅱloading condition. Two distinct features coexist on the fracture surfaces under mixedmode loading conditions, and the corresponding proportion varies with loading mix-ity. Void--growth processes are the failure mechanism in both predominately tensile-and shears--type fractures. The size and depth of dimples on the fracture surface varygreatly with thickness. Therefore, it is extraordinary necessary to take into accountthe thickness effect when a mixed mode fracture criterion is being established.展开更多
On the bases of high temperature creep experiments, the research on engineering application of rheological forming is carried out on two kinds of light metal alloy parts named cylindrical shell of Lc4 aluminum alloy a...On the bases of high temperature creep experiments, the research on engineering application of rheological forming is carried out on two kinds of light metal alloy parts named cylindrical shell of Lc4 aluminum alloy and vane disk with complex curved surface of TC11 titanium alloy. Moreover, the mechanical property tests under room and high temperatures for the workpieces produced by this new technique are also done, the results showed that they are much improved evidently compared with those produced by traditional method.展开更多
文摘Mixed mode Ⅰ/Ⅱ fracture erperiments of LC4-CS aluminum alloy were conductedby using tension--shear specimens with thicknesses of 2, 4, 8 and 14mm. Fracturemechanisms of thickness effect on mixed mode Ⅰ/Ⅱ fracture were first examined fromfracture surface morphology to correlate with the macroscopic fracture behavior andstress state. It is found that specimen thickness has a strong influence on mixed modefracture. As thickness varies from thin to thick the macroscopic fracture surfacesappear the characteristics of plane stress state (2mm, 4mm--thick specimen), three--dimensional stress state (8mm--thick specimens), and plane strain state (14mm--thickspecimens), respectively. The specimens of all kinds of thicknesses are typical of ten-sile type failure under mode Ⅰ loading condition and shear type failure under mode Ⅱloading condition. Two distinct features coexist on the fracture surfaces under mixedmode loading conditions, and the corresponding proportion varies with loading mix-ity. Void--growth processes are the failure mechanism in both predominately tensile-and shears--type fractures. The size and depth of dimples on the fracture surface varygreatly with thickness. Therefore, it is extraordinary necessary to take into accountthe thickness effect when a mixed mode fracture criterion is being established.
基金supported by the National Personnel Department for returned talents(lincaipeizi[2001]30#)the Education Ministry of China for the university with doctoral discipline (No. 200805380004)
文摘On the bases of high temperature creep experiments, the research on engineering application of rheological forming is carried out on two kinds of light metal alloy parts named cylindrical shell of Lc4 aluminum alloy and vane disk with complex curved surface of TC11 titanium alloy. Moreover, the mechanical property tests under room and high temperatures for the workpieces produced by this new technique are also done, the results showed that they are much improved evidently compared with those produced by traditional method.