Anthropogenic aluminum cycle in China was analyzed by the aluminum flow diagram based on the life cycle of aluminum products. The whole anthropogenic aluminum cycle consists of four stages： alumina and aluminum produ...Anthropogenic aluminum cycle in China was analyzed by the aluminum flow diagram based on the life cycle of aluminum products. The whole anthropogenic aluminum cycle consists of four stages： alumina and aluminum production, fabrication and manufacture, use and reclamation. Based on the investigation on the 2003-2007 aluminum cycles in China, a number of changes can be found. For instance, resources self-support ratio （RSR） in alumina production dropped from 95.42%to 55.50%, while RSR in the aluminum production increased from 52.45%to 79.25%. However, RSR in the Chinese aluminum industry leveled off at 50%in the period of 2003-2007. The respective use ratios of domestic and imported aluminum scrap in the aluminum industry of 2007 were 5.38% and 9.40%. In contrast, both the net imported Al-containing resources and the lost quantity of Al-containing materials in aluminum cycle increased during the same period, as well as the net increased quantity of Al-containing materials in social stock and recycled Al-scrap. Proposals for promoting aluminum cycle were put forward. The import/export policy and reducing the loss of Al-containing materials for the aluminum industry in China in the future were discussed.展开更多
The hardness, the tensile and the high-cycle fatigue（HCF） performances of 7075 aluminum alloy were investigated under temper T651, solution treated at 380 ℃ for 0.5 h and aged at different temperatures（150, 170, 1...The hardness, the tensile and the high-cycle fatigue（HCF） performances of 7075 aluminum alloy were investigated under temper T651, solution treated at 380 ℃ for 0.5 h and aged at different temperatures（150, 170, 190 ℃） for 10 hours. The optimal microstructures and the fatigue fracture surfaces were observed. The results show that the hardness and the tensile performances are at their optimum at T651, but the fatigue life is the shortest. The hardness and the elongation are the lowest after solution treatment. With the aging temperature increasing（150-190 ℃）, the HCF is improved. The crack is initiated from the impurity particles on the subsurface. Treated at 170 ℃,the area of the quasi-cleavage plane and the width of parallel serrated sections of the crack propagation are the largest. With increasing aging temperature, the dimple size of finally fracture surfaces becomes larger and the depth deeper.展开更多
基金Projects (71003018,71373003) supported by the National Natural Science Foundation of ChinaProjects (N110402003,N120302004) supported by the Fundamental Research Funds for the Central Universities,ChinaProject (13YJCZH172) supported by the Ministry of Education of China of Humanities and Social Sciences
文摘Anthropogenic aluminum cycle in China was analyzed by the aluminum flow diagram based on the life cycle of aluminum products. The whole anthropogenic aluminum cycle consists of four stages： alumina and aluminum production, fabrication and manufacture, use and reclamation. Based on the investigation on the 2003-2007 aluminum cycles in China, a number of changes can be found. For instance, resources self-support ratio （RSR） in alumina production dropped from 95.42%to 55.50%, while RSR in the aluminum production increased from 52.45%to 79.25%. However, RSR in the Chinese aluminum industry leveled off at 50%in the period of 2003-2007. The respective use ratios of domestic and imported aluminum scrap in the aluminum industry of 2007 were 5.38% and 9.40%. In contrast, both the net imported Al-containing resources and the lost quantity of Al-containing materials in aluminum cycle increased during the same period, as well as the net increased quantity of Al-containing materials in social stock and recycled Al-scrap. Proposals for promoting aluminum cycle were put forward. The import/export policy and reducing the loss of Al-containing materials for the aluminum industry in China in the future were discussed.
基金Funded by the National Natural Science Foundation of China(Nos.51375500,and 51375162)Scientific Research Project of Hunan Province Department of Education(No.17C0886)Open Funded Projects of Hunan Provincial Key Laboratory of Health Maintenance for Mechanical Equipment(No.201605)
文摘The hardness, the tensile and the high-cycle fatigue（HCF） performances of 7075 aluminum alloy were investigated under temper T651, solution treated at 380 ℃ for 0.5 h and aged at different temperatures（150, 170, 190 ℃） for 10 hours. The optimal microstructures and the fatigue fracture surfaces were observed. The results show that the hardness and the tensile performances are at their optimum at T651, but the fatigue life is the shortest. The hardness and the elongation are the lowest after solution treatment. With the aging temperature increasing（150-190 ℃）, the HCF is improved. The crack is initiated from the impurity particles on the subsurface. Treated at 170 ℃,the area of the quasi-cleavage plane and the width of parallel serrated sections of the crack propagation are the largest. With increasing aging temperature, the dimple size of finally fracture surfaces becomes larger and the depth deeper.