Preparation of ultrafine α-Al_2O_3 powders by catalytic sintering of ammonium aluminum carbonate hydroxide at low temperature

The precursor of ammonium aluminum carbonate hydroxide was synthesized by using aluminum sulfate（Al2（SO4）3） and ammonium carbonate（（NH4）2CO3）. The effects of α-Al2O3 seeds and mixture composed of α-Al2O3 and ammonium nitrate, as well as multiplex catalysts （AT） on phase transformation of alumina in sintering process were investigated respectively. The results show that the α-Al2O3 seeds and the mixture of α-Al2O3 and ammonium nitrate can lower the phase transformation temperature of α-Al2O3 to different extents while the particles obtained agglomerate heavily. AT has great potential synergistic effects on the phase transformation of alumina and reduces the phase transformation temperature of α-Al2O3 and the trends of necking-formation between particles. Therefore the dispersion of powder particles is improved significantly.

Preparation of Nano-Alumina with Aluminum Scraps as Raw Materials

Ammonium aluminum carbonate hydroxide (AACH) was synthesized by the reaction of ammonium aluminum sulphate (AA) with ammonium hydrogen carbonate (AHC). AA was obtained by the reaction of NH4HSO4 with aluminum scraps as the raw materials. According to this method, AACH samples prepared were used to fabricate nano alumina powders by thermal decomposition. The microstructural properties of as-formed alumina were characterized by X-ray diffraction (XRD), transmission electron microscopy (TEM), scanning electron microscopy (SEM), special surface analysis and inductively coupled plasma-atomic emission spectrometry (ICP-AES). Experimental observations revealed that highly pure (99.99%) α-alumina with mean diameter of 49 nm could be obtained.

Fibrous activated alumina prepared through phase transformation using dawsonite as a template

Fibrous activated alumina is widely applied in catalysts,adsorbents,and composite materials.This work presents a green approach in preparing the fibrous activated Al_(2)O_(3) with high purity and specific surface area through multistep phase transformation of aluminum-bearing substances using intermediate dawsonite as a template.Thermodynamic calculations and experimental results show that increasing the concentration of Na_(2)CO_(3) and(NH_(4))_(2)CO_(3) is remarkably beneficial to the formation of dawsonite and ammonium aluminum carbonate hydroxide,respectively.Based on determination of dissolution and precipitation mechanism,the ultrafine granular gibbsite is converted to the uniform fibrous dawsonite with a ratio of length to diameter over 50,and the fibrous dawsonite changes into the long fibrous ammonium aluminum carbonate hydroxide with a ratio of length to diameter is about 80 in above 70 g/L(NH_(4))_(2)CO_(3) solution.Furthermore,the activated alumina remains fibrous morphology after roasting ammonium aluminum carbonate hydroxide at a slow heating rate,plentiful open mesopore and weak aggregation of particles,which contributes to the high specific surface area of 159.37 m^(2)/g at 1273 K for the activated alumina.The complete transformation of dawsonite to ammonium aluminum carbonate hydroxide and high specific surface area contribute to the purity of the activated fibrous alumina above 99.9%with low Na and Fe content.

Preparation of γ-Al2O3 via Hydrothermal Synthesis Using ρ-Al2O3 as Raw Material for Propane Dehydrogenation

γ-Al2O3 was prepared by hydrothermal synthesis usingρ-Al2O3 and urea as raw materials.In this work,the eff ects of the molar ratio of CO(NH2)2/Al and reaction temperature were investigated,and a Pt–Sn–K/γ-Al2O3 catalyst was prepared.The ammonium aluminum carbonate hydroxide(AACH),γ-Al2O3,and Pt–Sn–K/γ-Al2O3 were characterized by X-ray diff raction,scanning electron microscopy,transmission electron microscopy,N2 adsorption–desorption,thermogravimetry–differential thermal analysis,and NH3 temperature-programmed desorption techniques.The reactivity of Pt–Sn–K/γ-Al2O3 for propane dehydrogenation was tested in a micro-fixed-bed reactor.The results show thatγ-Al2O3 with a specific surface area of 358.1 m 2/g and pore volume of 0.96 cm 3/g was obtained when the molar ratio of CO(NH2)2/Al was 3:1 and the reaction temperature was 140℃.The alumina obtained by calcination of AACH has a higher specific surface area and larger pore volume than the industrial pseudo-boehmite does.The catalyst prepared from AACH as precursor showed high selectivity and conversion,which can reach 96.1%and 37.6%,respectively,for propane dehydrogenation.

Synthesis, Characterization and Flame-retardant Properties of Epoxy Resins and AACHH Composites

Flame retardant epoxy resins were prepared by a simple mixed method using ammonium aluminum carbonate hydroxy hydrate （AACHH） as a halogen-free flame retardant. The prepared samples were characterized by X-ray diffraction, thermogravimetric and differential scanning calorimetry, scanning electron microscope and limiting oxygen index（LOI） experiments. Effects of AACHH content on LOI of epoxy resins/AACHH composite and flame retardant mechanism were investigated and discussed. Results show that AACHH exhibites excellent flame-retardant properties in epoxy resin（EP）. When the content of AACHH was 47.4%, the LOI of EP reached 32.2%. Moreover, the initial and terminal decomposition temperature of EP increased by 48 ℃ and 40 ℃, respectively. The flame retarded mechanism of AACHH is due to the synergic flame retardant effects of diluting, cooling, decomposition resisting and obstructing.