An organic silane acrylate resin （PMBK） was synthesized by free-radical solution polymerization using methyl methacrylate, butyl acrylate and （3-methacryloxypropyl）trimethoxysilane as monomers. Aluminum （AI） par...An organic silane acrylate resin （PMBK） was synthesized by free-radical solution polymerization using methyl methacrylate, butyl acrylate and （3-methacryloxypropyl）trimethoxysilane as monomers. Aluminum （AI） particles were then encapsulated in inorganic-organic hybrid films that were prepared by hydrolysis and condensation of PMBK and tetraethyl orthosilicate （TEOS） on the surface of AI pigments. Characterization results showed that PMBK and TEOS could simultaneously hydrolyze ancl condense with hydroxyl groups on the surface of the A1 particles to form composite AI particles coated with inorganic-organic hybrid films. Compared with raw AI particles, the corrosion resistance and adhesive properties of paint films containing the composite AI particles were improved greatly, while the glossiness of the paint films decreased slightly, from 48.6° to 47.0°. In alkaline media （pH 11 ）, the volume of evolved H2 of composite AI particles was only 3.5 mL, whereas that of raw AI was 83.5 mL. The glossiness of paint films containing composite A1 particles decreased by 1.66% after immersion in alkaline media for 24h, whereas that of raw AI decreased by 14.82%. Peel-off tests of the paint films showed that the composite particles moved slightly away from the paint films. In contrast, the raw A1 particles were seriously desquamated, suggesting encapsulation of hybrid films can greatly improve the adhesive properties of A1 particles in paint films.展开更多
A double-layer aluminum consisting of an aluminum core and a shellof SiO2 and polyacrylic acid was synthesized.This modified aluminum was used to improve the corrosion resistance and dispersive property of aluminum in...A double-layer aluminum consisting of an aluminum core and a shellof SiO2 and polyacrylic acid was synthesized.This modified aluminum was used to improve the corrosion resistance and dispersive property of aluminum in waterborne media.TEM,FTIR,XPS,and EDX determination showed that PAA and SiO2 were coated on the surface of aluminum.Evolved hydrogen detection showed that the corrosion resistance of composite particle had been markedly improved.Maximum corrosion inhibition efficiency of SiO2 coated aluminum（SiO2@Al）was 95.1% while that of double-layer coated aluminum（PAA/SiO2@Al）was 98.8%.Meanwhile,polyacrylic acid layer improved the agglomeration of aluminum significantly.According to the dispersibility test,the particle size of 50% volume fraction [d（0.5）] of aluminum,SiO2@Aland PAA/SiO2@Alwere 42,53,and 34 μm,respectively.展开更多
基金financially supported by the Natural Science Foundation of China(Grant Nos.20976059 and 21376093)Fundamental Research Funds for the Central Universities(Grant No.2013ZZ074)
文摘An organic silane acrylate resin （PMBK） was synthesized by free-radical solution polymerization using methyl methacrylate, butyl acrylate and （3-methacryloxypropyl）trimethoxysilane as monomers. Aluminum （AI） particles were then encapsulated in inorganic-organic hybrid films that were prepared by hydrolysis and condensation of PMBK and tetraethyl orthosilicate （TEOS） on the surface of AI pigments. Characterization results showed that PMBK and TEOS could simultaneously hydrolyze ancl condense with hydroxyl groups on the surface of the A1 particles to form composite AI particles coated with inorganic-organic hybrid films. Compared with raw AI particles, the corrosion resistance and adhesive properties of paint films containing the composite AI particles were improved greatly, while the glossiness of the paint films decreased slightly, from 48.6° to 47.0°. In alkaline media （pH 11 ）, the volume of evolved H2 of composite AI particles was only 3.5 mL, whereas that of raw AI was 83.5 mL. The glossiness of paint films containing composite A1 particles decreased by 1.66% after immersion in alkaline media for 24h, whereas that of raw AI decreased by 14.82%. Peel-off tests of the paint films showed that the composite particles moved slightly away from the paint films. In contrast, the raw A1 particles were seriously desquamated, suggesting encapsulation of hybrid films can greatly improve the adhesive properties of A1 particles in paint films.
基金Funded by the National Natural Science Foundation of China(31170558)the Fundamental Research Funds for the Central Universities(410500006)
文摘A double-layer aluminum consisting of an aluminum core and a shellof SiO2 and polyacrylic acid was synthesized.This modified aluminum was used to improve the corrosion resistance and dispersive property of aluminum in waterborne media.TEM,FTIR,XPS,and EDX determination showed that PAA and SiO2 were coated on the surface of aluminum.Evolved hydrogen detection showed that the corrosion resistance of composite particle had been markedly improved.Maximum corrosion inhibition efficiency of SiO2 coated aluminum（SiO2@Al）was 95.1% while that of double-layer coated aluminum（PAA/SiO2@Al）was 98.8%.Meanwhile,polyacrylic acid layer improved the agglomeration of aluminum significantly.According to the dispersibility test,the particle size of 50% volume fraction [d（0.5）] of aluminum,SiO2@Aland PAA/SiO2@Alwere 42,53,and 34 μm,respectively.